Aluminum member surface microetching method, aluminum member complex and preparation method thereof

A technology of micro-etching and composites, applied in the field of materials, can solve the problems of unsatisfactory bonding between metal and resin or plastic, unsatisfactory bonding, harsh process conditions, etc., and achieve excellent structural firmness and light performance. Products The effect of stable quality and easy process control

Active Publication Date: 2017-05-10
OPD TECH SHENZHEN
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome the above-mentioned deficiencies of the prior art, to provide a method for micro-etching the surface of aluminum parts, to solve the problems of harsh process conditions and complicated reagents in the existing chemical etching method, and the formation of metal parts such as aluminum parts on the surface. The hole is relatively single, which makes the bonding force between metal and resin or plastic not ideal.
[0008] Another object of the present invention is to provide an aluminum composite body and its preparation method to solve the technical problem that the bonding force between the metal and the resin or plastic in the existing metal resin or plastic composite material is not ideal enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0053] Correspondingly, on the basis of the above-mentioned method for microetching the surface of an aluminum part and the aluminum part composite, the embodiment of the present invention also provides a method for preparing the above-mentioned aluminum part composite. In one embodiment, the preparation method of the aluminum composite body includes the following steps:

[0054] Step S04: Treat the surface of the aluminum part according to the micro-etching method described above to obtain an aluminum part with micropores etched on the surface;

[0055] Step S05: the process of placing the aluminum part etched with micropores on the surface into a binder solution to form a bonding layer, or directly coating the aluminum part with a bonding agent on at least the surface etched with micropores agent process;

[0056] Step S06: forming or pressing a plastic part or a resin part on the surface of the aluminum part provided with an adhesive layer.

[0057] Specifically, the meth...

Embodiment 1

[0064] A method for microetching the surface of an aluminum piece, comprising the following process steps:

[0065] S11. Degreasing treatment process: the purpose is to remove these impurities first, to ensure that the surface of the product can be fully infiltrated by the subsequent treatment liquid, so as to obtain uniform treatment.

[0066] Equipment: Treatment tank: CPVC, PVC, PP or mild steel tank lined with suitable plastic.

[0067]Heater: It can be heated with steam, titanium heating tube, stainless steel heating tube or quartz electric heating pencil.

[0068] Filtration: Use the oil stain removal management device to remove oil stains, and meet the minimum filtration cycle of 5-8 per hour.

[0069] Air stirring: Try to use filter to stir the tank solution.

[0070] Configure bath:

[0071] 1. Clean the treatment tank. If it is a new tank, it is necessary to pre-soak with acid and alkali for about 8 hours;

[0072] 2. Add 80% deionized water into the tank;

[00...

Embodiment 2

[0148] A method for microetching the surface of an aluminum piece, comprising the following process steps:

[0149] S21. Degreasing treatment process: parameters of the degreasing treatment process in Example 1.

[0150] Working parameters of degreasing treatment process: concentration of MICRO CLEAN 302 in degreasing solution: 50g / L, temperature during degreasing treatment: 65°C, time: 2.5min;

[0151] S22. Neutralization treatment procedure: the neutralization treatment procedure in Example 1 of parameters.

[0152] Working parameters of neutralization treatment process: MICRO NEO PR concentration in neutralization solution: 150ml / L, temperature during neutralization treatment: 10°C, time: 0.5min;

[0153] S23 Alkaline etching treatment process: parameters of the alkali etching treatment process in Example 1.

[0154] Working parameters of alkali etching treatment process: concentration of MICRO ETC 05 in alkali etching solution: 70g / L, temperature during alkali etching tr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides an aluminum member surface microetching method, an aluminum member complex and a preparation method thereof. The aluminum member surface microetching method comprises the following steps: performing pretreatment of oil removing, neutralizing treatment and alkali corrosion treatment in order on an aluminum member, microetching on the pre-treated surface of the aluminum member, forming micropore on the surface of the aluminum member; performing micropore washing treatment and pore enlarging treatment on the micropore formed on the surface of the aluminum member. The aluminum member complex comprises the aluminium member and a bonding member combined with the aluminum member, the aluminum member is processed by an aluminum member surface microetching method, the surface etched with the micropore is coated by a binder, and the aluminum member is bound with a plastic member or a resin piece. The aluminum member surface microetching method can generate various micropores on the surface of the aluminum member, and can effectively enhance the bonding strength between the aluminum member and other materials or the members such as resin or plastics.

Description

technical field [0001] The invention belongs to the technical field of materials, in particular to a method for microetching the surface of an aluminum part, an aluminum part composite and a preparation method thereof. Background technique [0002] With the development of electronic products in the world and the development of other industries that require lightweight materials such as the aviation industry, products are extending towards thinner and lighter. Therefore, there is an increasing demand for lightweight materials, but also higher requirements for the relevant mechanical properties of the corresponding materials. [0003] Among them, aluminum and its alloys are widely used due to their light weight and good mechanical properties. However, it still cannot meet the current pursuit of light and thin materials in related industries. In this context, metal composite materials came into being. [0004] A metal composite is a multiphase solid material that combines me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23F1/20
CPCC23F1/20
Inventor 唐国军
Owner OPD TECH SHENZHEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap