Graded gravel mixture
A technology for grading gravel and mixing materials, which is applied in the direction of buildings, roads, and coagulating pavements laid on site. Effects of stability, improved strength, and improved mechanical properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0021] Example 1
[0022] Weigh the titanium dioxide into the muffle furnace, heat it up to 600℃, calcinate at a high temperature for 6 hours, take it out and cool it, pour it into a mortar and grind it into powder to obtain activated nano-titanium dioxide powder; select 80 parts by weight of 3~25mm. Graded crushed stone particles, 20 parts of expanded graphite, 5 parts of activated nano titanium dioxide powder, 5 parts of iron tailings slag, 10 parts of quartz sand, 2 parts of sodium nitrate and 3 parts of barium nitrate, put them in a high-speed mixer and mix them evenly. Mixture: Divide the mixture into 3 parts, and grind them in a grinder, respectively, and grind them into three particle sizes of 0.8mm, 5mm, and 20mm. After mixing, the aggregate raw materials are obtained; Weigh the epoxy resin and add it to the reaction kettle, heat up to 85°C, keep stirring for 20 minutes, then add 30% absolute ethanol by weight of epoxy resin and 15% ethylene glycol monobutyl ether by weig...
Example Embodiment
[0023] Example 2
[0024] Weigh the titanium dioxide into the muffle furnace, heat it up to 600℃, calcinate at a high temperature for 6 hours, take it out and cool it, pour it into a mortar and grind it into powder to obtain activated nano-titanium dioxide powder; select 80 parts by weight of 3~25mm. Graded crushed stone particles, 20 parts of expanded graphite, 5 parts of activated nano titanium dioxide powder, 5 parts of iron tailings slag, 10 parts of quartz sand, 2 parts of sodium nitrate and 3 parts of barium nitrate, put them in a high-speed mixer and mix them evenly. Mixture: Divide the mixture into 3 parts, and grind them in a grinder, respectively, and grind them into three particle sizes of 0.8mm, 5mm, and 20mm. After mixing, the aggregate raw materials are obtained; Weigh the epoxy resin and add it to the reaction kettle, heat up to 85°C, keep stirring for 20 minutes, then add 30% absolute ethanol by weight of epoxy resin and 15% ethylene glycol monobutyl ether by weig...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap