Method for preparing insulating material for black aerial insulated cables through one step

A technology for overhead insulated cables and insulating materials, applied in the field of insulating materials, can solve problems such as large gaps, achieve high insulation resistance, improve heat deformation resistance, and reduce quality

Inactive Publication Date: 2016-10-12
浙江太湖远大新材料股份有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As we all know, in the industry, the temperature grade of 105°C and below can meet the requirements no matter whether XLPE, XLPVC or PVC is used. Above 150°C, the application of silicone rubber, fluoroplastics, polyimide and other varieties has also matured, but in the middle temperature grade (such as 125°C, 150°C) application development, there is a big gap with foreign countries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing insulating material for black aerial insulated cables through one step
  • Method for preparing insulating material for black aerial insulated cables through one step
  • Method for preparing insulating material for black aerial insulated cables through one step

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Insulating material for black overhead insulated cables, the insulating material is prepared from the following components by weight percentage:

[0041]

[0042] The two-step method for preparing insulating materials for black overhead insulated cables mainly consists of two parts, one is the preparation of catalyst masterbatch, and the other is the preparation of finished products.

[0043] 1) Preparation of catalyst masterbatch: catalyst masterbatch is LDPE, organotin, antioxidant 1010, antioxidant DLTP, fluororubber masterbatch, black masterbatch;

[0044] Stir the above materials in the mixer, first stir at low speed for 1 minute and then at high speed for 3 minutes, then release and pour into the hopper of the extruder. After being blown dry by a fan, the pellets are cut into pellets. The pellets are dried in a drying tower at 80°C for more than 2 hours, and then packed in vacuum aluminum-plastic bags for temporary storage.

[0045] 2) Finished product prepara...

Embodiment 2

[0055] Insulating material for black overhead insulated cables, the insulating material is prepared from the following components by weight percentage:

[0056]

[0057] The insulating material mentioned above was prepared by the two-step method of Example 1.

Embodiment 3

[0059] Insulating material for black overhead insulated cables, the insulating material is prepared from the following components by weight percentage:

[0060]

[0061]

[0062] The invention discloses a method for preparing insulating material for black overhead insulated cables in one step. It mainly consists of two parts, one is the preparation of catalyst masterbatch, and the other is the preparation of finished products.

[0063] 1) Preparation of catalyst masterbatch: catalyst masterbatch is LDPE, organotin, antioxidant 1010, antioxidant DLTP, fluororubber masterbatch, black masterbatch;

[0064] Stir the above materials in the mixer, first stir at low speed for 1 minute and then at high speed for 3 minutes, then release and pour into the hopper of the extruder. After being blown dry by a fan, the pellets are cut into pellets. The pellets are dried in a drying tower at 80°C for more than 2 hours, and then packed in vacuum aluminum-plastic bags for temporary stora...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of insulating materials, in particular to an insulating material for black aerial insulated cables. A method for preparing the insulating material for the black aerial insulated cables through one step mainly comprises the two steps of catalyst master batch preparation and finished product preparation. The insulating material is prepared from, by weight, LLDPE-7042, LLDPE-8320, LDPE, a silane coupling agent, a cross-linking agent DCP, an antioxidant 300, an antioxidant 1010, an antioxidant DLTP, organotin, fluororubber master batches and black master batches. The insulating material is used for erecting overhead wires to transmit electricity, the insulating property is superior to that of PVC, PVC can emit toxic and harmful gases when the wires fire due to aging and the like, but the silane insulating material is poisonless and harmless.

Description

technical field [0001] The invention relates to the field of insulating materials, in particular to insulating materials for black aerial insulated cables. Background technique [0002] The types of polyolefins used in the cable industry mainly include PE, PP, EVA and EEA, etc. Among them, the relatively large amount and long application history are mainly PE, which include HDPE, MDPE, LDPE, LLDPE and cross-linked XLPE. Their application Needless to say. The current application and development trends of polyolefins in the industry mainly focus on the following aspects: [0003] (1) Serialization and perfection of halogen-free and low-smoke materials [0004] Halogen-free, low-smoke, flame-retardant cable materials have been developing rapidly in recent years, and thermoplastic materials that meet the requirements of the IEC92-359 standard have been more and more widely used. With the requirements of cables for oil platforms, nuclear power plants, ships and other harsh env...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/06C08K5/00C08K5/14C08K5/57C08J3/22B29C47/92B29C48/92
CPCC08L23/0815B29C48/92B29C2948/92704C08J3/226C08J2323/08C08J2423/06C08L2201/08C08L2203/202C08L2205/025C08L2205/035C08L2207/066C08L2312/08C08L23/06C08K5/00C08K5/14C08K5/57
Inventor 赵勇蔡煜明俞丽琴李顺利郑颜
Owner 浙江太湖远大新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com