Oxford spinning fabric

A technology of Oxford spinning and fabrics, which is applied in the production process of Oxford spinning fabrics. It can solve the problems that affect the appearance of the fabric, the sewing effect of the fabric, the fabric feels hard and not soft enough, and the production process cannot be eliminated, so as to eliminate splitting defects and three-dimensional effect. Strong, thick-feeling effect

Inactive Publication Date: 2016-09-21
JIANGSU JAMES TEXTILE
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the hand feeling of this kind of fabric is hard and not soft enough, and it needs to be washed to improve it. Moreover, the fabric surface is prone to splitting, which cannot be eliminated duri

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] 1. The whole production process is: blending, opening and cleaning, carding, drawing, roving, spun yarn, winding, dyeing, sizing, weaving, and finishing. The specific steps are as follows:

[0011] 1. Cotton blending: long-staple cotton and medium-fine-staple cotton are selected as raw materials, and are composed of the following parts by weight: long-staple cotton is 50-80 parts, and medium-fine-staple cotton is 20-50 parts.

[0012] 2. Opening and cleaning: The process of opening and cleaning is as follows: the dry weight of the lap is 400-450g / m, the weight of the lap is 10-15kg, the speed of the carding cylinder is 480-550r / min, and the combined beater is 700-800r / min.

[0013] 3. Carding: The process setting of the carding machine is: the licker-in speed is 820-900r / min, the cylinder speed is 300-350r / min, and the doffer speed is 20-28r / min.

[0014] 4. Drawing: Drawing process parameters are set as follows: cooked sliver weight 15-22g / 5m, sliver delivery speed 200...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an oxford spinning fabric, belongs to the technical field of spinning and particularly relates to a production technology of the oxford spinning fabric. The oxford spinning fabric is of a double-end texture, C50S compact spinning cotton yarn is formed in the warp direction, C8S ring spinning combed cotton yarn is formed in the weft direction, and the texture structure is weft ribs or squares. By adjusting yarn for a conventional oxford spinning fabric, the produced oxford spinning fabric has the advantages of being soft, thick, soft and breathable; due to the special point-shaped texture of a cloth cover, the granular sensation is stronger, third dimension is stronger, the oxford spinning fabric is more glossy, the fabric is better in sewability, and the fabric can be used in a cold area in the north of China. Particularly, 8 thick combed cotton yarn counts are adopted as weft yarn counts, the liquid ammonia finishing procedure is performed after matching, the fabric is softer and more comfortable in touch, split defects of the cloth cover are eliminated, the touch is thick and solid, and the requirement of a consumer for the cold area in the north of China is met.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a production process of Oxford fabrics. Background technique [0002] Conventional Oxford spinning has 21 strands in the weft direction and C40S in the warp direction, and its organizational structure is: weft-heavy flat or square flat. The unique graininess of Oxford fabric makes the fabric three-dimensional and full, moisture-absorbing and breathable, and comfortable to wear, which is deeply loved by consumers. [0003] However, the hand feeling of this kind of fabric is hard and not soft enough, and it needs to be washed to improve it, and the fabric surface is prone to splitting, which cannot be eliminated during the production process, affecting the appearance of the fabric surface and the subsequent sewing effect, and this kind of fabric is mostly thin fabrics. Not suitable for colder regions such as the north. Contents of the invention [0004] In view of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D13/00D03D15/00D03D15/217
CPCD03D13/008D03D15/00D10B2201/02
Inventor 顾义师唐志钢周丽红傅青于拥军
Owner JIANGSU JAMES TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap