Dentritic two-dimensional palladium-silver nanosheet and preparation method thereof

A dendritic, nanosheet technology, applied in nanotechnology, nanotechnology, nanotechnology for materials and surface science, etc., can solve the problem of low particle size uniformity, difficulty in controlling the synthesis method of water-air interface, and poor catalytic performance. Take advantage of the multi-element nanocrystalline catalyst binary synergy and other issues to achieve the effects of mild experimental conditions, excellent photothermal conversion performance, and excellent electrocatalytic performance

Active Publication Date: 2017-05-31
SUZHOU UNIV
View PDF14 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese invention patent CN 104551009 B discloses a method for preparing two-dimensional dendritic silver nanosheets; Zheng et al. synthesized two-dimensional fractal gold nanosheets (Crystal Growth&Design, ( 2010). 10, 4701–4705), but the disadvantages of the prior art are: (1) the synthesis method of water-air interface is relatively difficult to control, and the particle size uniformity is not high; (2) the particle composition is single element, cannot exert the binary synergistic effect of multi-element nanocrystal catalysts in terms of catalytic performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dentritic two-dimensional palladium-silver nanosheet and preparation method thereof
  • Dentritic two-dimensional palladium-silver nanosheet and preparation method thereof
  • Dentritic two-dimensional palladium-silver nanosheet and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Add 40 mg of cetyltrimethylammonium chloride and 10 mL of water into a 25 mL round bottom flask, mix well, add 200 uL of silver acetate solution and chloropalladium acid solution with a concentration of 10 mM, and ultrasonically Process for 10 min. Under the condition of water bath at 30 ℃, stir and add 400 uL of trisodium citrate solution with a concentration of 100 mM, and stir for 4 hours to obtain a solution of dendritic palladium-silver nanosheet particles. For the transmission electron microscope picture, see the attached figure 1 , the particle diameter is about 60 nm, and the particle shape is dendritic.

[0023] See attached figure 2 , is the atomic force microscopy analysis of the nanosheets prepared in this example, wherein, the figure a is the scanning image of the atomic force microscope, and the figure b is the thickness of the corresponding tangent section in the figure a.

Embodiment 2

[0025] Add 60 mg of cetyltrimethylammonium chloride and 10 mL of water into a 25 mL round bottom flask, mix well, add 300 uL of 10 mM silver acetate solution and chloropalladium acid solution, and ultrasonically Process for 10 min. Under the condition of a water bath at 35°C, 400 uL of 100 mM trisodium citrate solution was added with stirring, and stirred for 4 hours to obtain a solution of dendritic palladium-silver nanosheet particles.

Embodiment 3

[0027] Add 40 mg of cetyltrimethylammonium chloride and 10 mL of water into a 25 mL round bottom flask, mix well, add 300 uL of silver nitrate solution and chloropalladium acid solution with a concentration of 10 mM, and ultrasonically Process for 10 min. Under the condition of a water bath at 30°C, 400 uL of 100 mM trisodium citrate solution was stirred and added, and stirred for 4 hours to obtain a dendritic palladium-silver nanosheet particle solution.

[0028] Carry out X-ray energy spectrum analysis to the nanoplate that present embodiment prepares, the result sees attached image 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a two-dimensional dentritic palladium-silver nanosheet. The method comprises dispersing the palladium precursor, the silver precursor, the surfactant and the reducing agent into a solvent to react, thereby preparing a two-dimensional dentritic palladium-silver nanosheet. The preparation method disclosed by the invention is directly prepared through a one-pot method, the experimental operation is simple, the reaction condition is mild, and the repeatability is high. The invention further discloses the two-dimensional dentritic palladium-silver nanosheet prepared by use of the above mentioned method; the particles form the palladium-silver alloy; the particles extend to the edge from the center and form the dentritic shap; the palladium-silver alloy nanosheet has both the two-dimensional morphology and the dentritic structure at the same time, the specific surface area and the surface exposed atoms of the material are improved, and the catalytic performance of the nanocrystal is facilitated.

Description

technical field [0001] The invention relates to a noble metal nanomaterial and a preparation method thereof, in particular to a two-dimensional dendritic palladium silver nanosheet and a preparation method thereof, belonging to the technical field of noble metal nanomaterials. Background technique [0002] In the fields of electricity, optics, heat, catalysis, etc., noble metal nanomaterials exhibit excellent and unique properties, so they have received extensive attention and in-depth research. The physical and chemical properties of nanosheets are related to their size and shape. The asymmetric structure and high specific surface area of ​​two-dimensional dendritic palladium-silver nanosheets make them exhibit excellent properties in infrared hyperthermia, catalysis, and many other aspects. , medical, biosensing and other fields have broad application prospects. [0003] Compared with other kinds of noble metal nanosheets, palladium or silver nanocrystals are important no...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22F9/24B22F1/00B82Y40/00B82Y30/00
CPCB82Y30/00B82Y40/00B22F9/24B22F1/0551B22F1/054
Inventor 程丝康小林
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap