Ultrahigh-strength low-alloy wear-resistant steel used for forging and preparation method thereof
An ultra-high-strength, forging technology, applied in the direction of casting molding equipment, metal processing equipment, manufacturing tools, etc., to achieve the effects of improving hardenability and wear resistance, strengthening hardenability, and low production costs
Inactive Publication Date: 2017-06-20
HUBEI WANXIN PRECISION CASTING & FORGING INC
View PDF5 Cites 9 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0007] Therefore, the present invention proposes an ultra-high-strength low-alloy wear-resistant steel for forging that can simultaneously meet the requirements of mechanical properties and reduce manufacturing costs, which solves the problems of the existing low-alloy wear-resistant steel
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0043] An ultra-high-strength low-alloy wear-resistant steel for forging, the main chemical composition and content of its material are as follows (wt.%):
[0044]
Embodiment 2
[0046] An ultra-high-strength low-alloy wear-resistant steel for forging, the main chemical composition and content of its material are as follows (wt.%):
[0047]
Embodiment 3
[0049] A kind of ultra-high-strength low-alloy wear-resistant steel for forging, the main chemical composition and content of its material are as follows (wt.%):
[0050]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Property | Measurement | Unit |
---|---|---|
elongation | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
hardness | aaaaa | aaaaa |
Login to view more
Abstract
The invention provides ultrahigh-strength low-alloy wear-resistant steel used for forging. Main chemical components of the material of the low-alloy wear-resistant steel include 0.20 wt.%-0.40 wt.% of C, 1.00 wt.%-1.55 wt.% of Si, 0.70 wt.%-1.00 wt.% of Mn, 1.00 wt.%-1.40 wt.% of Cr, 0.05 wt.%-0.20 wt.% of Mo, 0.05 wt.%-0.10 wt.% of Ni, 0.05 wt.%-0.20 wt.% of Cu, not larger than 0.035 wt.% of S, not larger than 0.035 wt.% of P and the balance Fe. The ultrahigh-strength low-alloy wear-resistant steel has the beneficial effects that by means of the ultrahigh-strength low-alloy wear-resistant steel, hardenability and wear resistance of the wear-resistant steel can be greatly improved; and the ultrahigh-strength low-alloy wear-resistant steel used for forging has ultrahigh strength, good tenacity, high hardness and good wear resistance at the same time, and the service life of the ultrahigh-strength low-alloy wear-resistant steel can be prolonged by three or more times compared with the service life of ordinary low-alloy wear-resistant steel. The invention further provides a preparation method of the ultrahigh-strength low-alloy wear-resistant steel used for forging, and it is ensured that the process is not complex and is easy to control and the production cost is low.
Description
technical field [0001] The invention relates to the field of metal materials, in particular to an ultra-high-strength low-alloy wear-resistant steel for forging suitable for bucket teeth and a preparation method thereof. Background technique [0002] Bucket teeth are the most severely worn parts in excavators and loaders in the construction machinery industry. They are widely used in mining, metallurgy, water conservancy, electric power, construction, machinery and other industries. They are in direct contact with rocks, minerals, sand, soil, etc. for a long time. The working conditions are harsh. When contacting the material, it bears both the impact force and the bending force. The tip of the bucket tooth is often subjected to strong impact and sliding abrasive wear. The main failure mode of the bucket tooth is wear and fracture. The surface of the bucket tooth Abrasion leads to breakage, resulting in short service life of bucket teeth and frequent replacement. At present...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/42C22C38/44C22C38/34C22C38/02C22C38/04B22C9/04C21D8/00C22C33/06C21C5/56C21D1/18E02F9/28
CPCB22C9/046C21C5/562C21D1/18C21D8/005C21D2211/001C21D2211/008C22C33/06C22C38/02C22C38/04C22C38/34C22C38/42C22C38/44E02F9/285Y02P10/20
Inventor 万继文张从阳王正刚李宜荣杨永红
Owner HUBEI WANXIN PRECISION CASTING & FORGING INC
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap