Macromolecular composite membrane modified bituminous waterproof roll

A technology of modified asphalt and waterproof membrane, which is applied in the direction of asphalt layered products, layered products, synthetic resin layered products, etc. It can solve the problems of easy delamination and separation of film layers, and the decline and disappearance of waterproof membrane materials. , to achieve optimal design, good anti-asphalt swelling and penetration performance, and prevent penetration

Inactive Publication Date: 2018-01-26
XI NIU PI WATERPROOFING TECH CO LTD
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a polymer composite membrane modified asphalt waterproofing coiled material, which solves the problem that the membrane layer of the polymer composite membrane in the waterproofing coiled material is under high temperature and ultraviolet irradiation conditions, due to high temperature swelling and penetration of the asphalt, causing the coiled material to The film layers of the medium-polymer composite membrane are easy to delaminate and separate, which leads to the decline or even disappearance of the waterproof performance of the waterproof membrane.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Macromolecular composite membrane modified bituminous waterproof roll
  • Macromolecular composite membrane modified bituminous waterproof roll
  • Macromolecular composite membrane modified bituminous waterproof roll

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] This embodiment provides a multilayer polymer composite membrane modified asphalt waterproofing membrane, which is a 3-layer structure, such as figure 1 As shown, it includes 1 layer of polymer composite film layer 1, 1 layer of rubber material layer 2 and 1 layer of isolation protection layer 3. The rubber material layer is SBR modified asphalt rubber material, and the isolation protection layer is polyethylene film (PE). The molecular composite film has a three-layer structure with a thickness of 120 μm, such as figure 2 As shown, the order of each film layer from top to bottom is: functional layer 4, connecting layer 5 and barrier layer 6, and the material parameters and dosage of each layer are shown in Table 5 below:

[0060] Table 5 Three-layer polymer composite membrane layer material parameters and dosage

[0061]

[0062] The above-mentioned three-layer polymer composite film is prepared by a blown film co-extrusion process.

[0063] Use the above-mention...

Embodiment 2

[0065] This embodiment provides a multi-layer polymer composite membrane modified asphalt waterproof membrane, which is a 5-layer structure, including 1 polymer composite membrane layer, 2 rubber layers and 2 isolation protection layers, the rubber layer It is SBS modified asphalt compound, the isolation protective layer is polyethylene film (PE), and the polymer composite film is a five-layer structure with a thickness of 155 μm. The order of each film layer from top to bottom is: barrier layer Ⅰ, connecting layer Ⅰ. Functional layer, connection layer Ⅱ and barrier layer Ⅱ. The material parameters and dosage of each layer are shown in Table 6 below:

[0066] Table 6 Five-layer polymer composite film material parameters and dosage

[0067]

[0068] The above-mentioned five-layer polymer composite film is prepared by a flat film co-extrusion process.

[0069] The above-mentioned five-layer polymer composite membrane is used to prepare waterproof coiled material. First, the ...

Embodiment 3

[0071] This embodiment provides a multi-layer polymer composite membrane modified asphalt waterproofing membrane, which is a 3-layer structure, including a polymer composite membrane layer, a rubber layer and an isolation protection layer, the rubber layer It is APP modified asphalt compound, the isolation protective layer is polyethylene film (PE), and the polymer composite film has a nine-layer structure with a thickness of 190 μm. The order of each film layer from top to bottom is: functional layer Ⅰ, connecting layer Ⅰ. Functional layer II, connecting layer II, functional layer III, connecting layer III, functional layer IV, connecting layer IV and barrier layer. The material parameters and dosage of each layer are shown in Table 7 below:

[0072] Table 7 Nine-layer polymer composite film material parameters and dosage

[0073]

[0074] The above-mentioned nine-layer polymer composite film is prepared by a blown film co-extrusion process.

[0075] Use the above-mention...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a macromolecular composite membrane modified bituminous waterproof roll. The roll comprises at least one macromolecular composite membrane and at least one modified bituminous size layer bonded to the at least one macromolecular composite membrane, wherein the macromolecular composite membrane adopts a multilayer structure and can prevent layer separation, resist high temperatures and resist ultraviolet rays. Through optimization design of different membrane layer structures and materials of the multilayer macromolecular composite membranes in the macromolecular composite membrane modified bituminous waterproof roll, the waterproof roll has good bituminous swelling resistance and permeability, has good ultraviolet resistance at the high temperature and under ultraviolet irradiation and has the significant waterproof effect, and separation of composite membrane layers cannot occur easily.

Description

technical field [0001] The invention relates to the field of waterproof coiled materials, in particular to a polymer composite membrane modified asphalt waterproof coiled material. Background technique [0002] Waterproof membranes are mainly used in building walls, roofs, tunnels, roads, landfills, etc., to resist external rainwater and prevent groundwater leakage. As the non-leakage connection between the engineering foundation and the building, the waterproof membrane is the first barrier for the waterproofing of the entire project and plays a vital role in the waterproof quality of the entire project. Waterproof membrane is a flexible building material product that can be rolled into a roll, and is made of asphalt or polymer waterproof material impregnated on the carcass. According to the different main components, it can be divided into asphalt waterproof membrane, polymer modified asphalt waterproof membrane and synthetic polymer waterproof membrane. According to the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B11/04B32B27/06B32B27/18B32B27/32B32B27/34B32B27/36
Inventor 陆善庆陈立斌朱方伍伍盛江凌日华陈海红
Owner XI NIU PI WATERPROOFING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com