A technology of lightweight ceramsite and light through-hole ceramsite, which is applied in the field of ceramsite, can solve the problems of high specific gravity and bulk density, low water absorption, and inability to ensure the normal growth and development of plants, and achieve the effect of bright colors

Inactive Publication Date: 2018-02-02
蒋文兰
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The colored ceramsite sold in the market is made by mixing cement, fine sand and dyes and then granulating. The specific gravity and bulk density are very large, and the water absorption rate is small. It cannot ensure the normal growth and development of plants, and there is no adsorption and The function of purifying the air

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Burning-free quincuncial colorized bentonite lightweight ceramsite
  • Burning-free quincuncial colorized bentonite lightweight ceramsite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0040] Below in conjunction with embodiment the present invention will be further described:

[0041] 1. The ingredients of unburned plum-shaped white bentonite light ceramsite are composed of the following components by weight percentage: 32% of acidified bentonite, 8% of powdered bentonite foaming agent, 4% of light calcium carbonate, and light magnesium oxide 3%, hollow glass microspheres 3%, aluminum silicate fibers 2%, white Portland cement 25%, red Portland cement 0%, green Portland cement 0%, yellow Portland cement 0%, blue Colored Portland cement 0%, brown Portland cement 0%, black Portland cement 0%, titanium dioxide 3% and water 20%.

[0042] 2. The ingredients of unburned plum-shaped red bentonite light ceramsite are composed of the following components by weight percentage: acidified bentonite 34%, powdered bentonite foaming agent 8%, light calcium carbonate 4%, light magnesium oxide 3%, hollow glass microspheres 3%, aluminum silicate fibers 2%, white Portland cem...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a non-burning plum-shaped colored bentonite lightweight ceramsite. The main point of the technical scheme is that the ingredients of the unburned plum-shaped colored bentonite light ceramsite are acidified bentonite, colored Portland cement, powder Composed of bentonite foaming agent, light calcium carbonate, light magnesium oxide, hollow glass microspheres, aluminum silicate fiber and titanium dioxide; the ingredients are stirred and mixed, extruded and granulated, steam cured, steam dried, sieved and packaged It is non-burning plum-shaped colored bentonite lightweight ceramsite; it has the characteristics of bright color, beautiful appearance, good light strength, large specific surface area, low bulk density, excellent air permeability, high porosity and water absorption. Unburned plum-shaped colored bentonite light ceramsite can ensure good plant growth and development, high survival rate and longer life, and can greatly reduce the number of water replenishment. Unburned plum-shaped colored bentonite light ceramsite is suitable for garden landscape projects and households Gardening and preparing soilless growing substrates.

Description

technical field [0001] The invention relates to ceramsite, in particular to an unburned plum blossom-shaped colored bentonite lightweight ceramsite. Background technique [0002] The colored ceramsite sold in the market is made of cement, fine sand and dyes mixed and granulated. The specific gravity and bulk density are very large, and the water absorption rate is small. It cannot ensure the normal growth and development of plants, and there is no adsorption and The function of purifying the air. [0003] After several sampling tests: the average bulk density of colored ceramsite sold in the market is ≥1200kg / m³, and the average water absorption rate is ≤20%. Contents of the invention [0004] The purpose of the present invention is to overcome the disadvantages of the prior art and provide a kind of non-burning plum blossom-shaped colored bentonite lightweight ceramsite. [0005] The ingredients of unburned plum-shaped colored bentonite light ceramsite are acidified ben...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B38/08C04B38/10C04B111/40C04B111/82
CPCC04B28/04C04B2111/40C04B2111/82C04B2201/20C04B14/104C04B14/28C04B14/304C04B14/24C04B14/4656C04B14/305C04B38/10C04B38/085
Inventor王雨润吴一青金白云王鲁海黄允金袁欣许庆华蒋文兰
Owner蒋文兰