Concrete antifreeze and anti-cracking agent

An anti-cracking agent and concrete technology, applied in the field of concrete anti-freezing and anti-cracking agent, can solve problems such as poor anti-freezing and anti-cracking performance, and achieve the effects of improving waterproof and impermeability, improving compactness and strength, and prolonging migration path.

Active Publication Date: 2019-06-21
YELLOW RIVER ENG CONSULTING +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides an antifreeze and anticrack agent for concrete, aiming to solve the problem of poor antifreeze and anticrack performance of existing concrete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Concrete antifreeze and anti-cracking agent
  • Concrete antifreeze and anti-cracking agent
  • Concrete antifreeze and anti-cracking agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The first step, drying: weigh an appropriate amount of muscovite powder (or phlogopite, the effect is equivalent to muscovite), and dry it in an oven at 105 ℃ for 48 hours to remove moisture; the above-mentioned muscovite powder is commercially available micron-level flake powder Material, of which SiO 2 The content is 62.4%, Al 2 O 3 The content is 20.4%.

[0021] The second step, grinding: use a high-fineness pulverizer to further pulverize the above-mentioned dried muscovite powder to obtain flake powder with a thickness of about 2.5μm in a microscopic state. When sieved with an 80μm cement negative pressure sieve, the residue Below 15%.

[0022] The third step, hydrophobic modification treatment: take 98 parts by weight of the muscovite powder prepared in the second step, add 1 part by weight of KH-550 silane coupling agent and 1 part by weight of methyl silicone oil, and send it to 150°C High temperature modification treatment is carried out in the powder surface modif...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a concrete anti-freezing and anti-cracking agent. The concrete anti-freezing and anti-cracking agent is formed by mixing 95 parts by weight of hydrophobic modified mica powder with 5 parts of nano silicon dioxide. Hydrophobic modified mica is prepared by a method comprising the following steps: first step, drying white mica or bronze mica; step two, pulverizing the white mica or the bronze mica into flaky micro-powder of which the granularity is 80 mu m, the screen residues are 15% or below and the thickness is 2.5 mu m; and third step, after mixing a silane coupling agent, methylsilicone oil and white mica powder or bronze mica powder which is prepared in the second step according to a formula, carrying out modification treatment on the mixture at the temperature of 150 DEG C, and the pulverizing the mixture to obtain the finished hydrophobic modified mica powder. The shrinkage of the concrete added with the anti-freezing and anti-cracking agent is greatly reduced, and the anti-cracking property is greatly improved.

Description

Technical field [0001] The invention relates to the technical field of concrete admixtures, in particular to a concrete anti-freezing and anti-cracking agent. Background technique [0002] The frost and crack resistance of concrete is an important index to evaluate the performance of concrete. [0003] When the ambient temperature decreases, the volume of the moisture in the concrete pores will increase by about 9% after freezing, forming water pressure. This pressure will not be released in the saturated concrete, which will cause damage. At present, air-entraining agents are often used to improve the frost resistance of concrete. Air-entraining agent can introduce a large number of uniformly distributed, stable and closed tiny bubbles during the mixing process. These tiny bubbles can accommodate the migration of free water, ease the water pressure when freezing, and significantly improve the concrete's ability to withstand repeated freezing and thawing. However, every time the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/42
CPCC04B40/0042C04B2103/601C04B14/20C04B14/06C04B24/42C04B20/008
Inventor 张金良房后国杨林陈学理
Owner YELLOW RIVER ENG CONSULTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap