Method for preparing vanadium-nitrogen alloy through stone coal vanadium extraction vanadium-rich liquid

A technology of vanadium-nitrogen alloy and vanadium liquid, which is applied in the field of vanadium-nitrogen alloy to achieve the effects of reducing production costs, short reaction time, and saving raw materials

Active Publication Date: 2017-04-26
WUHAN UNIV OF SCI & TECH
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, there are no relevant reports on the production of vanadium-nitrogen alloys using vanadium-enriched liquid for extracting vanadium from stone coal as raw material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The invention discloses a method for preparing a vanadium-nitrogen alloy by using a vanadium-rich solution for extracting vanadium from stone coal. The concrete steps of the method described in this embodiment are:

[0033] Step 1. Precursor preparation

[0034] The carbonaceous reducing agent is added into the vanadium-rich liquid, stirred at 60-80°C for 3-4h, and dried at 250-350°C for 30-90min to obtain a precursor.

[0035] The molar weight of the carbonaceous reducing agent is 1.5-2.5 times of the total molar weight of cations in the vanadium-rich liquid.

[0036] Step two, briquetting

[0037] Pressing the precursor to a density of 1.5-1.8g / cm 3 block, to obtain a block precursor.

[0038] Step 3. Reductive nitriding

[0039] Under the conditions of normal pressure and nitrogen flow rate of 100-400mL / min, the bulk precursor is heated to 1000-1200°C and kept for 3-5h; cooled to room temperature-100°C with the furnace, taken out of the furnace, crushed and grou...

Embodiment 2

[0050] The invention discloses a method for preparing a vanadium-nitrogen alloy by using a vanadium-rich solution for extracting vanadium from stone coal. The present embodiment except carbonaceous reducing agent, all the other are the same as embodiment 1.

[0051] The carbonaceous reducing agent is a mixture of graphite and activated carbon.

[0052] The vanadium-nitrogen alloy prepared in this example is measured: the vanadium content is 78.56~80.47wt%; the nitrogen content is 12.67~13.97wt%; the apparent density is 3.12~3.52g / cm 3 .

Embodiment 3

[0054] The invention discloses a method for preparing a vanadium-nitrogen alloy by using a vanadium-rich solution for extracting vanadium from stone coal. The concrete steps of the method described in this embodiment are:

[0055] Step 1. Precursor preparation

[0056] The carbonaceous reducing agent is added into the vanadium-rich liquid, stirred at 70-90°C for 2.5-3.5h, and dried at 250-350°C for 30-90min to obtain the precursor.

[0057] The molar weight of the carbonaceous reducing agent is 2.0-3.5 times of the total molar weight of cations in the vanadium-rich liquid.

[0058] Step two, briquetting

[0059] Pressing the precursor to a density of 1.6-1.9g / cm 3 block, to obtain a block precursor.

[0060] Step 3. Reductive nitriding

[0061] Under the conditions of normal pressure and nitrogen flow rate of 200-500mL / min, the bulk precursor is heated to 1100-1300°C and kept for 2-4h; cooled to room temperature-100°C with the furnace, taken out of the furnace, crushed an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
yield strengthaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing vanadium-nitrogen alloy through stone coal vanadium extraction vanadium-rich liquid. According to the technical scheme, a carbonaceous reducing agent is added into the vanadium-rich liquid, stirring and drying are conducted, and a precursor is obtained; the vanadium-rich liquid is an intermediate product of stone coal vanadium extraction; the molar weight of the carbonaceous reducing agent is 1.5-4 times the total molar weight of positive ions in the vanadium-rich liquid, the precursor is mechanically pressed into a block shape, at the ordinary pressure and a nitrogen atmosphere, the blocky precursor is subjected to heat preservation for 1-5 h under the condition of 1000-1400 DEG C, then cooled with a furnace and levigated, and a second intermediate product is obtained; a hydrochloric acid solution is added into the second intermediate product, stirring and solid-liquid separation are conducted, and solid slag is obtained; the molar weight of HCl in the hydrochloric acid solution is 3-5 times the total molar weight of positive ions except vanadium positive ions in the vanadium-rich liquid; and the solid slag is dried and briquetted, and the vanadium-nitrogen alloy is obtained. The method has the characteristics that the stone coal vanadium extraction vanadium-rich liquid is used as a vanadium source, the production cost is low, the raw material consumption is low, and the reaction time is short.

Description

technical field [0001] The invention belongs to the technical field of vanadium nitrogen alloys. Specifically, it relates to a method for preparing a vanadium-nitrogen alloy by using a vanadium-rich solution for extracting vanadium from stone coal. Background technique [0002] Vanadium-nitrogen alloy is a new type of alloy additive. It is alloyed with vanadium-nitrogen without adding other precious alloy elements. Under normal hot rolling conditions, high-strength steel with a yield strength of 550~600MPa can be obtained. Therefore, vanadium-nitrogen alloys have been widely used in the R&D and production of high-strength steel bars, non-quenched and tempered steels, tool steels and other products. [0003] The raw materials for the production of vanadium-nitrogen alloys are various vanadium-containing materials, including vanadium metal, vanadium pentoxide, vanadium tetroxide, vanadium trioxide, ammonium metavanadate, ammonium polyvanadate, and vanadium chloride. There ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C35/00C22C29/16C22C1/00
CPCC22C1/00C22C29/16C22C35/00
Inventor 张一敏韩静利刘涛黄晶陈铁军
Owner WUHAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka