A kind of 800mpa low-carbon hot-dip galvanized dual-phase steel and its preparation method

An 800MPa, dual-phase steel technology, applied in the field of 800MPa low-carbon hot-dip galvanized dual-phase steel and its preparation, can solve the problems of production cost, formability, galvanizing performance and welding performance without comprehensive consideration, and achieve guaranteed strength, The effect of low production cost

Active Publication Date: 2018-01-26
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] To sum up, the existing invention mainly considers the galvanizing performance and mechanical properties of dual-phase steel unilaterally, and does not comprehensively consider factors such as production cost, formability, galvanizing performance and welding performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of 800mpa low-carbon hot-dip galvanized dual-phase steel and its preparation method
  • A kind of 800mpa low-carbon hot-dip galvanized dual-phase steel and its preparation method
  • A kind of 800mpa low-carbon hot-dip galvanized dual-phase steel and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0040] The preparation method of above-mentioned a kind of 800MPa level low-carbon hot-dip galvanized dual-phase steel comprises the following steps:

[0041] a. Smelting process: smelting according to the weight percentage composition of the above-mentioned 800MPa grade low-carbon hot-dip galvanized dual-phase steel, and controlling the vanadium content in the converter (that is, by controlling the vanadium content in the original molten iron instead of adding additional vanadium-iron alloy, reducing production costs), cast into slabs;

[0042] b. Hot rolling process: hot-rolled coils are obtained after the slab is heated, dephosphorized, hot-rolled and laminar cooling; wherein, the starting temperature of the finish rolling is 1000-1100°C, and the finishing rolling temperature is 850-950°C. Take the temperature as 600~700℃;

[0043] c. Pickling process: hot-rolled coils are pickled and then cold-rolled to obtain cold-rolled thin strip steel; wherein, the cold-rolled reducti...

Embodiment 1

[0052] The preparation method of 800MPa grade low-carbon hot-dip galvanized dual-phase steel provided by the present invention has the following processes:

[0053] (1) Through the smelting process, a dual-phase steel slab with the chemical composition shown in Table 1 is prepared:

[0054] Table 1 Chemical Composition of Duplex Steel (wt.%)

[0055] Numbering

C

Si

mn

P

S

als

Cr

Mo

V

N

DP1

0.08

0.30

1.70

0.012

0.002

0.050

0.50

0.25

0.07

0.004

DP2

0.09

0.25

1.60

0.011

0.002

0.030

0.45

0.30

0.10

0.005

[0056] (2) After heating, dephosphorization, hot rolling and laminar cooling to obtain hot rolled coils, the starting temperature of finish rolling is 1000-1100°C, the finishing rolling temperature is 850-950°C, and the coiling temperature is 600°C ~700°C; the specific hot rolling process parameters are shown in Table 2 below:

[0057] Table 2 Main process p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of preparation of high-strength steel, and in particular, relates to 800 MPa-grade low-carbon hot-galvanized dual-phase steel and a preparation method thereof. The 800 MPa-grade low-carbon hot-galvanized dual-phase steel comprises the following components in percentage by weight: 0.05-0.10% of C, 0.20-0.60% of Si, 1.30-1.80% of Mn, 0.10-0.60% of Cr, 0.20-0.50% of Mo, 0.02-0.06% of Al, 0.05-0.10% of V, P not more than 0.015%, S not more than 0.005%, N not more than 0.006%, and the balance of Fe and inevitable impurities. The 800 MPa-grade low-carbon hot-galvanized dual-phase steel is low in production cost, high in forming performance and welding performance and excellent in galvanizing performance and mechanical performance, and reaches the yield strength of 450-520 MPa, the tensile strength of 805-840 MPa and the elongation of 15-18%.

Description

technical field [0001] The invention belongs to the technical field of high-strength steel preparation, and in particular relates to an 800MPa low-carbon hot-dip galvanized dual-phase steel and a preparation method thereof. Background technique [0002] With the development of automobile lightweight technology, it has become an inevitable trend for automobile steel to develop towards high-strength steel. Due to the characteristics of low yield strength, high tensile strength and excellent plasticity, dual-phase steel has become the preferred high-strength steel for automobiles, and its consumption is expected to exceed 70% of the advanced high-strength steel for automobiles. With the continuous release of domestic auto sheet production capacity, the competition in the high-strength steel market has become increasingly fierce. Low-cost, high-performance dual-phase steel has become the goal pursued by various companies and has attracted great attention. [0003] Patent (CN 10...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/18C22C38/12C22C38/06C21D8/02
CPCC21D8/0226C21D8/0236C21D8/0247C22C38/001C22C38/02C22C38/04C22C38/06C22C38/12C22C38/18
Inventor 郑之旺邝春福左军张功庭王敏莉余灿生于秀
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com