Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

Method for preparing antibacterial ecological composite board

A composite board and ecological technology, which is applied in the field of preparation of antibacterial ecological composite boards, can solve the problems of easy cracking, poor antibacterial properties, and inability to use the whole root, and achieves good anti-cracking performance, good antibacterial properties, and reduced breeding effects.

Inactive Publication Date: 2017-09-26
安徽省科晟生态木装饰材料有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, there are very few decorative substrates using bamboo as raw material. Due to the rapid growth of bamboo in the later period and the large output, there are not many levels of deep processing at present, mainly in the field of tables and chairs. Due to the physiological characteristics of bamboo, it is impossible to whole In use, the broken bamboo is usually bonded with glue to prepare ecological boards. Although it is widely used, it has poor antibacterial properties and is easy to crack.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A preparation method for an antibacterial ecological composite board, comprising the steps of:

[0017] S1, pulverizing the bamboo and drying until a prefabricated material is obtained;

[0018] S2. Add cellulose gel to the prefabricated material, then add polyethylene glycol and water to mix evenly, heat up, keep warm, cool down, then add titanium dioxide, disproportionated rosin, polyurethane binder, mix evenly, put it into the mold for pre-pressing , molding, and natural air-drying to obtain an antibacterial ecological composite board.

Embodiment 2

[0020] A preparation method for an antibacterial ecological composite board, comprising the steps of:

[0021] S1, pulverizing the bamboo, drying to a moisture content of 3wt%, to obtain a prefabricated material;

[0022] S2. Add 30 parts of cellulose gel to 80 parts of prefabricated materials in parts by weight, then add 160 parts of polyethylene glycol and 40 parts of water and mix evenly, heat up to 135°C, keep warm for 3 hours, cool, then add 12 parts of titanium dioxide, 4 parts of disproportionated rosin and 35 parts of polyurethane adhesive are mixed evenly, put into a mold, paved and pre-pressed, shaped, and naturally air-dried to obtain an antibacterial ecological composite board.

Embodiment 3

[0024] A preparation method for an antibacterial ecological composite board, comprising the steps of:

[0025] S1, pulverizing the bamboo, drying to a moisture content of 5wt%, to obtain a prefabricated material;

[0026] S2. Add 20 parts of cellulose gel to 90 parts of prefabricated materials in parts by weight, then add 120 parts of polyethylene glycol and 80 parts of water and mix evenly, heat up to 125 ° C, keep warm for 5 hours, cool, and then add 6 parts of titanium dioxide, 8 parts of disproportionated rosin and 25 parts of polyurethane adhesive are mixed evenly, put into a mold, paved and pre-pressed, shaped, and naturally air-dried to obtain an antibacterial ecological composite board.

[0027] The cellulose gel is prepared by the following process: uniformly mix beef extract, corncob powder, glucose, and water, inoculate Gluconacetobacter xylinum, culture dynamically on a shaker, filter, and wash to obtain the cellulose gel.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing an antibacterial ecological composite board. The method comprises the following steps: grinding bamboo wood, and drying so as to obtain a prefabricated material; adding cellulose gel into the prefabricated material, adding polyethylene glycol and water for uniform mixing, raising the temperature, maintaining the temperature, and cooling; adding titanium dioxide, disproportionated rosin and a polyurethane adhesive for uniform mixing, paving and pre-pressing in a mold, molding, and naturally airing, so as to obtain the antibacterial ecological composite board. The cellulose gel is prepared by the following process steps: uniformly mixing beef extract, corncob powder, glucose and water, inoculating gluconacetobacter xylinus, performing dynamic culture in a shake table, filtering, and washing, so as to obtain the cellulose gel. The prepared antibacterial ecological composite board is excellent in antibacterial property, high in product density and difficult to crack.

Description

technical field [0001] The invention relates to the technical field of ecological composite boards, in particular to a preparation method of an antibacterial ecological composite board. Background technique [0002] At present, there are few decorative substrates using bamboo as raw material. Due to the rapid growth of bamboo in the later period and the large output, there are not many levels of deep processing at present, mainly in the field of tables and chairs. Due to the physiological characteristics of bamboo, it is impossible to complete the whole In use, the broken bamboo is usually bonded with glue to prepare ecological boards. Although it is widely used, it has poor antibacterial properties and is easy to crack. Contents of the invention [0003] Based on the technical problems in the background technology, the present invention proposes a method for preparing an antibacterial ecological composite board. The obtained ecological composite board has good antibacteri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L71/02C08L97/02C08L1/02C08L93/04C08L75/04C08K3/22B27N3/00B27N3/02C12P19/04C12R1/02
CPCC08L71/02B27N3/002B27N3/02C08K2003/2241C08L2205/035C08L2205/16C12P19/04C08L97/02C08L1/02C08L93/04C08L75/04C08K3/22
Inventor 吴万水
Owner 安徽省科晟生态木装饰材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com