Treatment method for eliminating residual stress of stainless steel welding piece
A technology of residual stress and treatment method, applied in the direction of heat treatment furnace, heat treatment equipment, improvement of process efficiency, etc., can solve the problems affecting the working life and residual tensile stress of stainless steel welding parts, and achieve the effect of eliminating residual stress and reducing residual stress.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0017] Example 1
[0018] A treatment method for eliminating residual stress of stainless steel welded parts, including the following steps:
[0019] (1) Dipping treatment: soak the stainless steel welded parts in absolute ethanol for 30 minutes, then take it out, wash with deionized water, and dry to constant weight;
[0020] (2) Quenching treatment: The stainless steel welded parts are heated in a resistance furnace, and the stainless steel is preheated at 520°C for 35 minutes; after preheating, the stainless steel is heated at 780°C for 25 minutes. The welded parts are taken out of the furnace and quenched into quenching oil at 40°C for cooling. The cooling time is 1 hour, and the quenching oil is taken out when the temperature of the stainless steel welded parts reaches 150°C;
[0021] (3) Ultrasonic treatment: The stainless steel welded parts proposed in step (2) self-quenching oil are treated with 500W and 800W ultrasonic waves respectively. During ultrasonic treatment, keep the...
Example Embodiment
[0029] Example 2
[0030] A treatment method for eliminating residual stress of stainless steel welded parts, including the following steps:
[0031] (1) Dipping treatment: soak the stainless steel welded parts in absolute ethanol for 30 minutes, then take it out, wash with deionized water, and dry to constant weight;
[0032] (2) Quenching treatment: The stainless steel welded parts are heated in a resistance furnace, and the stainless steel welded parts are preheated at 560°C for 40 minutes; after preheating, they are heated at 820°C for 30 minutes; the stainless steel is heated after the heat preservation is completed. The welded parts are taken out of the furnace and quenched in 42°C quenching oil for cooling. The cooling time is 1 hour until the temperature of the stainless steel welded parts is 160°C.
[0033] (3) Ultrasonic treatment: The stainless steel welded parts proposed in step (2) self-quenching oil are treated with 500W and 800W ultrasonic waves respectively. During ult...
Example Embodiment
[0041] Example 3
[0042] A treatment method for eliminating residual stress of stainless steel welded parts, including the following steps:
[0043] (1) Dipping treatment: soak the stainless steel welded parts in absolute ethanol for 30 minutes, then take it out, wash with deionized water, and dry to constant weight;
[0044] (2) Quenching treatment: The stainless steel welded parts are heated in a resistance furnace, and the stainless steel welded parts are preheated at 550°C for 38 minutes; after preheating, they are heated at 790°C for 28 minutes; the stainless steel is heated after the insulation is completed. The welded parts are quenched into 41℃ quenching oil to cool down, cooling time is 1 hour, until the stainless steel welded parts temperature is 155℃, the quenching oil will be taken out;
[0045] (3) Ultrasonic treatment: The stainless steel welded parts proposed in step (2) self-quenching oil are treated with 500W and 800W ultrasonic waves respectively. During ultrasonic ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology