A kind of growth of SIC crystal for off-axis substrate and preparation method of n-type SIC substrate with high electrical uniformity

A growth method and substrate technology, applied in crystal growth, single crystal growth, single crystal growth, etc., can solve problems such as difficult to meet high-performance power devices, achieve the effect of reducing defect density and improving resistivity uniformity

Active Publication Date: 2018-06-19
SHANDONG UNIV
View PDF12 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally, the resistivity deviation between the facet position and other positions exceeds 10%. Such a large resistivity deviation is difficult to meet the needs of high-performance power devices.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of growth of SIC crystal for off-axis substrate and preparation method of n-type SIC substrate with high electrical uniformity
  • A kind of growth of SIC crystal for off-axis substrate and preparation method of n-type SIC substrate with high electrical uniformity
  • A kind of growth of SIC crystal for off-axis substrate and preparation method of n-type SIC substrate with high electrical uniformity

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The growth device used in Example 1 is a single crystal growth furnace, including a growth chamber, a graphite crucible, an insulating material and an induction heating system. There is a water cooling device on the side wall of the growth chamber, and the water cooling device is a sealed double-layer tube made of quartz glass. The circulating working medium in the tube is water, and the water temperature is kept constant during the growth process; the seed crystal is fixed on the graphite upper cover; the crucible and insulation material are placed in the growth chamber, and the growth chamber can reach 1×10 -6 Vacuum above mbar. Regarding the growth device, refer to Example 1 of CN1554808A, and the parts that are not inconsistent with the present invention are included in the present invention by reference.

[0040] As a comparative example, the traditional symmetric bonded seed crystal is shown as image 3 As shown, a 4-inch (r=50mm) SiC seed crystal 7 is symmetrica...

Embodiment 2

[0046] Example 2: Preparation of 4-inch 4° N-type SiC substrate

[0047] 1. The SiC crystal with a diameter of 120 mm obtained in Example 1 is subjected to rounding processing, and the small face and the junction area growing outward along the small side of the seed crystal are removed, so that the diameter of the SiC single crystal rod is 100 mm,

[0048] 2. Cut, grind and polish the SiC single crystal rod with a diameter of 100 mm to obtain a 4° N-type SiC substrate. Figure 7 , Figure 8 It is a photo of the fabricated 4° N-type SiC substrate material, numbered wafer 06 and wafer 20 respectively.

[0049] The partial 4° N-type SiC substrates numbered wafer 06 and wafer 20 were taken to test the resistivity. The results are as follows: there is still a residual small area on the far right side of wafer 06, the maximum resistivity is 0.01792 ohm*cm, and the minimum The value is 0.01735 ohm*cm with a deviation of 3.1%. However, the facet area of ​​the wafer 20 has been comp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for growth of a SiC crystal for an off-axis substrate and a method for preparing an N type SiC substrate with high electric uniformity. A deviating SiC seed crystal is adopted, a mechanism of controlling facet growth by a seed crystal asymmetric bonding way is used, and a SiC single-crystal material having the diameter increased by 20 mm than a standard diameter is obtained through an atmosphere guide plate. The asymmetrical rounding work is performed, and the SiC single-crystal material without facets is obtained. The N type SiC single-crystal substrate material with low defect density and electrical deviation of 3.5% or less can be obtained by the method.

Description

technical field [0001] The invention relates to the growth of SiC crystals for off-axis substrates and a method for preparing N-type SiC single crystal substrates with low defect density and high electrical uniformity, belonging to the technical field of crystal growth. Background technique [0002] Silicon carbide is the representative of the third generation of wide bandgap semiconductors. It has excellent electrical and thermal properties such as large bandgap, high mobility, and high thermal conductivity. It has become an ideal material for making high-frequency, high-power, high-temperature and radiation-resistant devices. In terms of device development, silicon carbide blue LEDs have been commercialized; research and development of silicon carbide power devices has become the mainstream of research and development of new power semiconductor devices; see CN104246979A "High-voltage semiconductor devices on SiC". In terms of high-temperature semiconductor devices, silicon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C30B23/02C30B29/36
CPCC30B23/025C30B23/066C30B29/36
Inventor 彭燕徐现刚陈秀芳胡小波
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap