A kind of interlayer inorganic pipeline and preparation method thereof

A pipeline and inorganic technology, applied in the field of interlayer inorganic pipelines and its preparation, can solve the problems of unsuitable interlayer conveying pipelines, unstable quality, length limitation, etc., and achieve the effects of easy promotion and application, improved curing quality, and improved mechanical properties

Active Publication Date: 2019-01-22
SUZHOU SHINWU OPTRONICS TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to reduce the joints connecting engineering pipelines, the transmission pipeline has to meet the specification requirements of a certain length, but the existing technology and equipment for preparing laminated flat glass have strict restrictions on the length of the prepared products, which is not suitable for the production of interlayer transmission pipelines
[0005] In addition, the existing method of producing laminated flat glass adopts the operation of edge sealing and swing method or vacuum kettle method to remove the air bubbles in the middle layer. The operation of air removal is not only cumbersome, inefficient, but also unstable in quality
The swing method is to use the buoyancy of the bubbles in the prepolymer and the centrifugal force that rises with the swing of the entire flat glass to be eliminated. It is not easy to get rid of the viscous slurry; the vacuum kettle method not only vacuumizes the middle layer, but also requires the entire space in the vacuum kettle to reach a certain degree of vacuum, so it takes a long time for vacuuming and consumes a lot of energy.
[0006] The process and equipment for preparing laminated flat glass by the existing method cannot eliminate the curing exotherm or heat the curing in time, and the curing of the prepolymer requires a strict "temperature-time" system to improve the curing quality of the intermediate layer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of interlayer inorganic pipeline and preparation method thereof
  • A kind of interlayer inorganic pipeline and preparation method thereof
  • A kind of interlayer inorganic pipeline and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0044] A method for preparing an interlayer inorganic pipeline, comprising the steps of:

[0045] 1) Add organic monomers or polymer resins into the reaction kettle, and according to the material performance and According to the requirements of process performance, select diluent, initiator, coupling agent and other auxiliary agents; initiate polymerization and control the conversion rate of monomer; add inorganic modified powder treated with or without coupling agent under high-speed stirring, and prepolymerize The mass ratio of body and inorganic modified powder is 1:0.01~3.0, and then vacuum degassing or not to obtain slurry;

[0046] 2) Rinse and clean the inorganic pipeline with conventional cleaning agent solution and water and dry it;

[0047] 3) The first diameter pipe 7 and the second diameter pipe 8 are nested together to form a set of nested inorganic pipes; wherein, the first diameter pipe 7 and the second diameter pipe 8 are inorganic pipes with a diameter differ...

example 1

[0059] Step 1) Add a certain amount of polymer monomers, diluents, initiators, coupling agents, curing agents and other additives into the reactor to initiate polymerization and control the conversion rate of monomers; Inorganic modified powder treated with coupling agent, the mass ratio of prepolymer and inorganic modified powder is 1:0.01~3.0, and then vacuum degassing or not to obtain slurry;

[0060] Step 2) washing and drying the borosilicate glass pipes or silicate glass pipes of the first diameter pipe 7 and the second diameter pipe 8 with cleaning agent solution and water;

[0061] Step 3) nesting the first diameter pipe 7 and the second diameter pipe 8 together to form a set of nested inorganic pipes; wherein, the first diameter pipe 7 and the second diameter pipe 8 are inorganic pipes with a diameter difference greater than 1.0 mm;

[0062] Step 4) Put one or more U-shaped ring grooves 11 of the upper elastic rubber sealing ring 1 with a height of 20-40mm on the uppe...

example 2

[0068] Step 1) First add methyl acrylate, dibutyl ester, benzoic acid, silane, benzoyl peroxide, coupling agent and other auxiliary agents in the reaction kettle according to the weight ratio to initiate polymerization and control the monomer conversion rate; high-speed stirring Next, add inorganic modified powder treated with or without coupling agent, the mass ratio of prepolymer and inorganic modified powder is 1:0.01~3.0, and then vacuum degassing or not to obtain slurry;

[0069] Step 2) Rinse and dry lithium-aluminosilicate glass-ceramic pipes of different diameters, and / or borosilicate glass or silicate glass pipes with cleaning agent solution and water;

[0070] Step 3) nesting the first diameter pipe 7 and the second diameter pipe 8 together to form a set of nested inorganic pipes; wherein, the first diameter pipe 7 and the second diameter pipe 8 are inorganic pipes with a diameter difference greater than 1.0 mm;

[0071] Step 4) Cover the U-shaped ring groove 11 of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
collision energyaaaaaaaaaa
impact strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sandwich inorganic pipeline, which belongs to the technical field of pipeline transportation, and comprises two pipelines with different diameters, a first diameter pipeline and a second diameter pipeline. The second diameter pipeline is set on the outer periphery of the first diameter pipeline to form a sandwich inorganic pipeline. A central hole is formed in the diameter pipe, an interlayer is formed between the first diameter pipe and the second diameter pipe, and the interlayer is filled with slurry to solidify to form a polymer intermediate layer; wherein, the slurry includes prepolymer and inorganic modified powder, prepolymer The mass ratio of polymer and inorganic modified powder is 1:0.01-3.0. The invention also discloses a preparation method of the interlayer inorganic pipeline. In the present invention, inorganic modified powder is added to the prepolymer, and the mechanical properties are significantly improved; the prepolymer can be polymerized and solidified in a more accurate and stable environment, and the curing quality is improved; the preparation method of the present invention has a simple process , easy to promote and apply, and has good practicability.

Description

technical field [0001] The invention belongs to the technical field of pipeline transportation, and in particular relates to a sandwich inorganic pipeline and a preparation method thereof. Background technique [0002] Metal pipelines are widely used in the field of transportation technology, but the corrosion resistance of metal pipelines is not as good as that of inorganic materials, especially in the occasions of transporting highly corrosive liquids, gases and powders, while inorganic material pipelines can transport hydrofluoric acid and Any corrosive substances other than hot phosphoric acid; some metal pipes containing heavy metals will also pollute the conveying objects, while inorganic material pipes will not; however, inorganic materials are brittle, such as glass pipes are well-known representatives of typical brittle materials, The impact resistance is poor, and the medium pressure resistance does not exceed 0.6MPa, which limits its application in the pipeline tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F16L9/14B32B1/08B32B27/18B32B27/06B32B17/10B32B9/04B32B7/12B32B37/12B32B37/00
CPCF16L9/14B32B1/08B32B7/12B32B9/045B32B27/06B32B27/18B32B37/00B32B37/12B32B2597/00B32B2307/50B32B17/10036B32B17/10614B32B17/10761
Inventor 程俊华韩朋德陈华蔡树元吴浪
Owner SUZHOU SHINWU OPTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products