A kind of manufacturing method of bimetallic hot-dip coating steel plate and steel plate thereof

A manufacturing method and hot-dip plating technology, applied in hot-dip plating process, metal material coating process, coating and other directions, can solve the problems of high price, unsuitable for large-scale industrial production, etc., and achieve the effect of convenient and fast manufacturing

Active Publication Date: 2019-01-08
ANGANG STEEL CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] When used under some harsh conditions, a single coating cannot meet the requirements of use, so a double-layer coating has been developed, including methods such as painting on the coating, double-layer paint, etc. In this case, the double-metal coating It has also been developed, and the manufacturing methods include vacuum evaporation, magnetron sputtering, electroplating, etc., but these methods are either expensive or not suitable for large-scale industrial production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The bath of the traditional zinc pot is pure aluminum, the bath temperature is 690°C, the bath of the bottomless zinc pot is Zn+0.2%Al, the temperature is 460°C, the temperature of the strip steel entering the traditional zinc pot is 700°C, and the temperature of the bottomless zinc pot is 700°C. The temperature of the bottom zinc pot is 462°C, the thickness of the aluminum coating layer is 20 microns, and the thickness of the zinc coating layer is 10 microns. The coating structure is steel substrate - aluminum-iron alloy layer - aluminum coating layer - aluminum zinc alloy layer - galvanized layer.

[0016] The steel plate of the invention can work at a temperature of 450 DEG C, and its corrosion resistance is more than five times that of a galvanized steel plate with the same coating weight.

Embodiment 2

[0018] The bath of traditional zinc pot is pure aluminum, the bath temperature is 720°C, the bath of bottomless zinc pot is Zn+0.2%Al, the temperature is 450°C, the temperature of strip steel entering the traditional zinc pot is 710°C, and the temperature of the bottomless zinc pot is 710°C. The temperature of the bottom zinc pot is 455°C, the thickness of the aluminum coating layer is 30 microns, and the thickness of the galvanized layer is 15 microns. layer.

[0019] The steel plate of the invention can work at a temperature of 500 DEG C, and its corrosion resistance is more than five times that of a galvanized steel plate with the same coating weight.

Embodiment 3

[0021] The plating solution of the traditional zinc pot is 90% Al+10% Si, the bath temperature is 680°C, the bath of the bottomless zinc pot is Zn+2%Al+3%Mg, the temperature is 475°C, the strip enters the traditional zinc The temperature of the pot is 700°C, the temperature entering the bottomless zinc pot is 480°C, the thickness of the aluminum coating layer is 20 microns, the thickness of the zinc coating layer is 10 microns, and the coating structure is steel substrate-aluminum-iron alloy layer-aluminum coating Layer—aluminum-zinc alloy layer—galvanized aluminum-magnesium layer.

[0022] The steel plate of the invention can work at a temperature of 500 DEG C, and its corrosion resistance is more than 10 times that of a galvanized steel plate with the same coating weight. The coating can be used as a protective coating for hot-pressed steel to prevent high-temperature oxidation during heating and stamping and anti-corrosion during use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a double-metal hot dip coating steel plate manufacturing method and a steel plate thereof. The double-metal hot dip coating steel plate manufacturing method comprises the steps that the steel plate to be subjected to hot dip coating sequentially enters two zinc pots arranged on a continuous hot dip coating production line, and a double-metal coating of aluminum alloy and zinc alloy is obtained; the steel plate to be subjected to hot dip coating enters the traditional zinc pot with a sinking roller at first and then enters the electromagnetic force suspension bottomless type zinc pot arranged over the traditional zinc pot; the traditional zinc pot is internally provided with aluminum or aluminum-silicon alloy in a molten state; the bottomless type zinc pot is internally provided with zinc or zinc alloy in a molten state; and the coating structure of the double-metal hot dip coating steel plate is a steel substrate-an aluminum-iron alloy layer-an aluminized layer-an aluminum-zinc alloy layer-a galvanized layer. The steel plate produced through the manufacturing method has the sacrificial anode protective effect of a galvanized steel plate and also has the high temperature resistance of an aluminized steel plate, and the double-metal coating steel plate can be conveniently and rapidly manufactured.

Description

technical field [0001] The invention belongs to the field of continuous hot-dip coating of steel plates, and in particular relates to a method for manufacturing double-metal coated steel plates or steel strips. Background technique [0002] Steel plates are prone to corrosion and rust, and most of them require anti-corrosion treatment. The most common ones are galvanization, tin plating, nickel plating, painting, anti-corrosion coating, sacrificial anode, etc. Metal plating is the most common and effective way. Common plating methods include hot-dip plating, electroplating, vacuum evaporation, magnetron sputtering, spraying and other methods. [0003] When used under some harsh conditions, a single coating cannot meet the requirements of use, so a double-layer coating has been developed, including methods such as painting on the coating, double-layer paint, etc. In this case, the double-metal coating It has also been developed, and the manufacturing methods include vacuum ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C2/06C23C2/12
CPCC23C2/06C23C2/12
Inventor 吕家舜李锋杨洪刚周芳冯士杰肖宇
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products