Special ceramic plate for building and preparation process of ceramic plate

A preparation process and ceramic plate technology, which is applied in the field of plate materials, can solve the problems of uneven ceramic plates and achieve good wear resistance, low cost, and strong impact resistance

Inactive Publication Date: 2017-12-08
MAANSHAN SONGHAK INFORMATION TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the rapid development of buildings, ceramic plates are used more and more widely. Similarly, large or rapid temperature changes will not affect the characteristics and appearance of materials. The reasonable combination of bending strength and elasticity makes ceramic plates have high The impact resistance strength; at present, the special ceramic plates for construction are mixed, and the preparation process needs to be improved, which has great development prospects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A special ceramic plate for construction and its preparation process. The raw materials are composed of the following proportions in parts by weight: 40 parts of alumina, 16 parts of titanium dioxide, 12 parts of epoxy resin, 5 parts of dibutyl phthalate, zirconia 8 parts of beads, 6 parts of ceramic fiber, 5 parts of glass fiber, 3 parts of polyvinyl alcohol, 4 parts of magnesium oxide, 3 parts of boric acid, 4 parts of polysulfide rubber, and 10 parts of deionized water.

[0013] Its preparation method is as follows:

[0014] A. Mix ceramic fiber and glass fiber for stretching and recombination, and pull it into a continuous fiber shape of 3 μm, add epoxy resin and polysulfide rubber for high-temperature fusion, set the temperature to 130 ° C, and the pressure to 3500 KPa, and then put it into Aluminum oxide and titanium dioxide are mixed until viscous to obtain mixture A;

[0015] B. Add polyvinyl alcohol, magnesium oxide and boric acid to deionized water and stir a...

Embodiment 2

[0018] A special ceramic plate for construction and its preparation process. The raw materials are composed of the following proportions in parts by weight: 35 parts of alumina, 12 parts of titanium dioxide, 10 parts of epoxy resin, 3 parts of dibutyl phthalate, zirconia 6 parts of beads, 8 parts of ceramic fiber, 8 parts of glass fiber, 5 parts of polyvinyl alcohol, 2 parts of magnesium oxide, 2 parts of boric acid, 5 parts of polysulfide rubber, and 5 parts of deionized water.

[0019] Its preparation method is as follows:

[0020] A. The ceramic fiber and glass fiber are mixed and stretched and recombined, and stretched into a continuous fiber shape of 2 μm, and epoxy resin and polysulfide rubber are added for high-temperature fusion. The temperature is set to 120°C, and the pressure is 300KPa. Aluminum oxide and titanium dioxide are mixed until viscous to obtain mixture A;

[0021] B. Add polyvinyl alcohol, magnesium oxide and boric acid to deionized water and stir at a s...

Embodiment 3

[0024] A special ceramic plate for construction and its preparation process. The raw materials are composed of the following proportions in parts by weight: 45 parts of alumina, 10 parts of titanium dioxide, 15 parts of epoxy resin, 3 parts of dibutyl phthalate, zirconia 6 parts of beads, 8 parts of ceramic fiber, 4 parts of glass fiber, 3 parts of polyvinyl alcohol, 2 parts of magnesium oxide, 4 parts of boric acid, 5 parts of polysulfide rubber, and 15 parts of deionized water.

[0025] Its preparation method is as follows:

[0026] A. Mix ceramic fiber and glass fiber for stretching and recombination, and pull it into a continuous fiber shape of 4 μm, add epoxy resin and polysulfide rubber for high-temperature fusion, set the temperature to 140°C, and the pressure to 5000KPa, and then put it into Aluminum oxide and titanium dioxide are mixed until viscous to obtain mixture A;

[0027] B. Add polyvinyl alcohol, magnesium oxide and boric acid to deionized water and stir at a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a special ceramic plate for a building and a preparation process of the ceramic plate. The ceramic plate is prepared from raw materials in parts by weight as follows: 30-45 parts of aluminum oxide, 10-20 parts of titanium dioxide, 10-15 parts of epoxy resin, 3-5 parts of dibutyl phthalate, 6-10 parts of zirconia beads, 4-8 parts of ceramic fibers, 4-8 parts of glass fibers, 3-5 parts of polyvinyl alcohol, 2-5 parts of magnesium oxide, 2-4 parts of boric acid, 3-5 parts of polysulfide rubber and 5-15 parts of deionized water. The special ceramic plate is prepared from materials easy to obtain, is low in cost, environment-friendly and green, has very high impact resistance, scratch resistance and good wear resistance and has tight and non-permeation surface, so that dust cannot easily stick to the ceramic plate; the special ceramic plate is convenient to clean, good in waterproof and moisture-proof effect, long in service life, high in anti-ultraviolet strength and high in stability, has good fireproof effect and is insulated, anti-static and corrosion-resistant.

Description

technical field [0001] The invention relates to the field of plates, in particular to a ceramic plate for building and a preparation process thereof. Background technique [0002] The ceramic plate has extremely strong weather resistance, regardless of sunshine, rain (even acid rain), or moisture, it has no effect on the surface and substrate, and its resistance to ultraviolet radiation and color stability fully reach the international gray level 4-5. With the rapid development of buildings, ceramic plates are used more and more widely. Similarly, large or rapid temperature changes will not affect the characteristics and appearance of materials. The reasonable combination of bending strength and elasticity makes ceramic plates have high The impact resistance strength is high; at present, the ceramic plates for construction are good and bad, and the preparation process needs to be improved, which has great development prospects. Contents of the invention [0003] The objec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/10C04B35/632C04B35/634C04B35/80
CPCC04B35/803C04B35/10C04B35/632C04B35/634C04B35/63416C04B35/63452C04B2235/3206C04B2235/3232C04B2235/3244C04B2235/3409C04B2235/5216
Inventor 施享
Owner MAANSHAN SONGHAK INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com