Building decoration material

A technology of building decoration materials and raw materials, which is applied in the field of building materials, can solve the problems of fading, easy to absorb dirt, and many impurities and spots, and achieve the effect of reducing demand and mining, simple production process, and soft and natural color

Inactive Publication Date: 2017-12-05
ANHUI ZHENXIN PAINT
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are many pores on the surface and sides of polished vitrified tiles, which are easy to absorb dirt and have poor anti-fouling ability. At present, there is almost no polished vitrified tile in China that can really resist the pollution of tea or ink. Large-scale polished vitrified tiles generally have black hearts or Interlayer defects; Porous glass-ceramics is a decorative material that has only emerged in recent years. Its fatal disadvantages are many pores, easy deformation, many impurity spots, granular surface, easy to absorb dirt, and cannot be refurbished, which seriously affects its quality. Uses: Aluminum-plastic panels are made of composite aluminum panels and plastics, and the surface is coated or sprayed with a layer of decorative fabrics, which have poor weather resistance and are easily deformed and faded; artificial marble is made of resin and fillers after stirring, mixing, and low-temperature drying. Cheng, rich color, but poor surface hardness, easy to wear, deform and fade

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A building decoration material, the final product of which contains the following percentages of oxides:

[0018] SiO2: 20%; Li 2 O: 5%; MgO: 15%; Al 2 o 3 : 5%; Fe 2 o 3 : 1%; ZnO: 3%; BaO: 2%; TiO 2 : 1%; ZrO 2 : 2%; AsO 2 : 1%; B 2 o 3 :1%;

[0019] Further, the final product of the material also includes: LF 2 : 1%, where L is Ba, Mg, Ca, Sr, Zn, and the content of each substance is 0.2%.

[0020] Further, the final product of the material also includes: Ga F 3 : 0.2%, Al F 3 : 0.3%, SbF 3 : 0.5%.

[0021] Further, the final product of the material also includes: Zr F4: 0.5%, As F4: 0.5% in terms of net fluoride content by weight percentage.

Embodiment 2

[0023] A building decoration material, the final product of which contains the following percentages of oxides:

[0024] SiO2: 62%; Na 2 O: 30%; CaO: 50%; Al 2 o 3 : 10%; Fe 2 o 3 : 8%; ZnO: 9%; BaO: 5%; TiO 2 : 6%; ZrO 2 : 8%; AsO 2 : 3%; B 2 o 3 :8%;

[0025] Further, the final product of the material also includes: BaF 2 : 3%, MgF 2 : 4%.

[0026] Further, the final product of the material also includes: Ga F 3 : 2%, Al F 3 : 3%.

[0027] Further, the final product of the material also includes: ZrF4: 5% in weight percent of net fluoride content.

Embodiment 3

[0029] A building decoration material, the final product of which contains the following percentages of oxides:

[0030] SiO2: 40%; RK 2 O: 25%; BeO: 30%; Al 2 o 3 : 8%; Fe 2 o 3 : 5%; ZnO: 5%; BaO: 4%; TiO 2 : 5%; ZrO 2 : 3%; AsO 2 : 2%; B 2 o 3 : 6%;

[0031] Further, the final product of the material also includes: BaF 2 : 5%.

[0032] Further, the final product of the material also includes: GaF 3 : 3%.

[0033] Further, the final product of the material also includes the weight percent of net fluoride content: AsF4: 4%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a building decoration material comprising 20-62% of SiO2, 5-30% of R2O, 15-50% of RO, 5-10% of Al2O3, 1-8% of Fe2O3, 3-9% of ZnO, 2-5% of BaO, 1-6% of TiO2, 2-8% of ZrO2, 1-3% of AsO2 and 1-8% of B2O3. The material is glittering and translucent, smooth and bright in texture, soft and natural in color and luster, free of pores, impurities and spots in the whole body, incapable of absorbing stains, environment-friendly, high in hardness, bending-resistant, compression-resistant, impact-resistant, weather-resistant, fadeless, high-temperature-resistant, wear-resistant and corrosion-resistant and can be randomly renovated. The production process of the material is relatively simple, defects of natural stone and artificial stone are overcome, demands of people for the natural stone and the mining quantity of the natural stone are reduced, and the material is an ideal decoration material and plays good roles in protecting the nature and the environment and beautifying the life.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a building decoration material. Background technique [0002] At present, the popular architectural decorative panels in the domestic and foreign markets mainly include granite, marble, ceramics, porous glass-ceramics, aluminum-plastic panels, and artificial marble. Granite has pores and cracks throughout the body, easy to absorb dirt, difficult to clean, uneven surface hardness, easy to wear, not durable surface gloss, easy to weather and deteriorate, large color difference, most of them have high radioactivity, great harm to the human body, and a large number of Mining will seriously damage the ecological environment, cause water and soil erosion, and endanger nature; marble structure is loose, low in strength, has cracks and a large number of pores, easy to absorb dirt, difficult to clean, low surface hardness, easy to wear, not suitable for paving, only...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/14C04B35/622
CPCC04B35/14C04B35/622C04B2235/3201C04B2235/3203C04B2235/3205C04B2235/3206C04B2235/3208C04B2235/3215C04B2235/3217C04B2235/3232C04B2235/3244C04B2235/3272C04B2235/3284C04B2235/34C04B2235/3409C04B2235/445
Inventor 姚丽玉
Owner ANHUI ZHENXIN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com