Water-based double-component polyurethane finish paint and preparation method thereof

A two-component polyurethane and water-based technology, applied in the field of coatings, can solve the problems of poor compatibility and achieve good compatibility, high cross-linking density of the paint film, and low VOC content

Inactive Publication Date: 2017-06-06
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF2 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The hydrophobic low-viscosity asymmetric isocyanate trimer, with 100% solid content and a viscosity lower than 1000mPa·s, can be directly added to the water-based paint system. Chemical properties are good, but there is still a problem of poor compatibility when manually stirring in actual use
[0007] At present, there is a lack of a water-based two-component polyurethane topcoat with high foam-free film thickness and good chemical resistance and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based double-component polyurethane finish paint and preparation method thereof
  • Water-based double-component polyurethane finish paint and preparation method thereof
  • Water-based double-component polyurethane finish paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of waterborne two-component polyurethane topcoat of the present invention, described waterborne twocomponent polyurethane topcoat is made up of A component and B component, and described A component is made up of following components by weight percentage:

[0029]

[0030]

[0031] B component is isocyanate curing agent.

[0032] The weight ratio of the A component and the B component is 4:1.

[0033] The curing agent is a mixture of hydrophilic polyisocyanate and hydrophobic low-viscosity asymmetric isocyanate trimer.

[0034] The mass ratio of the hydrophilic polyisocyanate to the hydrophobic low-viscosity asymmetric isocyanate trimer is 1:1.

[0035] The hydrophilic polyisocyanate is WL72-100 from Asahi Kasei, and the hydrophobic low-viscosity asymmetric isocyanate trimer is XP 2840 from Covestro.

[0036] The preparation method of waterborne two-component polyurethane topcoat of the present invention, comprises the steps:

[0037] (1) Preparation of ...

Embodiment 2

[0041] The difference between embodiment 2 and embodiment 1 is:

[0042] A kind of waterborne two-component polyurethane topcoat of the present invention, described waterborne twocomponent polyurethane topcoat is made up of A component and B component, and described A component is made up of following components by weight percentage:

[0043]

[0044]

[0045] B component is isocyanate curing agent.

[0046] The weight ratio of the A component and the B component is 6:1.

[0047] The mass ratio of the hydrophilic polyisocyanate to the hydrophobic low-viscosity asymmetric isocyanate trimer is 3:1. The hydrophilic polyisocyanate is WL72-100 from Asahi Kasei, and the hydrophobic low-viscosity asymmetric isocyanate trimer is XP 2840 from Covestro.

[0048] The preparation method of waterborne two-component polyurethane topcoat of the present invention, comprises the steps:

[0049] (1) Preparation of component A: add deionized water, wetting and dispersing agent, defoamer...

Embodiment 3

[0053] The difference between embodiment 3 and embodiment 1 is:

[0054]A kind of waterborne two-component polyurethane topcoat of the present invention, described waterborne twocomponent polyurethane topcoat is made up of A component and B component, and described A component is made up of following components by weight percentage:

[0055]

[0056] B component is isocyanate curing agent.

[0057] The weight ratio of the A component and the B component is 5:1.

[0058] The mass ratio of the hydrophilic polyisocyanate to the hydrophobic low-viscosity asymmetric isocyanate trimer is 4:1. The hydrophilic polyisocyanate is WL72-100 from Asahi Kasei, and the hydrophobic low-viscosity asymmetric isocyanate trimer is XP 2840 from Covestro.

[0059] The preparation method of waterborne two-component polyurethane topcoat of the present invention, comprises the steps:

[0060] (1) Preparation of component A: add deionized water, wetting and dispersing agent, defoamer, and pigment...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based double-component polyurethane finish paint and a preparation method thereof. The water-based double-component polyurethane finish paint is composed of a component A and a component B. The component A is composed of the following ingredients in percentage by weight: 10-15% of deionized water, 0.5-1.2% of wetting and dispersing agent, 0.1-0.5% of defoaming agent, 12-25% of pigment, 58-70% of water-based hydroxyacrylic acid dispersion, 0.5-1% of leveling agent, 0.1-0.5% of substrate wetting agent and 0.1-0.5% of rheologic assistant. The component B is an isocyanate curing agent. The water-based double-component polyurethane finish paint has the advantages of low VOC (volatile organic compound) content, high bubble-free film thickness and favorable chemical resistance. The paint film has high crosslinking density, and can not easily peel.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a water-based two-component polyurethane topcoat and a preparation method thereof. Background technique [0002] Water-based coatings are based on a variety of polymer resins and water is the dispersion medium. Compared with traditional solvent-based coatings, they have lower volatile organic compound (VOC) emissions and are green, safe and environmentally friendly coatings. my country is a big manufacturing country. A large amount of oil-based two-component polyurethane topcoat is used in machinery, rolling stock, steel structures and wooden furniture industries every year, which pollutes the surrounding environment and wastes oil resources to a great extent. At present, the water-based two-component polyurethane topcoat has the disadvantages of high VOC content, easy rash when sprayed, and poor chemical resistance of the paint film, so it is still difficult to popularize and apply it on...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C08G18/72C08G18/79C08G18/62
CPCC09D175/04C08G18/6216C08G18/721C08G18/79
Inventor 郭晓峰王瑞宏郭晓猛李幕英
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com