Carbon nanotube reinforced anti-oxidation geogrid and preparation method thereof

A technology of geogrid and carbon nanotubes, applied in the field of geogrid, can solve the problems of limited application field and use effect, insoluble in water and organic solvent, poor compatibility of dispersed matrix, etc., to achieve delay Oxidative degradation process, improvement of antioxidant performance, effect of eliminating alkyl free radicals

Inactive Publication Date: 2016-09-28
ANHUI JIEAOMAKE SYNTHETIC MATERIAL TECH
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although carbon nanotubes have many excellent properties, their applications are greatly limited due to their poor sol

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] A carbon nanotube reinforced anti-oxidation geogrid, which is composed of the following raw materials in parts by weight:

[0021] Calcium acetylacetonate 1.6, alkenyl succinic anhydride 0.7, barium stearate 1, lithium aluminum hydride 0.1, 4 dimethylaminopyridine 0.3, antioxidant 10100.4, multi-walled carbon nanotubes 10, antioxidant 1680.6, polypropyleneimine 10. tert-butyl acrylate 6, high-density polyethylene 140, bisphenol a diglycidyl ether 0.3, 2-mercaptobenzimidazole 0.6, dibutyl maleate 4, lithium naphthenate 0.4.

[0022] A preparation method of the carbon nanotube reinforced anti-oxidation geogrid, comprising the following steps:

[0023] (1) Add the above-mentioned 2-mercaptobenzimidazole to 10 times the weight of absolute ethanol, stir evenly, add alkenyl succinic anhydride, raise the temperature to 60°C, keep the reaction for 20 minutes, add the above-mentioned tert-butyl acrylic acid ester, stirred to normal temperature to obtain modified monomer;

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a carbon nanotube reinforced anti-oxidation geogrid, which is composed of the following raw materials in parts by weight: 1.6-2 calcium acetylacetonate, 0.7-1 alkenyl succinic anhydride, and 1-2 barium stearate , lithium aluminum hydride 0.1‑0.3, 4‑dimethylaminopyridine 0.3‑1, antioxidant 10100.4‑1, multi-walled carbon nanotubes 10‑15, antioxidant 1680.6‑1, polypropylene imine 10‑17, acrylic acid Tert-butyl ester 6-8, high-density polyethylene 140-160, bisphenol a diglycidyl ether 0.3-1, 2-mercaptobenzimidazole 0.6-1, dibutyl maleate 4-6, cycloalkane Lithium Oxide 0.4‑1. The invention greatly reduces the content of free radicals participating in the automatic oxidation chain reaction of polymers, delays the oxidation degradation process of polymers, and improves the oxidation resistance of finished materials.

Description

technical field [0001] The invention relates to the technical field of geogrids, in particular to a carbon nanotube-reinforced anti-oxidation geogrid and a preparation method thereof. Background technique [0002] As a typical one-dimensional nanomaterial, carbon nanotubes have a large aspect ratio, ultra-high elastic modulus and bending strength, unique electrical conductivity, excellent thermal conductivity, and strong acid resistance compared with traditional fillers. , strong alkali and other advantages. Studies have shown that by combining carbon nanotubes and polyolefins to fully combine their respective properties, a multifunctional polyolefin / carbon nanotube composite material with excellent mechanical, electrical conductivity, and flame-retardant properties can be prepared. The potential huge advantages of polyolefin / carbon nanotube composite materials have attracted extensive attention from researchers at home and abroad; [0003] Although compared with ordinary ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08K13/06C08K9/04C08K9/02C08K7/24
CPCC08K13/06C08K7/24C08K9/02C08K9/04C08K9/08C08K2201/011C08L2201/08C08L2207/062
Inventor 叶磊
Owner ANHUI JIEAOMAKE SYNTHETIC MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap