Preparing method for sodium alginate wound application with thrombin
An alginate and thrombin technology, applied in the field of medical care, can solve the problems of inability to moisturise wounds, stop bleeding, apply a single core, and cannot meet the needs of clinical doctors and patients, so as to promote wound healing and reduce sensitization. rate, the effect of increasing the contact area
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0032] Example 1:
[0033] A preparation method of alginate wound dressing with thrombin, the preparation process is as follows:
[0034] (1) Configure the ethanol aqueous solution of thrombin, the volume ratio of ethanol to water is 2:1, and the thrombin content is 50 units / ml;
[0035] (2) Put the long alginate fiber into a reaction tank containing thrombin ethanol water solution for constant temperature soaking. The reaction tank is equipped with an "S" channel, the soaking time is 0.5h, and the temperature is 30°C;
[0036] (3) After soaking, pull the long fiber bundles out of the reaction tank and dry them in an oven at a drying temperature of 35°C and a drying time of 1h;
[0037] (4) After drying, cut into a certain length of alginate short fibers with thrombin, and crimp the short fibers. The length of the cut short fibers is 38mm, and the number of crimps is 3 / cm;
[0038] (5) The short fiber is woven into a non-woven fabric through non-woven processes such as opening, carding, ...
Example Embodiment
[0042] Example 2:
[0043] A preparation method of alginate wound dressing with thrombin, the preparation process is as follows:
[0044] (1) Configure the ethanol aqueous solution of thrombin, the volume ratio of ethanol to water is 3:1, and the thrombin content is 100 units / ml;
[0045] (2) Put the long alginate fiber into a reaction tank containing thrombin ethanol water solution for constant temperature soaking. The reaction tank is equipped with an "S" channel, the soaking time is 1h, and the temperature is 35℃;
[0046] (3) After soaking, pull the long bundle of fibers out of the reaction tank and dry in an oven at a drying temperature of 37°C and a drying time of 2h;
[0047] (4) After drying, cut into a certain length of alginate short fiber with thrombin, and crimp the short fiber, the length of the cut short fiber is 60mm, and the number of crimps is 4 / cm;
[0048] (5) The short fiber is woven into a non-woven fabric through non-woven processes such as opening, carding, netting...
Example Embodiment
[0052] Example 3: Hemostatic performance test
[0053] Test group: The product prepared in Example 2 is selected as the test group;
[0054] Control group: Gauze hemostatic products on the market are the control group.
[0055] The test steps are as follows:
[0056] (1) According to 1ml / kg, slowly inject 3% sodium pentobarbital into the ear vein of the rabbit for anesthesia, then put a wound towel on the left ventral side of the rabbit, and disinfect the surgical site with iodine and 75% alcohol.
[0057] (2) Make a 5.0cm longitudinal incision along the left inner edge, about 1cm to the left of the mid-abdominal line, cut the abdominal muscles to the peritoneum, and cut the peritoneum.
[0058] (3) Use 2 fingers or tweezers to find out the spleen of the rabbit, and use normal saline to keep the spleen moist.
[0059] (4) Blank control group: On the spleen surface, use a scalpel to make two symmetrical wounds 1 cm long and 1 mm deep along the long axis of the spleen, with active bleeding ...
PUM
Property | Measurement | Unit |
---|---|---|
Length | aaaaa | aaaaa |
Gram weight | aaaaa | aaaaa |
Aperture | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap