Anti-wear coating for chemical pump

A wear-resistant coating, chemical pump technology, applied in the direction of epoxy resin coating, coating, pigment slurry, etc., can solve the problems of increased corrosion of chemical pump body, shortened life of chemical pump, coating surface wear, etc., to achieve wear-resistant performance improvement, wear resistance, stress dispersion effects

Inactive Publication Date: 2017-09-08
ANHUI LUYUAN PUMP&VALVE CO LTD
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chemical pumps not only need to have strong corrosion resistance, but also need to have a certain strength of wear resistance when transporting some special materials. However, most of the existing coatings have poor wear resistance. When transporting special materials After a long period of time, the problem of serious wear on the surface of the coating is prone to occur. After the coating of the chemical pump is worn, the corrosion of the special material to the chemical pump body increases, the corrosion intensifies, and the service life of the chemical pump is greatly shortened.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A wear-resistant coating for chemical pumps, comprising the following steps: it is prepared by mixing color paste and emulsion:

[0015] (1) Preparation of color paste: Put 12 parts of epoxy resin, 6 parts of pigment, 12 parts of glycerin, 0.2 parts of glyceryl tristearate, and 18 parts of deionized water into the dispersion pot by weight, and put them into the dispersion pot at 500r / min Stir for 4 hours, then stir for 15 minutes at a speed of 300r / min, and use a sand mill to grind to a fineness of ≤12 μm to obtain a color paste;

[0016] (2) Emulsion preparation: 10 parts of polyglycol, 3 parts of sodium lauryl sulfate, 1.2 parts of glycerol phosphate, 0.2 parts of polyoxypropylene triol, 2 parts of silicone oil, 0.14 parts of dibutyltin dilaurate in parts by weight parts evenly mixed together, then heated to 80°C, then added 0.45 parts of modified sericite powder, heated to 102°C, rotated at 380r / min for 3.5 hours, then stood for 2.5 hours, cooled to 60°C, added 0.26...

Embodiment 2

[0022] A wear-resistant coating for chemical pumps, comprising the following steps: it is prepared by mixing color paste and emulsion:

[0023] (1) Preparation of color paste: Put 14 parts of epoxy resin, 8 parts of pigment, 15 parts of glycerin, 0.6 parts of glyceryl tristearate and 20 parts of deionized water into the dispersion pot by weight, and put them into the dispersion pot at 800r / min Stir for 4 hours at high speed, then stir for 20 minutes at a speed of 400r / min, and grind to a fineness of ≤12 μm with a sand mill to obtain a color paste;

[0024] (2) Emulsion preparation: 13 parts of polyglycol, 5 parts of sodium lauryl sulfate, 1.6 parts of glyceryl phosphate, 0.6 parts of polyoxypropylene triol, 4 parts of silicone oil, 0.16 parts of dibutyltin dilaurate in parts by weight parts evenly mixed together, then heated to 100°C, then added 0.52 parts of modified sericite powder, heated to 105°C, rotated at 380r / min for 3.5 hours, then stood for 2.5 hours, cooled to 70°C,...

Embodiment 3

[0030] A wear-resistant coating for chemical pumps, comprising the following steps: it is prepared by mixing color paste and emulsion:

[0031] (1) Preparation of color paste: Put 13 parts of epoxy resin, 7 parts of pigment, 13 parts of glycerin, 0.4 parts of glyceryl tristearate, and 19 parts of deionized water into the dispersion pot by weight, and put them into the dispersion pot at 700r / min Stir at high temperature for 4 hours, then stir at 350r / min for 18 minutes, and use a sand mill to grind to a fineness of ≤12 μm to obtain a color paste;

[0032] (2) Emulsion preparation: 12 parts of polyglycol, 4 parts of sodium lauryl sulfate, 1.4 parts of glycerol phosphate, 0.4 parts of polyoxypropylene triol, 3 parts of organic silicone oil, 0.15 parts of dibutyltin dilaurate in parts by weight parts evenly mixed together, then heated to 90°C, then added 0.46 parts of modified sericite powder, heated to 103°C, rotated at 380r / min for 3.5 hours, then stood for 2.5 hours, cooled to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-wear coating for a chemical pump. The anti-wear coating is prepared according to the following step: mixing color paste with emulsion. By modification treatment of sericite powder, the surface of the sericite powder is covered by an organic group, so that the surface group property and the surface energy of the sericite powder can be effectively changed, and the compatibility between the modified sericite powder and other components in the coating can be fundamentally improved; by adding of isosorbide, the phenomenon that the sericite powder is easy to agglomerate can be improved, and the interfacial force between the sericite powder and a base body can be enhanced; therefore, the sericite powder can be dispersed more uniformly; in a friction process, damage within a relatively large range due to stress concentration can be avoided.

Description

technical field [0001] The invention belongs to the technical field of chemical pump coatings, in particular to a wear-resistant coating for chemical pumps. Background technique [0002] Chemical pumps are a general term for mechanical chemical pumps used to transport liquids and increase their pressure. They can meet the requirements of high temperature resistance, low temperature resistance, corrosion resistance, wear resistance, no leakage or less leakage, and pumps that can transport liquids in a critical state. These pumps are collectively referred to as chemical pumps. Chemical pumps not only need to have strong corrosion resistance, but also need to have a certain strength of wear resistance when transporting some special materials. However, most of the existing coatings have poor wear resistance. When transporting special materials After a long time, the problem of serious wear on the surface of the paint is prone to occur. After the paint of the chemical pump is wo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D171/02C09D183/04C09D163/00C09D17/00C09D7/12
CPCC09D171/02C08K2201/014C08L2205/025C08L2205/035C09D17/001C09D17/003C08L71/02C08L83/04C08L63/00C08K13/06C08K9/04C08K3/34C08K5/053C08K5/103C08K5/521
Inventor 凤元军
Owner ANHUI LUYUAN PUMP&VALVE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com