Anti-static flame-retardant fabric and production method thereof

A technology of flame-retardant fabrics and production methods, applied in the direction of fabrics, flame-retardant fibers, textiles, etc., to achieve the effects of high strength, soft hand feeling, and good wearing comfort

Inactive Publication Date: 2017-01-04
JIHUA 3509 TEXTILE
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The fire accidents caused by this and the phenomenon of huge losses are too numerous to enumerate at home and abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] 1) Warping process

[0035] Warp the strands of the blended yarn × 2 and the conductive yarn respectively, the warping speed is controlled at 450 m / min, and the weight of the tension disc of the conductive yarn is 2 times the weight of the strand tension disc of the blended yarn × 2.

[0036] 2) Sizing process

[0037] The strands of the blended yarn × 2 and the conductive yarn were sizing respectively, and the sizing speed was 42.5 m / min.

[0038] The slurry used includes the following raw materials in parts by weight: 37.5 parts of phosphate starch, 5 parts of liquid propylene, 10 parts of smoothing agent, 1 part of dinaphthol, and the solid content of the slurry is 4.2 ± 1%. Single size tank sizing.

[0039] 3) Denting

[0040] According to the design requirements of the upper machine diagram, the warp dropper, the heddle and the reed are sequentially passed through, and when the warp is drawn in, it is threaded strictly according to the arrangement ratio of the t...

Embodiment 2

[0045] 1) Warping process

[0046] Warp the strands of the blended yarn × 2 and the conductive yarn respectively, the warping speed is controlled at 400 m / min, and the weight of the conductive yarn tension disc is 2.2 times the weight of the strand tension disc of the blended yarn × 2.

[0047] 2) Sizing process

[0048] The strands of the blended yarn × 2 and the conductive yarn were sizing respectively, and the sizing speed was 45 m / min.

[0049] The slurry used includes the following raw materials in parts by weight: 35.00 parts of phosphate starch, 5.5 parts of liquid propylene, 9.0 parts of smoothing agent, 1.1 parts of dinaphthol, and the solid content of the slurry is 4.2 ± 1%. Single size tank sizing.

[0050] 3) Denting

[0051] According to the design requirements of the upper machine diagram, the warp dropper, the heddle and the reed are sequentially passed through, and when the warp is drawn in, it is threaded strictly according to the arrangement ratio of the t...

Embodiment 3

[0056] 1) Warping process

[0057] Warp the strands of the blended yarn × 2 and the conductive yarn respectively, the warping speed is controlled at 500 m / min, and the weight of the tension disc of the conductive yarn is 2.2 times the weight of the strand tension disc of the blended yarn × 2.

[0058] 2) Sizing process

[0059]The strands of the blended yarn × 2 and the conductive yarn were sizing respectively, and the sizing speed was 40 m / min.

[0060] The slurry used includes the following raw materials in parts by weight: 40.0 parts of phosphate starch, 4.5 parts of liquid propylene, 11.0 parts of smoothing agent, 0.9 part of dinaphthol, and the solid content of the slurry is 4.2 ± 1%. Single size tank sizing.

[0061] 3) Denting

[0062] According to the design requirements of the upper machine diagram, the warp dropper, the heddle and the reed are sequentially passed through, and when the warp is drawn in, it is threaded strictly according to the arrangement ratio of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Widthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of production of textiles and particularly relates to anti-static flame-retardant fabric and a production method thereof. The fabric is twill consisting of warp and weft, wherein the warp consists of folded yarns of double blended yarn and conductive yarn, the blended yarn is formed by blending flame-retardant viscose, aramid fibers and acrylic fibers, and the conductive yarn is formed by doubling polyester filament yarn and polyester conductive filaments; the weft consists of folded yarns of double blended yarn, and the blended yarn is formed by blending flame-retardant viscose, aramid fibers and acrylic fibers. The production method of the fabric comprises steps as follows: 1) a warping process; 2) a sizing process; 3) reeding; 4) a weaving process. Two pieces of warp of the anti-static flame-retardant fabric are spaced reasonably, and the fabric touches soft, is good in breathability, good in anti-static property and high in strength and has better wearing comfort.

Description

technical field [0001] The invention belongs to the technical field of textile production, and in particular relates to an antistatic flame retardant fabric and a production method thereof. Background technique [0002] With the development of the economy, the application fields of textiles are constantly expanding, especially in the application of industrial textiles, which brings a lot of convenience to people's production and life, but at the same time, it also brings some troubles and even hazards. For example, during the wearing process of textiles, the static electricity generated can easily accumulate charges and cause dust to adhere. Higher voltages can easily cause electric shocks, and even explosions may occur in flammable and explosive environments. The resulting fire accidents and the phenomenon of huge losses are too numerous to enumerate at home and abroad. Therefore, how to endow textiles with more functionality has important practical significance. Content...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D13/00D03D15/00D02G3/04D02H3/00D02H13/22D06M15/11D06M13/03D06M13/152D06M101/08D06M101/36D06M101/28D03D15/225D03D15/283D03D15/47D03D15/513D03D15/533
CPCD02G3/045D02H3/00D02H13/22D03D13/00D03D13/008D06M13/03D06M13/152D06M15/11D10B2201/24D10B2331/021D10B2321/10D10B2401/063D10B2401/16D06M2101/36D06M2200/30D06M2101/08D06M2101/28D03D15/533
Inventor 刘渊民张一村邓红卫晏顺芝余胜熊原许鹤程小潭马菲
Owner JIHUA 3509 TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com