A kind of celadon and preparation method thereof

A technology of celadon and parts by weight, applied in the field of celadon and its preparation, can solve the problems of being unsuitable for mass production, easy to wear, break, and low yield, and achieve the effects of good compactness, unbreakable, and low yield.

Active Publication Date: 2020-12-01
龙泉市昌宏瓷业有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the current Longquan celadon is very easy to wear and break during use. In addition, the method of preparing celadon is not only high in cost but also low in yield, which is not suitable for mass production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of celadon and preparation method thereof
  • A kind of celadon and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of celadon, using mineral raw materials and polymer materials to prepare blanks and glazes, the blanks include component A, component B and component C, the weight and number ratio of each raw material in the component A is: 110 parts of kaolin, 15 parts of cooked talc, 25 parts of dolomite, 15 parts of high alumina bauxite; the weight and number ratio of each raw material in the described component B is: 40 parts of quartz, 10 parts of magnesite, 40 parts of calcite, specifically Yes, the ratio of parts by weight of the raw materials of the component C is: 5 parts of long-chain fatty acid ester, 8 parts of polyethylene wax, 3 parts of epoxy resin, 3 parts of silicone resin, and 5 parts of polyimide; The ratio of parts by weight of each component of the glaze is: 60 parts of kaolin, 20 parts of clay, 30 parts of quartz, 10 parts of wollastonite, 10 parts of muscovite, and 20 parts of glaze ash.

[0025] Prepare 2,000 celadon bowls according to the above raw mater...

Embodiment 2

[0039] A kind of celadon, using mineral raw materials and polymer materials to prepare blanks and glazes, the blanks include component A, component B and component C, the weight and number ratio of each raw material in the component A is: 120 parts of kaolin, 20 parts of cooked talc, 30 parts of dolomite, 20 parts of high alumina bauxite; the weight and number ratio of each raw material in the component B is: 50 parts of quartz, 20 parts of magnesite, 50 parts of calcite, and 10 parts of C, specifically, the weight-to-number ratio of each raw material of the component C is: 8 parts of long-chain fatty acid ester, 12 parts of polyethylene wax, 5 parts of epoxy resin, 5 parts of silicone resin, polyimide 8 parts; the ratio of parts by weight of each component of the glaze is: 80 parts of kaolin, 30 parts of clay, 40 parts of quartz, 20 parts of wollastonite, 15 parts of muscovite, and 30 parts of glaze ash.

[0040] Prepare 2,000 celadon bowls according to the above raw material...

Embodiment 3

[0051] A kind of celadon, using mineral raw materials and polymer materials to prepare blanks and glazes, the blanks include component A, component B and component C, the weight and number ratio of each raw material in the component A is: 115 parts of kaolin, 18 parts of cooked talc, 28 parts of dolomite, 16 parts of high alumina bauxite; the weight and number ratio of each raw material in the described component B is: 45 parts of quartz, 16 parts of magnesite, 44 parts of calcite, specifically The weight-to-number ratio of each raw material of the component C is: 7 parts of long-chain fatty acid ester, 9 parts of polyethylene wax, 4 parts of epoxy resin, 4 parts of silicone resin, and 7 parts of polyimide; The weight ratio of each component of the glaze is: 66 parts of kaolin, 26 parts of clay, 35 parts of quartz, 18 parts of wollastonite, 12 parts of muscovite, and 25 parts of glaze ash.

[0052] The weight-to-number ratios of the raw materials of component C are: 7 parts of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a celadon and a preparation method thereof. A mineral raw material and a polymer material are used for preparation of a blank and glaze. The blank comprises a component A, a component B and a component C. The component A comprises, by weight, 20-30 parts of dolomite and 10-20 parts of high bauxite. The component B includes 10-20 parts by weight of magnesite. The component Ccomprises 3-5 parts by weight of epoxy resin and 3-5 parts by weight of organic silicon resin. The glaze comprises 10-20 parts by weight of wollastonite and 10-15 parts by weight of white mica. The preparation method comprises blank slurry preparation, glaze preparation, blank molding, biscuiting, glazing and glaze firing. The celadon has the advantages of high strength, high temperature resistance and corrosion resistance. The preparation method realizes a low cost, has a high yield and is suitable for mass production.

Description

technical field [0001] The invention belongs to the technical field of porcelain, and in particular relates to celadon and a preparation method thereof. Background technique [0002] Longquan celadon is a treasure of traditional porcelain with Chinese characteristics. During the Southern and Northern Dynasties, people in Longquan, Zhejiang Province made use of the local superior natural conditions to manufacture celadon. Longquan celadon is known as the center of the porcelain garden for its glaze color as green as jade, bright as a mirror, and sound like a chime. A bright pearl, loved by celadon lovers all over the world. [0003] However, the current Longquan celadon is very easy to wear and break during use, and the method for preparing celadon is not only high in cost but also low in yield, and is not suitable for mass production. Contents of the invention [0004] In order to overcome the deficiencies of the prior art, the present invention provides a high-strength, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/14C04B33/13C04B33/24C04B33/34
CPCC03C8/14C04B33/13C04B33/1305C04B33/24C04B33/34C04B35/63408C04B35/63452C04B35/63468C04B2235/3206C04B2235/3208C04B2235/321C04B2235/3217C04B2235/3418C04B2235/483
Inventor 金乾华李启岳梅景丰金建峰
Owner 龙泉市昌宏瓷业有限公司