Finishing paint coating construction process of high-elasticity UV closed sheet having matte effect

A construction technique and a high-elasticity technology, which is applied in the direction of surface coating liquid devices, coatings, manufacturing tools, etc., to achieve good sanding effect, high adhesion and fast drying speed

Inactive Publication Date: 2018-01-16
惠州市摩彩装饰材料有限公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the deficiencies in the prior art, the technical problem to be solved by the present invention is to provide a topcoat coating construction process for highly elastic UV-enclosed matte effect thin plates. UV coating, and then roll coating the high-elastic UV matte surface, and the primer has been polished, and then bent, so that the obtained paint film is evenly coated, the thickness of the paint film is greatly improved, and orange peel is not easy to occur and cracking problems, strong adhesion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A topcoat coating construction process for highly elastic UV-enclosed matte effect sheets, comprising the following steps:

[0031] (1) Thin plate treatment: take a thin plate substrate with a thickness of 3mm, which can be processed into a size of 2440*1220, pasted with a natural veneer with a thickness of 0.45mm, and sanded with a special sander for thin plates deal with;

[0032] (2) Roller coating of high elastic UV putty: the coating amount of high elastic UV putty is 25g / m 2 , UV drying with double mercury lamp after roller coating, the drying strength is 200mJ / m 2 , the drying time is 1 second; the dry film thickness of the high elastic UV putty is 30μm;

[0033] (3) Roller coating with high elasticity UV elastic primer: the amount of roller coating with high elasticity UV elastic primer is 60g / m 2 , UV drying with double mercury lamp after roller coating, the drying strength is 200mJ / m 2 , the drying time is 2 seconds; the dry film thickness of the high elas...

Embodiment 2

[0042] A topcoat coating construction process for highly elastic UV-enclosed matte effect sheets, comprising the following steps:

[0043] (1) Thin plate treatment: take a thin plate base material with a thickness of 3mm, which can be processed into a size of 2000*1000, paste a technical veneer with a thickness of 0.45mm, and use a special sander for thin plates for sanding deal with;

[0044](2) Roller coating of high elastic UV putty: the coating amount of high elastic UV putty is 30g / m 2 , UV drying with double mercury lamp after roller coating, the drying strength is 200mJ / m 2 , the drying time is 2 seconds; the dry film thickness of high elastic UV putty is 45μm;

[0045] (3) Roller coating with high elasticity UV elastic primer: the coating amount of roller coating with high elasticity UV elastic primer is 70g / m 2 , UV drying with double mercury lamp after roller coating, the drying strength is 200mJ / m 2 , the drying time is 1 second; the dry film thickness of the hi...

Embodiment 3

[0054] A topcoat coating construction process for highly elastic UV-enclosed matte effect sheets, comprising the following steps:

[0055] (1) Thin plate treatment: take a thin plate substrate with a thickness of 3mm, which can be processed into a size of 2200*1200, pasted with a natural veneer with a thickness of 0.45mm, and sanded with a special sander for thin plates deal with;

[0056] (2) Roller coating of high elastic UV putty: the coating amount of high elastic UV putty is 30g / m 2 , UV drying with double mercury lamp after roller coating, the drying strength is 200mJ / m 2 , the drying time is 1 second; the dry film thickness of the high elastic UV putty is 40μm;

[0057] (3) Roller coating with high elasticity UV elastic primer: the coating amount of roller coating with high elasticity UV elastic primer is 65g / m 2 , UV drying with double mercury lamp after roller coating, the drying strength is 200mJ / m 2 , the drying time is 2 seconds; the dry film thickness of the h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a finishing paint coating construction process of a high-elasticity UV closed sheet having a matte effect. The finishing paint coating construction process comprises the following steps that the sheet is treated, high-elasticity UV putty is coated in a rolling mode, and the coating amount is 25-30 g / m<2>; a high-elasticity UV primer is coated in a rolling mode, and the coating amount is 60-70 g / m<2>; a high-elasticity UV sanding primer is coated in a rolling mode, and the coating amount is 25-30 g / m<2>; sanding and dust removal treatment is performed; a high-elasticityUV matte surface is coated in a rolling mode, and the coating amount is 25-30 g / m<2>; bending treatment is performed; a protective film is attached, and detection and package are performed. Accordingto the finishing paint coating construction process of the high-elasticity UV closed sheet having the matte effect, the sheet is firstly subjected to coating of the high-elasticity putty, the high-elasticity primer and the sanding primer and then coating of the high-elasticity UV matte surface in the rolling mode, the primer is ground, and then bending is performed, so that an obtained paint filmis uniform and flat in coating, the thickness of the paint film is greatly improved, the problems of crocodile skin and cracking are not likely to occur, and an attachment force is strong.

Description

technical field [0001] The invention relates to the technical field of a chemical coating construction method, in particular to a topcoat coating construction process for a high-elasticity UV-enclosed matte effect thin plate. Background technique [0002] The parapet sheet is a new type of decorative wall material developed in recent years, and generally uses wood as the base material. The protective wall thin board has the characteristics of light weight, fire prevention, moth resistance, and simple construction. It is low in cost, safe in use, obvious in decorative effect, and convenient in maintenance. It can not only replace wooden dado, but also replace wall materials such as wallpaper and wall bricks, so it is widely used. [0003] When decorative wall panels are used, they need to be painted and bent. At present, the main construction process of the bent parapet sheet produced in the market is to directly coat the surface of the bent sheet with veneer without any co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B05D3/00B05D3/06B05D7/00B05D7/08B24B19/24B27G3/00B27H1/00
Inventor 余文强
Owner 惠州市摩彩装饰材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com