An electrothermal method and ferromolybdenum technology, applied in the field of metallurgy, can solve the problems of complex equipment cost, not conforming to the concept of energy-saving and environmental protection production, and large pollution of reaction products, and achieve the effects of low manufacturing cost, short preparation process cycle and simple equipment

Inactive Publication Date: 2017-06-30
SICHUAN DONGYU INFORMATION TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ferro-molybdenum alloys are currently prepared by the aluminothermic method. The heat sources are mainly aluminum and silicon. The equipment required is not only complicated but also expensive, and the reaction products pollute the environment. Therefore, it seriously does not meet the production concept of energy saving and environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Embodiment 1: a kind of technique of the present invention produces ferromolybdenum by electrothermal method, comprises the following steps: A, molybdenite is roasted to obtain molybdenum oxide ore; B, after molybdenum oxide ore is pulverized, add iron oxide powder, carbon powder and mix Uniform, the mass ratio of molybdenum oxide powder, iron oxide powder, and carbon powder is 3:1:1; C, add binder to the mixed powder and then press into block; D, put the block blank into a high-temperature electric furnace Ferromolybdenum can be obtained by smelting in the medium. The electric furnace used in the step D is a plasma electric furnace.

Embodiment 2

[0012] Embodiment 2: A kind of technique of the present invention produces ferromolybdenum by electrothermal method, comprises the following steps: A, molybdenite is roasted to obtain molybdenum oxide ore; B, after molybdenum oxide ore is pulverized, add iron oxide powder, carbon powder and mix Uniform, the mass ratio of molybdenum oxide powder, iron oxide powder, and carbon powder is 4:1:1; C, add binder to the mixed powder and then press into block; D, put the block into a high-temperature electric furnace Ferromolybdenum can be obtained by smelting in the medium. The electric furnace used in the step D is a plasma electric furnace.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a process for producing ferro-molybdenum through an electrothermal method. The process includes the following steps that A, molybdenite is roasted to obtain molybdenum oxide minerals; B, the molybdenum oxide minerals are smashed, ferric oxide powder and carbon powder are added into the smashed molybdenum oxide minerals for uniform mixing; C, a binder is added into mixed powder and then briquetting is performed; and D, a briquetted blank is put in a high-temperature electrothermal furnace to be smelted, and then the ferro-molybdenum can be obtained. By means of the process for producing the ferro-molybdenum through the electrothermal method, the molybdenite is roasted, powdered and uniformly mixed together with the ferric oxide powder and the carbon powder to obtain the mixture, the mixture is briquetted, smelting is performed through the high-temperature electrothermal furnace so as to obtain the ferro-molybdenum, equipment is simple, the period of the preparation process is short, the operation difficulty is low, the environment is protected, pollution is avoided, and the production and manufacturing cost is low.

Description

technical field [0001] The invention relates to a metallurgical method, in particular to a process for producing ferromolybdenum. Background technique [0002] Ferro-molybdenum alloys are currently prepared by the aluminothermic method. The heat sources are mainly aluminum and silicon. The equipment required is not only complicated but also expensive, and the reaction products pollute the environment. Therefore, it seriously does not meet the production concept of energy saving and environmental protection. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a process for producing molybdenum ferromolybdenum with simple required equipment and no pollution by electrothermal method. [0004] In order to solve the above technical problems, the present invention adopts the following technical solutions: [0005] A process for producing ferromolybdenum by electrothermal method, comprising the following steps: A, roasting...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22B4/06
CPCC22B4/06
Inventor 李成
Owner SICHUAN DONGYU INFORMATION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products