Waterproof flexible material for external insulating wall space

A flexible material and external thermal insulation technology, applied in the direction of filling slurry, etc., can solve the problems of destroying the overall decorative effect of the building, cracking of the coating film, cracking of the wall, etc., and achieve fine and smooth surface texture, strong waterproof and strong water resistance The effect of cohesiveness

Inactive Publication Date: 2017-12-08
合肥翠鸟节能建材有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In my country, the use of architectural coatings to decorate the exterior walls of buildings has become more and more widespread. However, there is a serious quality problem that the coating film cracks along with the cracks in the wall, which gradually destroys the overall decorative effect of the building. Many buildings After a period of use, the paint surface of the object will appear peeling and falling off, which will eventually lead to cracking and leakage of the wall

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof flexible material for external insulating wall space

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] The preparation method of the above-mentioned waterproof flexible material for external thermal insulation wall comprises the following steps:

[0025] (1) Weigh the heavy calcium powder and sand according to the proportion, put them into the mixer one by one, stir them thoroughly, mix them evenly, and then grind them for 5-10 minutes, so that the two are fully mixed;

[0026] (2) Weigh the Portland cement according to the proportion, add it to the material obtained in step (1), mix and stir evenly;

[0027] (3) Add cellulose ether and wood fiber weighed according to the ratio to the material obtained in step (2), and grind for 5-10 minutes to make the two fully mixed;

[0028] (4) Weigh the redispersible rubber powder 5044N and redispersible rubber powder 8034H according to the proportion, put them into the high-speed disperser in order to fully disperse, and then add the silicone weighed according to the proportion at a speed of 1000-1200r / min Hydrophobic agent, stir...

Embodiment 1

[0031] [Example 1] A waterproof flexible material for external thermal insulation walls, including the following raw material formula components in parts by weight: 235 parts of Portland cement, 568 parts of sand, 148 parts of heavy calcium powder, and 18 parts of redispersible rubber powder 5044N, 14.5 parts of redispersible rubber powder 8034H, 1.8 parts of cellulose ether, 2.7 parts of wood fiber, 0.8 parts of silicone water repellent.

[0032] The preparation method of the above-mentioned waterproof flexible material for external thermal insulation wall comprises the following steps:

[0033] (1) Weigh the heavy calcium powder and sand according to the ratio, put them into the mixer in turn, stir them thoroughly, mix them evenly, and then grind them for 5 minutes;

[0034] (2) Weigh the Portland cement according to the proportion, add it to the material obtained in step (1), mix and stir evenly;

[0035] (3) Add cellulose ether and wood fiber weighed according to the prop...

Embodiment 2

[0039] [Example 2] A waterproof flexible material for external thermal insulation walls, including the following raw material formula components in parts by weight: 240 parts of Portland cement, 569 parts of sand, 150 parts of heavy calcium powder, and 20 parts of redispersible rubber powder 5044N, 15 parts of redispersible rubber powder 8034H, 2 parts of cellulose ether, 3 parts of wood fiber, 1 part of silicone water repellent.

[0040] The preparation method of the above-mentioned waterproof flexible material for external thermal insulation wall comprises the following steps:

[0041] (1) Weigh the heavy calcium powder and sand according to the proportion, put them into the mixer one by one, stir them thoroughly, and grind them for 8 minutes after mixing evenly;

[0042] (2) Weigh the Portland cement according to the proportion, add it to the material obtained in step (1), mix and stir evenly;

[0043] (3) Add cellulose ether and wood fiber weighed according to the proport...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Bond strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a waterproof flexible material for an external insulating wall space. The material is prepared from the following raw materials in parts by weight: 235-245 parts of silicate cement, 568-570 parts of sand, 14-152 parts of ground calcium carbonate powder, 18-22 parts of redispersible rubber powder 5044N, 14.5-15.5 parts of redispersible rubber powder 8034H, 1.8-2.2 parts of cellulose ether, 2.7-3.4 parts of wood fibers and 0.8-1.2 parts of an organosilicone water repellent. The waterproof flexible material for the external insulating wall space disclosed by the invention not only has extremely high water resistance and caking property, but also has the advantages of high-low temperature change resistance, crack resistance and the like, solves the problem that existing external wall putty powder is relatively poor in weather resistance, is free of phenomena of hollowing, peeling, cracking and falling if encountering with water and being moisturized, is extremely high in waterproofness, green and environment-friendly, good in flexibility, difficult to pulverize, is fine and smooth in surface texture if being scraped, and is safe and environment-friendly and long in service life.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a waterproof flexible material for external thermal insulation walls. Background technique [0002] Putty material is a supporting product for base treatment when building fillers are painted. Putty materials are generally composed of base materials, fillers, water and additives. The base material, also known as the binder, is the most important component of the putty material, and it mainly plays various functions such as bonding. The filler mainly acts as a filling, and the commonly used ones are calcium oxide, talcum powder and quartz sand. Additives include thickeners, water retaining agents, preservatives, etc. Thickeners and water-retaining agents play the role of water retention, improving storage and construction, and cellulose is generally used. Preservatives are mainly used to prevent deterioration due to corruption during storage. In addition, there are...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 吴龙生
Owner 合肥翠鸟节能建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap