Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

Straw processing fuel

A straw and fuel technology, applied in the field of straw processing fuel, can solve the problems of large wood consumption, long production cycle, small processing capacity, etc., and achieve the effect of improving biomass fuel with large ash content, short production cycle and large processing capacity

Inactive Publication Date: 2017-05-31
安徽润发生物能源科技有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the biomass fuel carbonization technology in the prior art basically uses wood to burn charcoal, and burning charcoal needs to consume a large amount of wood
In addition, the biological straw is first crushed into fine powder, then made into rods, and then sent to the carbonization furnace for carbonization. The disadvantages of this carbonization method are complex process, long production cycle, high cost, and small daily processing capacity of a single machine.
Therefore, most of the biological straw is directly used as waste and burned directly, resulting in a great waste of resources and environmental pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The following will clearly and completely describe the technical solutions in the embodiments of the present invention. Obviously, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0012] A fuel for straw processing, which comprises, in parts by weight, 40-50 parts of crushed straw, 30-40 parts of carbon powder, and 3-10 parts of adhesive.

[0013] Further, the crushed straw has a particle size of 10-150 mesh.

[0014] Further, the binder is a 1:1 mixture of bentonite and sodium silicate.

[0015] Further, 40 parts of the crushed straw, 35 parts of the carbon powder, and 6 parts of the binder.

[0016] Further, there are 45 parts of the crushed straw, 36 parts of the carbon powder, and 8 parts of the bin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a straw processing fuel, belonging to the technical field of straw processing fuels. The straw processing fuel is composed of the following components in parts by weight: 40 to 50 parts of crushed straw, 30 to 40 parts of carbon powder and 3 to 10 parts of an adhesive. The straw processing fuel provided by the invention has the advantages of simple process, short production period, low cost and large single-machine daily processing capacity; meanwhile, conventional waste biological straw in the rural area can be changed into treasure; and the disadvantage of large ash content of a biomass fuel of pure straw in the prior art is effectively improved.

Description

technical field [0001] The invention relates to straw processing fuel and belongs to the technical field of straw processing fuel. Background technique [0002] At present, the biomass fuel carbonization technology in the prior art basically uses wood to burn charcoal, and burning charcoal needs to consume a large amount of wood. In addition, the biological straw is first crushed into fine powder, then made into rods, and then sent to the carbonization furnace for carbonization. The disadvantages of this carbonization method are complex process, long production cycle, high cost, and small daily processing capacity of a single machine. Therefore, most of the biological straw is directly used as waste and burned directly, which causes a great waste of resources and also causes environmental pollution. Contents of the invention [0003] The technical problem to be solved by the present invention adopts the following technical solutions to realize: [0004] The beneficial ef...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10L5/44
CPCY02E50/10Y02E50/30C10L5/445
Inventor 夏银胜
Owner 安徽润发生物能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com