Antirust paint for metal steel pipe

A technology for anti-rust paint and steel pipes, applied in anti-corrosion coatings, dry oil coatings, coatings, etc., can solve the problems of poor anti-corrosion performance and slow drying, and achieve the effects of good anti-corrosion performance, simple raw materials, and simple preparation methods

Inactive Publication Date: 2016-11-23
朱小龙
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The invention provides an antirust paint for metal steel pipes with fast drying and good anticorrosion performance, which solves the technical problems of slow drying and poor anticorrosion performance of existing metal steel pipe materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Step 1: Weigh 100 parts of No. 200 solvent oil according to the ratio of parts by mass, 30 parts of xylene, 10 parts of phthalic anhydride, 1 part of lithium hydroxide, 0.2 part of manganese naphthenate, 0.5 part of lead naphthenate, 2 parts of tung oil 15 parts of linseed oil, 5 parts of rosin, 10 parts of pentaerythritol.

[0018] Step 2: Put No. 200 solvent oil, xylene, phthalic anhydride, lithium hydroxide and lead naphthenate into the reaction kettle, heat to 140°C, and stir at 200r / min for 20min.

[0019] Step 3: Put the stirred liquid aside for 90 minutes, add manganese naphthenate, tung oil, No. 200 solvent oil, rosin and pentaerythritol, mix well at 180°C, put it into a grinder for 10 hours, filter and pack.

[0020] It is used for anti-rust and anti-corrosion of metal steel pipe therapy appliances, with a viscosity of 105s; good anti-corrosion performance, impact resistance of 50cm, salt water resistance of 10d, no blistering and no falling off; surface dry 14...

Embodiment 2

[0022] Step 1: Weigh 100 parts of No. 200 solvent oil, 50 parts of xylene, 30 parts of phthalic anhydride, 5 parts of lithium hydroxide, 0.6 parts of manganese naphthenate, 4.5 parts of lead naphthenate, and 8 parts of tung oil according to the ratio of parts by mass. 35 parts of linseed oil, 25 parts of rosin, 30 parts of pentaerythritol.

[0023] Step 2: Put No. 200 solvent oil, xylene, phthalic anhydride, lithium hydroxide and lead naphthenate into the reaction kettle, heat to 160°C, and stir at 400r / min for 40min.

[0024] Step 3: Put the stirred liquid aside for 130 minutes, add manganese naphthenate, tung oil, No. 200 solvent oil, rosin and pentaerythritol, mix well at 220°C, put it into a grinder for 14 hours, filter and pack.

[0025] It is used for anti-rust and anti-corrosion of metal steel pipe therapy appliances, with a viscosity of 110s; good anti-corrosion performance, impact resistance of 55cm, salt water resistance of 15d without blistering or falling off; surf...

Embodiment 3

[0027] Step 1: Weigh 100 parts of No. 200 solvent oil, 35 parts of xylene, 15 parts of phthalic anhydride, 2 parts of lithium hydroxide, 0.3 parts of manganese naphthenate, 1.5 parts of lead naphthenate, and 3 parts of tung oil according to the ratio of parts by mass. 20 parts of linseed oil, 10 parts of rosin, 15 parts of pentaerythritol.

[0028] Step 2: Put No. 200 solvent oil, xylene, phthalic anhydride, lithium hydroxide and lead naphthenate into the reaction kettle, heat to 140°C, and stir at 200r / min for 20min.

[0029] Step 3: Put the stirred liquid aside for 90 minutes, add manganese naphthenate, tung oil, No. 200 solvent oil, rosin and pentaerythritol, mix well at 180°C, put it into a grinder for 10 hours, filter and pack.

[0030] It is used for anti-rust and anti-corrosion of metal steel pipe therapy appliances, with a viscosity of 115s; good anti-corrosion performance, impact resistance of 60cm, salt water resistance of 20d without blistering or falling off; surfa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antirust paint for metal steel pipes. The raw materials are: solvent oil No. 200, xylene, phthalic anhydride, lithium hydroxide, manganese naphthenate, lead naphthenate, tung oil, linseed oil, rosin and pentaerythritol; Anti-rust and anti-corrosion for metal steel tube therapy equipment, viscosity 105-125s; good anti-corrosion performance, impact resistance 50-70cm, salt water resistance 10-30d without foaming or falling off; surface dry 10-14h, hard work 18-22h, preparation The method is simple, the raw materials are simple and easy to obtain, and it can be widely produced and continuously replace the existing materials.

Description

technical field [0001] The invention relates to the technical field of materials for metal steel pipes, in particular to an antirust paint for metal steel pipes. Background technique [0002] Antirust paint is a coating that protects metal surfaces from chemical or electrochemical corrosion from the atmosphere, sea water, etc. Mainly divided into two categories of physical and chemical antirust paint. The former relies on the proper coordination of pigments and paints to form a dense paint film to prevent the intrusion of corrosive substances, such as iron red, aluminum powder, graphite antirust paint, etc.; the latter relies on the chemical antirust effect of antirust pigments, such as 200 Solvent oil, zinc yellow antirust paint, etc. Used for rust prevention of bridges, ships, pipelines and other metals. No. 200 solvent oil antirust paint is a kind of paint mixed with No. 200 solvent oil and drying oil. It has good permeability and wettability, soft paint film and stro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D191/00C09D5/08C09D7/12
CPCC09D191/005C08L2205/025C08L2205/03C09D5/08C09D7/61C09D7/63C09D7/65
Inventor 朱小龙
Owner 朱小龙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com