Low-temperature orange material for ceramic glaze and preparation method of low-temperature orange material
A production method and orange technology, applied in the field of ceramic pigments, can solve the problems of environmental influence and complicated operation, and achieve the effects of low equipment requirements, bright texture, and small color difference changes.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] A low-temperature orange-yellow material for ceramic glaze, comprising the following raw materials in terms of mass percentage: 65% of Dehua Gaide soil, 18% of low-temperature frit, 11% of Longyan kaolin, and 6% of magnesium chloride, wherein the low-temperature frit The number LK7340 low-temperature frit produced for Zibo Fuxing Ceramic Color Glaze Co., Ltd. has a softening point of 700°C and a firing temperature of 1000°C-1080°C.
[0024] The preparation method of the low-temperature orange-yellow material for the above-mentioned ceramic glaze comprises the following steps:
[0025] 1) After weighing each raw material component according to the proportioning ratio, mix evenly, soak for 24 hours and then dehydrate;
[0026] 2) Calcining the material obtained in step 1) for 8 hours, and controlling the calcination temperature at 1250°C-1270°C;
[0027] 3) The calcined material is poured into water and quenched for 1 min;
[0028] 4) After quenching, put it into a ball...
Embodiment 2
[0030] A low-temperature orange material for ceramic glaze, comprising the following raw materials in terms of mass percentage: 66.5% of Dehua Gaide soil, 20% of low-temperature frit, 12% of Longyan kaolin, and 1.5% of magnesium chloride, wherein the low-temperature frit is Zibo The low-temperature frit produced by Fuxing Ceramic Color Glaze Co., Ltd., numbered LK7340, has a softening point of 700°C and a firing temperature of 1000°C-1080°C.
[0031] The preparation method of the low-temperature orange-yellow material for the above-mentioned ceramic glaze comprises the following steps:
[0032] 1) first crush and sieve each raw material component, then weigh according to the proportion, mix evenly, soak for 24 hours and then dehydrate;
[0033] 2) Calcining the material obtained in step 1) for 12 hours, and controlling the calcination temperature at 1250°C-1270°C;
[0034] 3) The calcined material is poured into water and quenched for 2 minutes;
[0035] 4) After quenching, ...
Embodiment 3
[0037] A low-temperature orange-yellow material for ceramic glaze, comprising the following raw materials in terms of mass percentage: 66% of Dehua Gaide soil, 19% of low-temperature frit, 11.5% of Longyan kaolin, and 3.5% of magnesium chloride, wherein the low-temperature frit is Zibo The model of Shuntai ceramics is T-908 low-temperature frit, the softening point is 600°C, and the firing temperature is 1000°C-1080°C.
[0038] The preparation method of the low-temperature orange-yellow material for the above-mentioned ceramic glaze comprises the following steps:
[0039] 1) first crush and sieve each raw material component, then weigh according to the proportion, mix evenly, soak for 24 hours and then dehydrate;
[0040] 2) Calcining the material obtained in step 1) for 12 hours, and controlling the calcination temperature at 1250°C-1270°C;
[0041] 3) The calcined material is poured into water and quenched for 3 minutes;
[0042] 4) After quenching, put it into a ball mill...
PUM
| Property | Measurement | Unit |
|---|---|---|
| softening point | aaaaa | aaaaa |
| softening point | aaaaa | aaaaa |
| temperature | aaaaa | aaaaa |