Rubber non-slipping sole and preparation method thereof

A non-slip, rubber technology, applied in soles, applications, clothing and other directions, can solve the problems of non-wear, insufficient wear resistance, short life and so on

Inactive Publication Date: 2018-02-23
NANTONG LONGBANG PLASTIC
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the rubber anti-slip bottom of the prior art needs to be in contact with the ground, and the friction force encountered is relatively large. Generally, the wear resistance of the material is not enough, and the service life is relatively short. Some are made of natural rubber, but they are not very wear-resistant.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A rubber non-slip bottom, its components and the mass parts of each component are as follows:

[0027] Hemp fiber: 20 parts;

[0028] Rice husk powder: 45 parts;

[0029] Butyl rubber: 50 parts;

[0030] EPDM rubber: 10 parts;

[0031] Plasticizer: 2 parts;

[0032] Foaming agent: 2 parts

[0033] Anti-aging agent: 2 parts

[0034] Vulcanizing agent: 2 parts.

[0035] The antiaging agent is a mixture of antiaging agent AW, antiaging agent RD, antiaging agent A and antiaging agent D, and the mass ratio of antiaging agent AW, antiaging agent RD, antiaging agent A and antiaging agent D is: 1:3:2: 1.

[0036] The plasticizer is a phthalate plasticizer.

[0037] Described plasticizer is dioctyl phthalate

[0038] The blowing agent is carbon black.

[0039] The vulcanizing agent is a mixture of vulcanizing agent DTDM and bis-25.

[0040] The preparation method of the rubber anti-slip bottom, the steps contained in the method are as follows:

[0041] (a) prepare ma...

Embodiment 2

[0045] A rubber non-slip bottom, its components and the mass parts of each component are as follows:

[0046] Hemp fiber: 30 parts;

[0047] Rice husk powder: 55 parts;

[0048] Butyl rubber: 70 parts;

[0049] EPDM rubber: 20 parts;

[0050] Plasticizer: 4 parts;

[0051] Foaming agent: 4 parts

[0052] Anti-aging agent: 4 parts

[0053] Vulcanizing agent: 4 parts.

[0054] The anti-aging agent is a mixture of anti-aging agent AW, anti-aging agent RD and anti-aging agent A.

[0055] The plasticizer is a phthalate plasticizer.

[0056] The plasticizer is a mixture of dioctyl phthalate, dicyclohexyl phthalate and dimethyl phthalate.

[0057] The blowing agent is carbonate.

[0058] The vulcanizing agent is a mixture of vulcanizing agent DTDM, vulcanizing agent double 25, and vulcanizing agent PDM.

[0059] The preparation method of the rubber anti-slip bottom, the steps contained in the method are as follows:

[0060] (a) prepare materials according to the mass parts...

Embodiment 3

[0064] A rubber non-slip bottom, its components and the mass parts of each component are as follows:

[0065] Hemp fiber: 25 parts;

[0066] Rice husk powder: 50 parts;

[0067] Butyl rubber: 60 parts;

[0068] EPDM rubber: 15 parts;

[0069] Plasticizer: 3 parts;

[0070] Foaming agent: 3 parts

[0071] Anti-aging agent: 3 parts

[0072] Vulcanizing agent: 3 parts.

[0073] The anti-aging agent is anti-aging agent AW.

[0074] The plasticizer is a phthalate plasticizer.

[0075] The plasticizer is dicyclohexyl phthalate.

[0076] The blowing agent is carbonate.

[0077] The vulcanizing agent is a mixture of vulcanizing agent DTDM, vulcanizing agent double 25, and vulcanizing agent PDM.

[0078] The preparation method of the rubber anti-slip bottom, the steps contained in the method are as follows:

[0079] (a) prepare materials according to the mass parts of the components and each component;

[0080] (b) put the hemp fiber, rice husk powder, butyl rubber, EPDM ru...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rubber anti-slip bottom and a preparation method thereof. The components of the rubber anti-slip bottom and the parts by mass of each component are as follows: hemp fiber: 20-30 parts; rice husk powder: 45-55 parts; butyl Rubber: 50-70 parts; EPDM rubber: 10-20 parts; plasticizer: 2-4 parts; foaming agent: 2-4 parts; anti-aging agent: 2-4 parts; vulcanizing agent: 2 parts ~ 4 servings. The invention is not only elegant in appearance, but also has excellent anti-skid performance, acid and alkali resistance, and long service life.

Description

technical field [0001] The invention relates to a rubber antiskid bottom and a preparation method thereof. Background technique [0002] At present, the rubber anti-slip bottom of the prior art needs to be in contact with the ground, and the friction force encountered is relatively large. The wear resistance of the general material is not enough, and the service life is relatively short. Some are made of natural rubber, but they are not very wear-resistant. . Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the defects of the prior art and provide a rubber anti-slip bottom, which is not only elegant in appearance, but also has excellent anti-slip performance, acid and alkali resistance, and long service life. [0004] In order to solve the above technical problems, the technical solution of the present invention is: a rubber anti-slip bottom, its components and the parts by mass of each component are as follows:...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/22C08L97/02C08L1/02C08L23/16C08K5/00C08K5/12C08K5/18C08J9/04C08J9/08A43B13/04
CPCC08L23/22A43B13/04C08J9/04C08J9/08C08J2323/22C08J2497/02C08K2201/014C08L2203/14C08L2205/035C08L2205/16C08L97/02C08L1/02C08L23/16C08K5/00C08K5/12C08K5/18
Inventor 钱忠华
Owner NANTONG LONGBANG PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com