Wax mold casting technology
A wax mold casting and process technology, applied in manufacturing tools, casting molding equipment, casting molds, etc., can solve the problems of insufficient wax mold shell strength, poor surface quality of castings, long production cycle, etc., and achieve good surface quality and modeling. The effect of high success rate and low labor intensity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0014] Example 1
[0015] A wax mold casting process, which consists of the following steps:
[0016] (1) Make a wax mold consistent with the shape of the casting;
[0017] (2) Apply a strengthening agent on the surface of the wax mold and then dry it at a temperature of 70°C, a drying time of 3 hours, and a drying wind speed of 1.5 m / s;
[0018] (3) Put the wax mold in a large pot containing clear water and cook at a temperature of 60°C and a boiling time of 25 minutes to obtain a melted paraffin shell mold;
[0019] (4) Put a fixed shell on the shell mold, and add dry sand between the shell mold and the fixed shell to fix the shell mold;
[0020] (5) Dry the shell mold obtained in step (4) at a drying temperature of 180°C and a drying time of 1.2 hours;
[0021] (6) Pour the molten liquid metal into the shell mold, then cool and remove the shell to obtain a molded casting.
[0022] The strengthening agent in step (2) is made of the following components by weight: aluminum nitride 1.1, si...
Example Embodiment
[0025] Example 2
[0026] A wax mold casting process, which consists of the following steps:
[0027] (1) Make a wax mold consistent with the shape of the casting;
[0028] (2) Apply a strengthening agent on the surface of the wax mold and then dry it at a temperature of 80°C, a drying time of 4 hours, and a drying wind speed of 1.7 m / s;
[0029] (3) Put the wax mold in a large pot containing clear water and cook at a temperature of 65°C and a boiling time of 30 minutes to obtain a melted paraffin shell mold;
[0030] (4) Put a fixed shell on the shell mold, and add dry sand between the shell mold and the fixed shell to fix the shell mold;
[0031] (5) Dry the shell mold obtained in step (4) at a drying temperature of 190°C and a drying time of 1.4 hours;
[0032] (6) Pour the molten liquid metal into the shell mold, then cool and remove the shell to obtain a molded casting.
[0033] The strengthening agent in step (2) is made of the following components by weight: aluminum nitride 1.2, si...
Example Embodiment
[0037] Example 3
[0038] A wax mold casting process, which consists of the following steps:
[0039] (1) Make a wax mold consistent with the shape of the casting;
[0040] (2) Apply a strengthening agent on the surface of the wax mold and then dry it at a temperature of 90°C, a drying time of 5 hours, and a drying wind speed of 1.9 m / s;
[0041] (3) Put the wax mold in a large pot containing clear water and cook at a temperature of 70°C and a boiling time of 35 minutes to obtain a shell mold after the paraffin wax has melted;
[0042] (4) Put a fixed shell on the shell mold, and add dry sand between the shell mold and the fixed shell to fix the shell mold;
[0043] (5) Dry the shell mold obtained in step (4) at a drying temperature of 200°C and a drying time of 1.6 hours;
[0044] (6) Pour the molten liquid metal into the shell mold, then cool and remove the shell to obtain a molded casting.
[0045] The strengthening agent in step (2) is made of the following components by weight: alumin...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap