Preparation method for normal-temperature rapid repairing material for municipal roads and bridges and construction step of preparation method

A technology for repairing materials and construction steps is applied in the field of preparation of rapid repairing materials at room temperature for municipal roads and bridges. The effect of large water volume and simple process

Inactive Publication Date: 2017-05-31
南通福伦利新材料有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Usually, a single polymer is used to improve its physical and mechanical properties, and often the bonding performance, high temperature resistance and other properties are improved, and its low temperature resistance and durability cannot be taken into account, and the research on multi-polymer composite modification is not enough.
[0006] (3) It is difficult to meet the opening-to-traffic requirements of rapid repairs such as large pits and large cracks
[0007] (4) Long setting time, poor construction effect, cumbersome operation, long repair and health maintenance period, affecting traffic opening
[0008] (5) The flatness of the ultra-thin repaired road is poor, which reduces the use function and aesthetics of the road surface
This brings confusion to the rapid repair of municipal roads and bridges, so it is imminent to develop new materials for normal temperature construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for normal-temperature rapid repairing material for municipal roads and bridges and construction step of preparation method
  • Preparation method for normal-temperature rapid repairing material for municipal roads and bridges and construction step of preparation method
  • Preparation method for normal-temperature rapid repairing material for municipal roads and bridges and construction step of preparation method

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0043] Such as figure 1 Shown, a kind of preparation method of normal temperature fast repair material for municipal road and bridge comprises the following steps:

[0044](1) Choose 42.5 ordinary Portland cement, special cement, mixed aggregate (select the corresponding gradation according to the thickness of the part used), cement polymer emulsion, retarder (determine the amount according to the transportation distance or construction time) , water, artificial or mechanical stirring at room temperature can quickly form strength, and can be closely combined with the old concrete structure to form a whole, with good crack resistance and freeze-thaw resistance;

[0045] The special cement is one of high-grade portland cement or special cement; the special cement is composed of the following components in parts by weight: 15 parts of powder anti-stripping agent, 15 parts of mineral powder, 10 parts of polymer rubber powder part and 50 parts of sulphoaluminate cement;

[0046] ...

specific Embodiment 2

[0057] Such as figure 1 Shown, a kind of preparation method of normal temperature fast repair material for municipal road and bridge comprises the following steps:

[0058] (1) Choose 42.5 ordinary Portland cement, special cement, mixed aggregate (select the corresponding gradation according to the thickness of the part used), cement polymer emulsion, retarder (determine the amount according to the transportation distance or construction time) , water, artificial or mechanical stirring at room temperature can quickly form strength, and can be closely combined with the old concrete structure to form a whole, with good crack resistance and freeze-thaw resistance;

[0059] The special cement is one of high-grade portland cement or special cement; the special cement is composed of the following components in parts by weight: 20 parts of powder anti-stripping agent, 20 parts of mineral powder, 20 parts of polymer rubber powder part and 70 parts of sulphoaluminate cement;

[0060]...

specific Embodiment 3

[0071] Such as figure 1 Shown, a kind of preparation method of normal temperature fast repair material for municipal road and bridge comprises the following steps:

[0072] (1) Choose 42.5 ordinary Portland cement, special cement, mixed aggregate (select the corresponding gradation according to the thickness of the part used), cement polymer emulsion, retarder (determine the amount according to the transportation distance or construction time) , water, artificial or mechanical stirring at room temperature can quickly form strength, and can be closely combined with the old concrete structure to form a whole, with good crack resistance and freeze-thaw resistance;

[0073] The special cement is one of high-grade Portland cement or special cement; the special cement is composed of the following components in parts by weight: 17 parts of powder anti-stripping agent, 18 parts of mineral powder, 14 parts of polymer rubber powder part and 63 parts of sulphoaluminate cement;

[0074]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method for a normal-temperature rapid repairing material for municipal roads and bridges and construction steps of the preparation method. According to the preparation method, a normal-temperature quick-strengthened asphalt composite emulsion is prepared by using a 'chemical network cross-linking emulsion technique', that is, a rapid normal-temperature composite emulsion-based repairing material for roads and bridges. The material is developed on the basis of modified emulsified asphalt and in addition is a high-tech environmental-friendly product which is particularly added with a tackifying and toughening aqueous polymer emulsion and is compounded under certain process conditions.

Description

technical field [0001] The invention belongs to the field of cement polymer emulsion, and in particular relates to a preparation method and construction steps of a normal-temperature rapid repair material for municipal roads and bridges. Background technique [0002] With the development of society, the traffic volume has increased significantly, and the transportation has the characteristics of "heavy load, large flow and channelized traffic". With the rapid growth of traffic volume and the aggravation of overloading and overloading, a large number of new roads have been open to traffic within 1-2 years, and early damages such as rutting, congestion and pushing have appeared to varying degrees. In order to keep the municipal roads in a good state of economic operation, the state requires frequent maintenance and repairs of the roads to prevent further aging and wear and tear of the roads. However, in urban centers with heavy municipal traffic and dense crowds, how to quick...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B24/26E01C11/00E01C7/14E01C7/18
CPCC04B28/06C04B24/2623C04B24/2676C04B2201/50E01C7/147E01C7/187E01C11/005C04B7/02C04B24/24C04B14/02C04B2103/0068C04B14/06C04B22/002C04B2103/22
Inventor 蔡海军瞿志军张建辉
Owner 南通福伦利新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap