Method for manufacturing aluminum alloy rivet rod for aerospace product

A manufacturing method and aluminum alloy technology, applied in the field of manufacturing aluminum alloy rivet bars, can solve the problems of low tensile strength, non-proportional elongation strength, elongation after fracture and low shear strength, and achieve good surface quality and comprehensive mechanical properties Excellent, good molding performance

Active Publication Date: 2012-11-21
哈尔滨东轻特种材料有限责任公司
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problems of low tensile strength, non-proportional elongation strength, elongation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0007] Specific Embodiment 1: The manufacturing method of an aluminum alloy rivet bar for aerospace according to the present embodiment is realized according to the following steps: 1. According to the mass percentage of elements in the aluminum alloy bar, Mg: 0.5% to 1.0%, Cr: 0.10%~0.20%, Si: 0~0.25%, Fe: 0~0.35%, Cu: 4.5%~5.2%, Mn: 0.40%~0.6%, Ti: 0.04%~0.12%, Zr: 0.1%~0.2% % and the ratio of the balance Al Weigh aluminum ingots, aluminum-manganese alloys, aluminum-zirconium alloys, aluminum-titanium alloys, aluminum-chromium alloys, copper ingots and magnesium ingots, and add them to the melting furnace. Smelting at low temperature for 3 to 4 hours to obtain molten aluminum alloy; 2. The molten aluminum alloy obtained in step 1 is cast at a casting temperature of 725°C to 750°C, a casting speed of 90mm / min to 95mm / min, and a cooling water intensity of 0.01MPa ~ 0.03MPa and cooling water temperature of 10 ℃ ~ 20 ℃ under the conditions of casting into cast rods with a diamet...

specific Embodiment approach 2

[0010] Specific embodiment 2: The difference between this embodiment and specific embodiment 1 is that in step 1, the mass percentages of elements in the aluminum alloy bar are Mg: 0.7%-0.9%, Cr: 0.12%-0.16%, Si: 0.01 %~0.15%, Fe: 0.1%~0.25%, Cu: 4.6%~5.1%, Mn: 0.49%~0.55%, Ti: 0.06%~0.10%, Zr: 0.12%~0.18% and the ratio of the balance Al , weighing aluminum ingots, aluminum-manganese alloys, aluminum-zirconium alloys, aluminum-titanium alloys, aluminum-chromium alloys, copper ingots and magnesium ingots. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0011] Specific embodiment 3: The difference between this embodiment and specific embodiment 1 or 2 is that in step 1, the mass percentages of elements in the aluminum alloy bar are Mg: 0.75%, Cr: 0.13%, Si: 0.06%, Fe: 0.16%, Cu: 4.79%, Mn: 0.51%, Ti: 0.084%, Zr: 0.14% and the ratio of the balance Al, weighing aluminum ingots, aluminum-manganese alloys, aluminum-zirconium alloys, aluminum-titanium alloys, aluminum-chromium alloys, Copper and Magnesium Ingots. Others are the same as in the first or second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for manufacturing a high shear-resistant strength and high percentage elongation after fracture aluminum alloy rivet rod for the aerospace product, belonging to the method for manufacturing an aluminum alloy rod, and aiming to solve the problems of low non-proportional extension strength, shearing strength, tensile strength and extension at break of the existing aluminum alloy rivet rod for the aerospace product. The method comprises the following steps: (1) preparing molten alloy; (2) casting an alloy rod; (3) cutting off the cast alloy rod; (4) turning the peel of the cast alloy rod; (5) carrying out homogenizing annealing; (6) heating the cast alloy rod; (7) extruding; (8) carrying out cold-drawing by using a mold; (9) quenching; (10) straightening; and (11) aging to obtain the aluminum alloy rivet rod for the aerospace product. The aluminum alloy rivet rod manufactured by adopting the method has the tensile strength of not less than 431N/mm<2>, the non-proportional extension strength of not less than 265N/mm<2>, the extension at break of not less than 16% and the shearing strength of not less than 255N/mm<2> and meets the application requirement of the aerospace product. The method can be used for processing and manufacturing the aluminum alloy rivet for the aerospace product.

Description

technical field [0001] The invention relates to a method for manufacturing an aluminum alloy rivet bar. Background technique [0002] At present, a certain aerospace product in our country needs a special rivet, which requires the tensile strength of this alloy bar to reach 431N / mm 2 , non-proportional extension strength 265N / mm 2 , elongation after breaking 16%, shear strength 255N / mm 2 , but the tensile strength of the alloy produced by the existing process is 339-427N / mm 2 , elongation after breaking 10.3~14.5%, shear strength 245~253N / mm 2 , so it cannot meet the application requirements of aerospace products. Contents of the invention [0003] The purpose of the invention is to solve the problems of low tensile strength, non-proportional elongation strength, elongation after fracture and low shear strength of existing rivet bars, and provides a manufacturing method of aluminum alloy rivet bars for aerospace. [0004] A method for manufacturing an aluminum alloy r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C21/12C22C1/03C22F1/057C21D8/06
Inventor 刘记伟罗建华刚建伟孙荣滨张燕飞苏玉洁
Owner 哈尔滨东轻特种材料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap