High-tenacity antibacterial plastic and preparation process thereof
An antibacterial plastic and high toughness technology, applied in the field of plastics, can solve the problems of poor heat resistance, poor durability, easy leakage, etc., and achieve the effects of good safety, good antibacterial ability, excellent mechanical properties and processing performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0034] Example 1 High-toughness antibacterial plastic and its preparation
[0035] The formula of high-toughness antibacterial plastic: 40 parts by weight of polyphenylene ether, 80 parts by weight of polystyrene, 1 part by weight of oleic acid and n-propylamine modified silver nanoparticles, methacrylate-butadiene-styrene core-shell structure copolymer 物20 parts by weight.
[0036] The preparation process of high toughness antibacterial plastic includes the following steps:
[0037] (1) Dry the raw materials at 75°C for 10 hours;
[0038] (2) Weigh the dried raw materials according to the formula, stir and mix in a high-speed mixer at 70°C at 400 rpm for 10 minutes, and then extrude and granulate in a twin-screw extruder. The temperatures from the feeding section to the die are: 25°C, 230°C, 240°C, 240°C, 240°C, 250°C, 250°C, 250°C, 240°C, and the rotating speed is 180 revolutions per minute. The mixture is heated and melted. The body, driven by the screw, flows out from the die, is...
Example Embodiment
[0040] Example 2 High-toughness antibacterial plastic and its preparation
[0041] The formulation of the high-toughness antibacterial plastic: 40 parts by weight of polyphenylene ether, 80 parts by weight of polystyrene, 1 part by weight of oleic acid and n-propylamine modified silver nanoparticles, maleic anhydride modified styrene-(ethylene-butene)- 20 parts by weight of styrene block copolymer.
[0042] The preparation process of high toughness antibacterial plastic includes the following steps:
[0043] (1) Dry the raw materials at 75°C for 10 hours;
[0044] (2) Weigh the dried raw materials according to the formula, stir and mix in a high-speed mixer at 70°C at 400 rpm for 10 minutes, and then extrude and granulate in a twin-screw extruder. The temperatures from the feeding section to the die are: 25°C, 230°C, 240°C, 240°C, 240°C, 250°C, 250°C, 250°C, 240°C, and the rotating speed is 180 revolutions per minute. The mixture is heated and melted. The body, driven by the screw, ...
Example Embodiment
[0047] Example 3 High-toughness antibacterial plastic and its preparation
[0048] The formulation of the high-toughness antibacterial plastic: 40 parts by weight of polyphenylene ether, 80 parts by weight of polystyrene, 1 part by weight of oleic acid and n-propylamine modified silver nanoparticles, maleic anhydride modified methacrylate-butadiene-benzene 20 parts by weight of ethylene core-shell structure copolymer.
[0049] The preparation process of high toughness antibacterial plastic includes the following steps:
[0050] (1) Dry the raw materials at 75°C for 10 hours;
[0051] (2) Weigh the dried raw materials according to the formula, stir and mix in a high-speed mixer at 70°C at 400 rpm for 10 minutes, and then extrude and granulate in a twin-screw extruder. The temperatures from the feeding section to the die are: 25°C, 230°C, 240°C, 240°C, 240°C, 250°C, 250°C, 250°C, 240°C, and the rotating speed is 180 revolutions per minute. The mixture is heated and melted. The body, d...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap