Multi-functional high-silica gold paint for architectural collection

A high-silica gold, multi-functional technology, used in anti-corrosion coatings, fire-resistant coatings, coatings, etc., can solve the problem of acid, alkali, and salt spray resistance of coatings without a clear description, and delay the development of fires. , Excellent seawater corrosion resistance and stable quality

Active Publication Date: 2016-10-12
沁阳市皇甫喷射防腐技术有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Through the patent search and query of the Intellectual Property Office of the People's Republic of China, the invention patent application of CN201510396824.X: a room temperature curing inorganic coating and its manufacturing method, the patent has no clear performance on the acid, alkali and salt spray resistance of the coating Explanation; CN201510283440.7 patent application for invention: a method for preparing heat-reflecting and heat-insulating inorganic coatings, which only solves the heat insulation performance of inorganic coatings; CN103496917A patent application for invention: ecological inorganic coatings for interior and exterior walls, the Patents also frame inorganic coatings for interior and exterior wall decoration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multi-functional high-silica gold paint for architectural collection
  • Multi-functional high-silica gold paint for architectural collection
  • Multi-functional high-silica gold paint for architectural collection

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The present invention is used for the multifunctional high silica gold paint of serial building, expressed by weight g, is made up of 40g of raw material composite curing agent, composite binder 25g and composite aluminosilicate 35g;

[0037] Expressed in weight g, the raw material composition of the composite curing agent 40g is liquid silicon dioxide 20g (density is 1.05g / cm 3 ), emboss powder 10g (particle size is 30 nanometers) and pyrophyllite powder 10g (10 nanometers);

[0038] Expressed in weight g, the raw material composition of the composite adhesive 25g is potassium silicate 12.5g (density is 1.45g / cm 3 ), magnesium oxide 7.5g (particle size is 50 nanometers) and high alumina powder 5g (particle size is 30 nanometers);

[0039] Represented by weight g, the raw material composition of the composite aluminosilicate 35g is silicon dioxide powder 1.75g ​​(particle size is 50 nanometers), magnesium silicate 8.75g (particle size is 20 nanometers) and aluminum sil...

Embodiment 2

[0041] The present invention is used for the multifunctional high silica gold paint of serial building, expressed by weight g, is made up of 42g of raw material composite curing agent, composite binder 23g and composite aluminosilicate 35g;

[0042] Expressed in weight g, the raw material composition of the composite curing agent 42g is liquid silicon dioxide 24g (density is 1.05g / cm 3 ), emboss powder 10g (particle size is 30 nanometers) and pyrophyllite powder 8g (particle size is 15 nanometers);

[0043] Expressed in weight g, the raw material composition of the composite adhesive 23g is potassium silicate 13g (density is 1.35g / cm 3 ), magnesium oxide 5g (particle size is 30 nanometers) and high alumina powder 5g (particle size is 30 nanometers);

[0044] Represented by weight g, the raw material composition of the composite aluminosilicate 35g is silicon dioxide powder 4g (particle size is 40 nanometers), magnesium silicate 10g (particle size is 20 nanometers) and aluminum ...

Embodiment 3

[0046] The present invention is used for the multifunctional high silica gold coating of serial building, expressed with weight g, is made up of raw material composite curing agent 45g, composite binder 25g and composite aluminosilicate 30g;

[0047] Expressed in weight g, the raw material composition of the composite curing agent 45g is liquid silicon dioxide 31g (density is 1.05g / cm 3 ), emboss powder 10g (particle size is 10 nanometers) and pyrophyllite powder 4g (particle size is 30 nanometers);

[0048] Expressed in weight g, the raw material composition of the composite adhesive 25g is potassium silicate 15g (density is 1.35g / cm 3 ), magnesium oxide 5g (particle size is 40 nanometers) and high alumina powder 5g (particle size is 30 nanometers);

[0049] Represented by weight g, the raw material composition of 30g of the composite aluminosilicate is silicon dioxide powder 6g (particle size is 40 nanometers), magnesium silicate 8g (particle size is 20 nanometers) and alum...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses multi-functional high-silica gold paint for an architectural collection. The paint is mainly prepared from, by weight, 40-70% of composite curing agent, 15-25% of composite adhesive and 15-35% of composite aluminosilicate. The composite curing agent is mainly composed of liquid silicon dioxide, palygorskite powder and pyrophyllite powder. The composite adhesive is mainly composed of potash water glass, magnesium oxide and high aluminite powder. The composite aluminosilicate is mainly composed of silicon dioxide powder, magnesium silicate and aluminum silicate. The paint is resistant to acid, alkali, salt mist corrosion, water, fire and flaming, environmentally friendly and durable, and can provide multi-aspect protection for buildings and equipment made of various materials; test detection proves that service life can be as long as 70 years. The coating is high in stable property under the condition that temperature changes dramatically under 350 DEG C.

Description

1. Technical field: [0001] The invention relates to a coating used in the architectural field, in particular to a multifunctional high-silica gold coating used in serial buildings. 2. Background technology: [0002] The application of high-silicon inorganic coatings can be traced back to the Spring and Autumn BC and the Roman period. Dunhuang murals and ancient Roman architecture have gone through thousands of years of wind and rain, and they are still as beautiful as new. The industrial production of inorganic coatings originated in Germany and emerged in the United States and Japan, with a history of more than 100 years. According to the national authoritative website, inorganic high-silicon coatings occupy the mainstream market of coating products in developed countries in Europe and America, accounting for 93% of the market share. However, the market share of domestic inorganic coatings is less than 5%, but they are still thermosetting, and room temperature curing inor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/18C09D5/08C09D7/12C04B28/26
CPCC04B28/26C09D1/00C09D5/08C09D5/18C09D7/61C04B14/06C04B14/102C04B14/041C04B9/00C04B22/04
Inventor 皇甫石金皇甫中杰
Owner 沁阳市皇甫喷射防腐技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com