Solvent-free type polyurethane nanometer TiO2 composite membrane and preparation method thereof
A polyurethane film and solvent-free technology, which is applied in the field of solvent-free polyurethane nano-TiO2 composite film and its preparation, can solve problems such as poor water resistance, poor high temperature resistance, and ecological environment pollution, and achieve environmental pollution and product safety issues , Put an end to ecological environment pollution problems, and the effect of eliminating pollution sources
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
example 2
[0028] Weigh 5 parts by mass of polyethylene glycol (PEG) and 6 parts by mass of TiO 2 Add it into a three-necked flask equipped with a stirring device and a reflux condensing device, heat and stir at 50°C for 70 minutes, and use an ultrasonic cell pulverizer to ultrasonically disperse or emulsify and disperse for 15 minutes to make TiO 2 The nanoparticles are evenly dispersed. After the composite emulsion is cooled to room temperature, add 3 parts by mass of toluene diisocyanate (TDI), and stir evenly at high speed. Coat the composite emulsion on release paper fixed on a horizontal plate. Remove the release paper and dry it in an oven at 110°C to form a film.
example 3
[0030] Weigh 5 parts by mass of polyethylene glycol (PEG) and 7 parts by mass of TiO 2 Add them into a three-necked flask equipped with a stirring device and a reflux condensing device, heat and stir at 55°C for 75 minutes, and use an ultrasonic cell pulverizer to ultrasonically disperse or emulsify and disperse for 15 minutes to make TiO 2 The nanoparticles are evenly dispersed. After the composite emulsion is cooled to room temperature, add 3 parts by mass of toluene diisocyanate (TDI), and stir evenly at high speed. Coat the composite emulsion on release paper fixed on a horizontal plate. Remove the release paper and dry it in an oven at 110°C to form a film.
[0031] Compared with the traditional polyurethane synthesis process, the technology involved in the present invention has significantly improved water vapor permeability and air permeability. Polyurethane / nano TiO 2 The water vapor permeability of the composite membrane is increased by 20.27%, and the air permeabi...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com