Pervious concrete and preparation method thereof

A technology of permeable concrete and Portland cement, applied in the field of building materials, can solve the problems of inability to replenish groundwater, subsidence of soil layers, poor air permeability and water permeability, etc., and achieve the effect of alleviating urban heat island effect, reducing urban noise, and strengthening water permeability.

Inactive Publication Date: 2018-02-23
山东鲁盛新能源有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, when this kind of concrete is used, especially in rainy weather, it does not directly contact the soil on the surface, resulting in poor air permeability and water permeability, and cannot replenish groundwater, alleviate some urban environmental problems such as the sharp decline of groundwater in the city, and also lead to underground subsidence

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of permeable concrete is provided in this embodiment, and the content of each component in the raw material includes: 29 parts of ore coarse aggregate, 24 parts of fine sand, 21 parts of Portland cement, 20 parts of diatom mud, and 14 parts of polymer cementing material , 3 parts of phosphorus slag fine powder, 3 parts of iron powder, 10 parts of phenolic fiber, 12 parts of polypropylene fiber.

[0030] The preparation method includes the following steps: 1) Proportioning according to the weight of the raw materials, first perform dry stirring for 1-2 minutes, then add an appropriate amount of water to mix, and stir for 120-130 minutes;

[0031] 2) Let the mixture in step 1) rest for 2-3 minutes, then stir in reverse for 30-40 minutes.

[0032] Further, the amount of water added in step 1) is 1 / 2 times the weight of the dry stirring mixture.

Embodiment 2

[0034] In this embodiment, a kind of permeable concrete is provided. The content of each component in the raw material includes: 27 parts of ore coarse aggregate, 25 parts of fine sand, 19 parts of Portland cement, 19 parts of diatom mud, and 15 parts of polymer cementitious material , Phosphorus slag fine powder 2 parts, iron powder 1 part, phenolic fiber 11 parts, polypropylene fiber 11 parts.

[0035] The preparation method includes the following steps: 1) Proportioning according to the weight of the raw materials, first perform dry stirring for 1-2 minutes, then add an appropriate amount of water to mix, and stir for 120-130 minutes;

[0036] 2) Let the mixture in step 1) rest for 2-3 minutes, then stir in reverse for 30-40 minutes.

[0037] Further, the amount of water added in step 1) is 1 / 2 times the weight of the dry stirring mixture.

[0038] Further, the amount of water added in step 1) is added in 2-3 times, adding 1 / 2 of the amount for the first time and then addi...

Embodiment 3

[0040] This embodiment provides a kind of permeable concrete. The content of each component in the raw material includes: 21 parts of ore coarse aggregate, 26 parts of fine sand, 17 parts of Portland cement, 23 parts of diatom mud, 13 parts of polymer cementing material, 3 parts of phosphorus slag powder, 3 parts of iron powder, 8 parts of phenolic fiber, and 15 parts of polypropylene fiber.

[0041] The preparation method includes the following steps: 1) Proportioning according to the weight of the raw materials, first perform dry stirring for 1-2 minutes, then add an appropriate amount of water to mix, and stir for 120-130 minutes;

[0042] 2) Let the mixture in step 1) rest for 2-3 minutes, then stir in reverse for 30-40 minutes.

[0043] Further, the amount of water added in step 1) is 1 / 2 times the weight of the dry stirring mixture.

[0044] Further, the amount of water added in step 1) is added in 2-3 times, adding 1 / 2 of the amount for the first time and then adding i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides pervious concrete and a preparation method thereof. The content of each component in raw materials is as follows: 21-34 parts of ore coarse aggregates, 23-27 parts of fine sand,17-24 parts of Portland cement, 16-23 parts of diatomite, 13-17 parts of a polymer cementing material, 2-4 parts of phosphorus slag fine powder, 1-3 parts of iron powder, 8-13 parts of phenolic fibers and 6-15 parts of polypropylene fibers. Through the preparation by using the preparation method, the adhesion degree of all the components in the raw materials can be enhanced; gaps are generated between the phenolic fibers and the polypropylene fibers, and facilitate water permeation; and the pervious concrete can be further promoted in the actual building industry.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a permeable concrete and a preparation method thereof. Background technique [0002] With the continuous development of the current social economy, people's living standards are also constantly improving, and the pursuit of quality of life is also getting higher and higher. [0003] Especially for the construction industry, due to the gradual expansion and improvement of urban modernization, the use of concrete is becoming more and more extensive. The surface and ground buildings of modern cities are gradually covered by reinforced concrete, which can keep the ground clean. [0004] However, when this kind of concrete is used, especially in rainy weather, it does not directly contact the soil on the surface, resulting in poor air permeability and water permeability, and cannot replenish groundwater, alleviate some urban environmental problems such as the sharp decline of groundw...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2111/00284C04B14/02C04B14/06C04B14/08C04B24/24C04B18/145C04B14/34C04B16/0633C04B16/0675
Inventor 杜永春
Owner 山东鲁盛新能源有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com