A technology of protein scaffold and silk fibroin, which is applied in the field of biomedical engineering materials to achieve the effects of improved resolution, clear magnetic resonance imaging maps, and easy access to raw materials

Active Publication Date: 2017-12-01
BEOGENE BIOTECH GUANGZHOU
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Based on this, in order to overcome the defects of the above-mentioned existing tissue engineering scaffolds, the present

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bone-induced composite silk fibroin stent for MRI sialography and preparation method thereof
  • Bone-induced composite silk fibroin stent for MRI sialography and preparation method thereof
  • Bone-induced composite silk fibroin stent for MRI sialography and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Example 1 Osteoinductive composite silk fibroin scaffold for MRI imaging and preparation method thereof

[0036] The preparation method of the osteoinductive composite silk fibroin scaffold for MRI imaging of the present embodiment comprises the following steps:

[0037] (1), take 8g silkworm cocoons and place them in a large beaker, add 400ml deionized water, and add 2gNaHCO at the same time 3 Sodium acid, boiled at 100°C for 30 minutes, taken out, washed several times with deionized water until neutral, boiled again and taken out, washed and dried in an oven at 50°C to obtain silk fibroin for use;

[0038](2), take 2.5g silk fibroin and add 25ml 9.3mol / L lithium bromide solution, after heating in a water bath at 60°C for 5h, dialyze with a dialysis bag (the molecular weight cut-off of the dialysis bag is 8kD, dialyze for 3 days, change the water 3 times a day ), and then at 25°C, centrifuged at 5000r / min for 10min, the obtained silk fibroin solution was reverse dialy...

Embodiment 2

[0042] Example 2 Osteoinductive composite silk fibroin scaffold for MRI imaging and its preparation method

[0043] The osteoinductive composite silk fibroin scaffold for MRI imaging of the present embodiment and the preparation method thereof comprise the following steps:

[0044] (1), take 8g silkworm cocoons and place them in a large beaker, add 400ml deionized water, and add 2g NaHCO at the same time 3 , the temperature reached 100°C, boiled for 30 minutes, took it out, washed it several times with deionized water until it was neutral, boiled it again and took it out, washed it and put it in an oven at 50°C to dry to obtain silk fibroin for use;

[0045] (2) Add 2.5g of silk fibroin to 25ml of 9.3mol / L lithium bromide solution, heat it in a water bath at 60°C for 5 hours, then dialyze with a dialysis bag (the molecular weight cut-off of the dialysis bag is 8kD and dialyze for 3 days, change the water 3 times a day) , and then at 25°C, centrifuged at 5000r / min for 10min, t...

Embodiment 3

[0049] Example 3 Osteoinductive composite silk fibroin scaffold for MRI imaging and its preparation method

[0050] The osteoinductive composite silk fibroin scaffold for MRI imaging of the present embodiment and the preparation method thereof comprise the following steps:

[0051] (1), take 8g silkworm cocoons and place them in a large beaker, add 400ml deionized water, and add 2g NaHCO at the same time 3 , the temperature reached 100°C, boiled for 30 minutes, took it out, washed it several times with deionized water until it was neutral, boiled it again and took it out, washed it and put it in an oven at 50°C to dry to obtain silk fibroin for use;

[0052] (2) Add 2.5g of silk fibroin to 25ml of 9.3mol / L lithium bromide solution, heat it in a water bath at 60°C for 5 hours, then dialyze with a dialysis bag (the molecular weight cut-off of the dialysis bag is 8kD and dialyze for 3 days, change the water 3 times a day) , and then at 25°C, centrifuged at 5000r / min for 10min, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Volumeaaaaaaaaaa
Average pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a bone-induced composite silk fibroin stent for MRI sialography and a preparation method thereof. The volume of the composite silk fibroin stent is 1. 5-2. 0 mm<3>, and the composite silk fibroin stent is loaded with 3*10<5> - 7*10<5> dental pulp stem cells; and the composite silk fibroin stent is prepared by taking a dispersing solution as a raw material, wherein the dispersing solution is formed by 2-10% of silk fibroin solution, hydroxyapatite and ultra paramagnetic ferroferric oxide. According to the bone-induced composite silk fibroin stent for MRI sialography, the composite silk fibroin stent has suitable pore size and porosity, adhesion and proliferation of the dental pulp stem cells are facilitated, the problems of an existing stent material are solved, various substances are compounded, the advantage of the original substance is maintained, the deficiency of the single original material performance is overcome, the preparation process is simple, the required raw materials are easy to obtain, the prepared composite stents are expected to be widely used in the biomaterial field; and as the marker of the tissue engineering stent, the ultra paramagnetic ferroferric oxide is expected to be applied to clinical medicine.

Description

technical field [0001] The invention belongs to the field of biomedical engineering materials. Specifically, the invention relates to an osteoinductive composite silk fibroin scaffold for MRI imaging and a preparation method thereof. Background technique [0002] With the development of imaging technology, various functional imaging studies have emerged. Magnetic resonance imaging (MRI) has been effectively used to monitor tissue engineering scaffolds because of its non-invasiveness, safety, and rich diagnostic information. The use of contrast agents can effectively improve the sensitivity and specificity of magnetic resonance diagnosis, enhance the signal contrast and improve the resolution of soft tissue images. Superparamagnetic iron tetroxide is a kind of nanoparticles with paramagnetism and significant negative effect, which has become a research hotspot in the field of magnetic resonance imaging. [0003] Dental pulp stem cells (DPSCs) have stem cell characteristics ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L27/22A61L27/38A61L27/12A61L27/02A61L27/50A61K49/08
CPCA61K49/08A61L27/025A61L27/12A61L27/227A61L27/3834A61L27/50A61L2300/112A61L2300/252A61L2300/412
Inventor 郭瑞李丹蓝咏
Owner BEOGENE BIOTECH GUANGZHOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap