Resin composite mica paper and preparation method thereof

A technology of resin compounding and mica paper, which is applied in the field of mica paper, can solve the problems of poor mechanical strength and toughness of mica paper, and cannot meet the needs of multi-field industry applications.

Active Publication Date: 2017-01-11
WUHU SAUNAKING ELECTRONICS TECH CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the mechanical strength and toughness of mica paper directly made from mica sheets are not good, and cannot meet the needs of many industries.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] 1) Stir and mix mica powder (120 mesh), polyacrylamide (weight-average molecular weight: 5,000), ethylenediaminetetraacetic acid and water according to the weight ratio of 255:5:5:100 to prepare mica pulp; The mica pulp is made into mica paper, and the mica paper is a mica layer; before 1), the mica sheet is washed with water with a liquid-solid ratio of 4 until the turbidity of the water is 11°, and washed 3 times.

[0023] 2) earlier novolac epoxy resin (weight-average molecular weight is 20,000), polyimide resin (weight-average molecular weight is 30,000), ethylene glycol ether, alcohol fat twelve, dibutyl phthalate and water Mix according to the weight ratio of 100:50:10:1:1:100, then perform heat treatment at 180° C. for 1.5 hours, and finally extrude to obtain a resin layer.

[0024] 3) Place the prepared mica paper on top of the prepared resin layer, heat-compress and compound at 170° C. with a pressure of 13 MPa for 4 hours, and then cool naturally to obtain the...

Embodiment 2

[0026] 1) Stir and mix mica powder (180 mesh), polyacrylamide (weight-average molecular weight: 20,000), ethylenediaminetetraacetic acid and water according to the weight ratio of 280:8:8:100 to prepare mica pulp; The mica pulp is made into mica paper, and the mica paper is a mica layer; before 1), the mica sheet is washed with water with a liquid-solid ratio of 5 until the turbidity of the water is 10°, and washed 3 times.

[0027] 2) earlier novolac epoxy resin (weight-average molecular weight is 30,000), polyimide resin (weight-average molecular weight is 40,000), ethylene glycol ether, alcohol fat twelve, dibutyl phthalate and water The mixture was mixed according to the weight ratio of 100:80:13:3:3:130, followed by heat treatment at 190° C. for 1.0 h, and finally extruded to obtain a resin layer.

[0028] 3) The prepared mica paper was placed on the prepared resin layer, and at 172° C., the pressure was selected to be 13 MPa for hot-compression lamination for 4 hours, fo...

Embodiment 3

[0030] 1) Mica powder (200 mesh), polyacrylamide (weight average molecular weight is 25,000), ethylenediaminetetraacetic acid and water are mixed according to the weight ratio of 300:10:10:100 to prepare mica pulp; finally The mica pulp is made into mica paper, and the mica paper is a mica layer; before 1), the mica sheet is washed with water with a liquid-solid ratio of 5 until the turbidity of the water is 12°, and washed 3 times.

[0031] 2) earlier novolac epoxy resin (weight-average molecular weight is 40,000), polyimide resin (weight-average molecular weight is 50,000), ethylene glycol ether, alcohol fat twelve, dibutyl phthalate and water Mixing according to the weight ratio of 100:95:15:5:5:150, followed by heat treatment at 200°C for 0.5h, and finally extrusion molding to obtain a resin layer.

[0032] 3) Place the prepared mica paper on top of the prepared resin layer, heat press and compound at 175° C. with a pressure of 14 MPa for 3 hours, and then cool naturally t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses resin composite mica paper. A preparation method of the resin composite mica paper includes: preparing a mica layer; preparing a resin layer, to be more specific, mixing novolac epoxy resin, polyimide resin, glycol ether, Texanol and dibutyl phthalate with water, performing thermal treatment, and performing extrusion forming to obtain the resin layer; performing resin compositing on the mica layer and the resin layer, to be more specific, placing the mica layer on the resin layer, performing hot-pressing resin compositing, and naturally cooling to obtain the resin composite mica paper. The resin composite mica paper has the advantages of excellent insulating performance and excellent high temperature resistance of the mica paper and is quite high in mechanical strength and toughness.

Description

technical field [0001] The invention relates to mica paper, in particular to resin composite mica paper and a preparation method thereof. Background technique [0002] Mica is a general term for a class of hydrous aluminosilicates. Mica has excellent properties such as insulation and high temperature resistance, and is widely used in coatings, paints, fire protection and electrical industries. Among them, making mica into mica paper is one of the most widely used mica applications. [0003] At present, mica paper has all the varieties corresponding to sheet mica products. The industry mainly uses the insulation and heat resistance of mica paper, as well as its acid and alkali resistance, to be used as insulating materials for electrical equipment and electrical equipment. However, the mechanical strength and toughness of the mica paper directly prepared from the mica sheets are not good, and cannot meet the needs of various industrial applications. Contents of the invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/38D21H13/44D21H17/55B32B37/15B32B37/06B32B19/04B32B27/10B32B27/42B32B27/38B32B27/40B32B27/20B32B7/10
CPCB32B7/10B32B19/045B32B27/10B32B27/20B32B27/38B32B27/40B32B27/42B32B37/06B32B37/15B32B37/153D21H13/44D21H17/55D21H27/38
Inventor 马西健
Owner WUHU SAUNAKING ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com