Lithium ion power battery and preparation method thereof

A power battery and lithium-ion technology, which is applied in the field of lithium-ion power batteries and their preparation, can solve the problems of poor battery performance, poor electrical conductivity, and large specific surface area, and achieve no environmental pollution, long cycle life, and high energy density. Effect

Inactive Publication Date: 2017-02-01
SHENZHEN ZHUONENG NEW ENERGY TECH
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, Li 4 Ti 5 o 12 Both NCA and NCA are in powder form, with fine particle size, large specific surface area, and relatively

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium ion power battery and preparation method thereof
  • Lithium ion power battery and preparation method thereof
  • Lithium ion power battery and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0034] A method for preparing a lithium ion power battery includes the following steps:

[0035] 1) Take the first active material, the first adhesive, the first conductive agent, the second active material, the second adhesive and the second conductive agent respectively in the formula amount, and bake them in an environment of 115-125℃ 11-13h, spare;

[0036] 2) Preparation of the positive electrode slurry: take the first active material, the first adhesive and the first conductive agent that have been baked in step 1), and mix to obtain the first mixed powder; take N-methylpyrrolidone or remove Ionized water is used as the first solvent, and the first mixed powder and the first solvent are mixed, and after stirring uniformly, a positive electrode slurry is obtained;

[0037] 3) Preparation of a positive electrode sheet: take the positive electrode slurry, uniformly coat it on the positive electrode current collector, dry, then place it on a roller press for rolling, and finally s...

Example Embodiment

[0042] Example 1

[0043] A lithium ion power battery includes a positive electrode sheet and a negative electrode sheet; the positive electrode sheet includes a positive electrode current collector and a positive electrode active material layer arranged on the surface of the positive electrode current collector; the negative electrode sheet includes a negative electrode current collector and is arranged on the The negative active material layer on the surface of the negative current collector. The formulations of the positive active material layer and the negative active material layer are shown in Table 1. The lithium ion power battery is prepared according to the following steps:

[0044] 1) Take the first active material, the first adhesive, the first conductive agent, the second active material, the second adhesive and the second conductive agent respectively in the formula amount, and bake them at 120°C for 12h, spare;

[0045] 2) Preparation of positive electrode slurry: ta...

Example Embodiment

[0051] Example 2

[0052] The difference between Example 2 and Example 1 lies in that the formulas of the positive active material layer and the negative active material layer are different, see Table 1 for details;

[0053] The preparation steps are different, including the following differences:

[0054] In step 1), the baking temperature is 125°C, and the baking time is 11h;

[0055] In step 2), the first solvent is deionized water, and the weight of the first solvent is 30% of the weight of the first mixed powder;

[0056] In step 3), the thickness of the positive electrode current collector is 13um, and the density of the positive electrode slurry on the positive electrode current collector is 2g / 100cm 2 ;

[0057] In step 4), the first solvent is deionized water, and the weight of the second solvent is 30% of the weight of the second mixed powder;

[0058] In step 5), the thickness of the negative electrode current collector is 12um, and the density of the negative electrode slurry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a lithium ion power battery. The lithium ion power battery comprises a positive plate and a negative plate, wherein the positive plate comprises a positive current collector and a positive active material layer arranged on the positive current collector; the positive current collector is prepared from the following components in percentages by weight: 85% to 98% of a first active material, 1% to 10% of a first binding material and 0.1% to 10% of a first conducting agent, wherein the first active material is nickel-cobalt-aluminum; the negative plate comprises a negative current collector and a negative active material layer arranged on the negative current collector; the negative active material layer is prepared from the following components in percentages by weight: 85% to 98% of a second active material, 1% to 10% of a second binding material and 0.1% to 10% of a second conducting agent, wherein the second active material is lithium titanate. The battery is high in capacity, good in rate capability, long in cycle life and high in safety performance. The invention also discloses a preparation method of the lithium ion power battery, and the preparation method is simple and safe in process, high in operability, green and environmentally-friendly.

Description

technical field [0001] The invention relates to the technical field of batteries, in particular to a lithium-ion power battery and a preparation method thereof. Background technique [0002] Lithium titanate (Li 4 Ti 5 o 12 ) is a new type of lithium-ion secondary battery anode material. During the intercalation or extraction of lithium ions, the Li 4 Ti 5 o 12 The crystal form will not change, and the volume change is less than 1%, so it is called "zero-strain material". cycle performance and service life. At 25°C, Li 4 Ti 5 o 12 The chemical diffusion coefficient is 2×10 -8 cm 2 / s, which is much higher than that of carbon anode materials, and the high diffusion coefficient makes this anode material fast charge and discharge. At the same time, Li 4 Ti 5 o 12 Its low temperature performance is good, its potential is higher than that of pure metal lithium, and it is not easy to produce lithium crystal dendrites, which provides a basis for ensuring the safety ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/36H01M4/485H01M4/525H01M4/62H01M10/0525H01M10/058B82Y30/00
CPCB82Y30/00H01M4/362H01M4/485H01M4/525H01M4/625H01M10/0525H01M10/058Y02E60/10Y02P70/50
Inventor 黄延新王保李亮乔晓宁
Owner SHENZHEN ZHUONENG NEW ENERGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products