Preparation method of bubble-resistant box sealing tape

A tape and box sealing technology, applied in the direction of adhesives, film/sheet adhesives, adhesive types, etc., can solve the problems of poor water resistance of adhesives, loss of bonding properties, easy foaming of glue, etc., to achieve blister resistance Excellent performance, remarkable adhesion, excellent blister resistance

Inactive Publication Date: 2017-09-22
阜南县力韦包装材料有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the sealing tape made by this process has the following defects: one is that the conventional adhesive has poor water resistance, and once it is damp, the glue is prone to foaming and loses its bonding performance; The process of cutting into strips after gluing leads to shear stress at the edge of the tape, and the tape is very prone to flanging at the edge during use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A preparation method of blister-resistant sealing tape, comprising the following steps:

[0016] (1) Cut the BOPP film to a width of 48mm, then put it into the mixed solution, raise the temperature of the mixed solution to 40°C, and heat it for 5 minutes, wherein the mixed solution is made of the following components by weight: emulsification Agent OP-6 14 parts, ethanol 30 parts;

[0017] (2) After the BOPP film treated in step (1) is coated with an adhesive, it is naturally dried and rolled up to obtain a finished product, wherein the adhesive is made of the following components by weight: 80 parts of ethyl acrylate, cyclohexyl methacrylate 11 parts of ester, 0.1 part of chain extender HER, 1 part of diethylene glycol chloroformate, 8 parts of glyceryl ether acrylate, 1 part of N,N-dimethyl-m-toluidine, 1,1-cyclopropyl dicarboxylic acid 0.1 parts, 400 parts of methanol.

[0018] Specifically, the mixed solution in the above step (1) was prepared by the following met...

Embodiment 2

[0022] A preparation method of blister-resistant sealing tape, comprising the following steps:

[0023] (1) Cut the BOPP film to a width of 60mm, then put it into the mixed solution, raise the temperature of the mixed solution to 45°C, and heat it for 6 minutes, wherein the mixed solution is made of the following components by weight: emulsification Agent OP-6 16 parts, ethanol 35 parts;

[0024] (2) After the BOPP film treated in step (1) is coated with an adhesive, it is naturally dried and rolled up to obtain a finished product, wherein the adhesive is made of the following components by weight: 85 parts of ethyl acrylate, cyclohexyl methacrylate 13 parts of ester, 0.2 part of chain extender HER, 1 part of diethylene glycol chloroformate, 10 parts of glyceryl ether acrylate, 1 part of N,N-dimethyl-m-toluidine, 1,1-cyclopropyl dicarboxylic acid 0.3 parts, 430 parts of methanol.

[0025] Specifically, the mixed solution in the above step (1) was prepared by the following me...

Embodiment 3

[0029] A preparation method of blister-resistant sealing tape, comprising the following steps:

[0030] (1) Cut the BOPP film to a width of 72mm, then put it into the mixed solution, raise the temperature of the mixed solution to 50°C, and heat it for 7 minutes, wherein the mixed solution is made of the following components by weight: emulsification Agent OP-6 18 parts, ethanol 40 parts;

[0031] (2) After the BOPP film treated in step (1) is coated with an adhesive, it is naturally dried and rolled up to obtain a finished product, wherein the adhesive is made of the following components by weight: 90 parts of ethyl acrylate, cyclohexyl methacrylate 16 parts of ester, 0.3 parts of chain extender HER, 2 parts of diethylene glycol chloroformate, 12 parts of glyceryl ether acrylate, 2 parts of N,N-dimethyl-m-toluidine, 1,1-cyclopropyl dicarboxylic acid 0.4 parts, 450 parts of methanol.

[0032] Specifically, the mixed solution in the above step (1) was prepared by the following...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a bubble-resistant box sealing tape. The preparation method comprises the following operation steps: (1) cutting a biaxially-oriented polypropylene (BOPP) thin film so as to enable the thin film to have a width of 48-72mm; then, putting the cut BOPP thin film into a mixed solution, heating the mixed solution up to 40-50 DEG C, and carrying out heat insulation treatment for 5-7min; (2) coating the BOPP thin film treated in the step (1) with an adhesive, then naturally drying, and winding to obtain a finished product. The bubble-resistant box sealing tape prepared by the method provided by the invention is high in adhesive property, and all performance indexes of the bubble-resistant box sealing tape meet the JB / T 10456-2004 industry requirements; furthermore, the bubble-resistant box sealing tape is excellent in bubble resistance, thus not having the phenomenon of blistering and the like after being wetted.

Description

technical field [0001] The invention belongs to the field of preparation of sealing tapes, in particular to a method for preparing blister-resistant sealing tapes. Background technique [0002] Sealing tape is also called BOPP tape, packaging tape, etc. It is based on BOPP biaxially oriented polypropylene film, and is evenly coated with pressure-sensitive adhesive emulsion after heating to form a glue layer ranging from 8 μm to 28 μm. It is an indispensable product in the life of light industry enterprises, companies and individuals. The common preparation method of sealing tape is as follows: after the BOPP original film is treated with high-voltage corona, one side of the surface is roughened, and then the glue is applied on it to form a tape master roll, and then cut into different specifications by a slitting machine. The small roll is the tape we use every day. The pressure-sensitive adhesive emulsion is mainly composed of butyl ester. However, the sealing tape made b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/02C09J133/08C08F220/18C08F220/32
CPCC08F220/18C08F222/18C09J133/08C09J2301/122C09J2301/302C09J2301/312C09J2423/106C09J2433/00C08F220/325
Inventor 王文朝
Owner 阜南县力韦包装材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com