High-heat resistance and high-toughness polycarbonate composition and preparation method thereof

A polycarbonate, high-toughness technology, applied in the field of engineering plastics, can solve the problems of high price of phosphazene flame retardants, limited large-area application, and limited application of aromatic phosphate ester flame retardants, etc. The effect of improving the flame retardant grade, improving heat resistance and toughness

Active Publication Date: 2016-11-09
JIANGSU KINGFA SCI & TECH ADVANCED MATERIALS CO LTD
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the application of aromatic phosphate flame retardants has been greatly limited
[0004] Chinese patent CN104583316 discloses a method for manufacturing a flame-retardant, high-heat-resistant, high-toughness polycarbonate composition. It uses PC with a special structure and adds a phosphazene flame retardant to improve the high-heat-resistant, high-toughness polycarbonate composition. The heat distortion temperature of the material, but the special structure of PC largely limits the large-area application of this method, and the high price of phosphazene flame retardant also limits the application of this method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-heat resistance and high-toughness polycarbonate composition and preparation method thereof
  • High-heat resistance and high-toughness polycarbonate composition and preparation method thereof
  • High-heat resistance and high-toughness polycarbonate composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The present invention will be described in further detail below in conjunction with specific examples, but the present invention is not limited to these examples.

[0020] As we all know, material selection, raw material formula, and preparation process are the three major factors that determine product quality, and the three influence each other. Therefore, in order to better illustrate the advantages and innovations of the high heat-resistant and high-toughness polycarbonate composition product obtained in the present invention, the material selection and raw material formula of the high heat-resistant and high-toughness polycarbonate composition product obtained in the present invention will be described below and the preparation method are described in detail.

[0021] (1) material selection situation of the present invention:

[0022] The invention discloses a polycarbonate composition with high heat resistance and high toughness. The raw materials mainly include ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-heat resistance and high-toughness polycarbonate composition and a preparation method thereof. The composition comprises, by weight, 60-90 parts of polycarbonate, 1-20 parts of a butadiene copolymer, 5-25 parts of a phosphate ester homopolymer, 0-8 parts of a flexibilizer and 0-9.6 parts of other assistants, and the quantity sum of weight parts of all above components is 100. Compared with the prior art, the preparation method has the following advantages: addition of the phosphate ester homopolymer to the raw material formula well overcomes an abuse that present organophosphate flame retardant greatly reduces the heat deformation temperature and the toughness of polycarbonate, effectively improves the heat resistance and the toughness of the polycarbonate composition, has a very good flame retardation effect, and effectively improves the flame retardation grade of the polycarbonate composition; and the phosphate ester homopolymer has extremely good compatibility with polycarbonate, has no plasticizing effect on alloy, and obviously improves the heat resistance of the polycarbonate composition without influencing the flame retardation grade or the toughness of the polycarbonate composition.

Description

technical field [0001] The invention relates to the technical field of engineering plastics, in particular to a polycarbonate composition with high heat resistance and high toughness and a preparation method thereof. Background technique [0002] Polycarbonate PC has the advantages of high impact resistance, heat resistance, good dimensional stability, electrical insulation performance, etc., but at the same time, PC has the disadvantages of being sensitive to notches and poor processing performance. In order to improve these defects, rubber modified polymers can usually be added, especially the PC / ABS alloy with PC and ABS as the main raw material is an important engineering plastic, which can not only improve the heat resistance and tensile strength of ABS, but also It can reduce the viscosity of PC melt, improve processing performance, and reduce the sensitivity of product internal stress and impact strength to product thickness. [0003] In addition, in order to meet th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L55/02C08L85/02
CPCC08L69/00C08L2201/02C08L2201/08C08L2205/03C08L2205/035C08L55/02C08L85/02
Inventor 董相茂田征宇刘贤文张永
Owner JIANGSU KINGFA SCI & TECH ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com