A multi-element alloyed aluminum alloy material, cylinder liner and preparation method thereof

A multi-element alloy and aluminum alloy technology, applied in the direction of cylinders, cylinder heads, mechanical equipment, etc., can solve the problems of complex formula composition, tensile strength to be improved, etc., and achieve the effect of compact structure, improved performance indicators, and increased tensile strength

Active Publication Date: 2019-05-31
HENAN UNIV OF SCI & TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a multi-element alloyed aluminum alloy cylinder liner, so as to solve the problems that the existing aluminum alloy cylinder liner has complex formula composition and the tensile strength needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A multi-element alloyed aluminum alloy material, cylinder liner and preparation method thereof
  • A multi-element alloyed aluminum alloy material, cylinder liner and preparation method thereof
  • A multi-element alloyed aluminum alloy material, cylinder liner and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The multi-element alloyed aluminum alloy cylinder liner of this embodiment is composed of the following components in weight percentage: 25% silicon, 6% magnesium, 0.5% titanium, 1% zirconium, and the balance is Al.

[0045] The preparation method of the multi-element alloyed aluminum alloy cylinder liner of this embodiment comprises the following steps:

[0046] 1) Heat crystalline silicon, aluminum block, magnesium block, Al-10Ti master alloy, and zirconium block to 850°C for melting to obtain an aluminum alloy melt;

[0047] After the aluminum alloy melt drops to 780°C, add a refining agent to refine the aluminum alloy melt. After refining, heat the aluminum alloy melt to 830°C and add a modifier for modification. The process of smelting, refining and modification is uniform Carry out slagging treatment and carry out under the protection of argon; stand still for 10 minutes after modification treatment to obtain aluminum alloy melt;

[0048] The refining agent used ...

Embodiment 2

[0053] The multi-element alloyed aluminum alloy cylinder liner of this embodiment is composed of the following components in weight percentage: 25% silicon, 6% magnesium, 0.5% titanium, 1% zirconium, and the balance is Al.

[0054] The preparation method of the multi-element alloyed aluminum alloy cylinder liner of the present embodiment adopts figure 1 The electromagnetic centrifugal casting equipment shown comprises the following steps:

[0055] 1) Heat crystalline silicon, aluminum block, magnesium block, Al-10Ti master alloy, and zirconium block to 850°C for melting to obtain an aluminum alloy melt;

[0056] After the aluminum alloy melt drops to 780°C, add a refining agent to refine the aluminum alloy melt. After refining, heat the aluminum alloy melt to 830°C and add a modifier for modification. The process of smelting, refining and modification is uniform Carry out slagging treatment and carry out under the protection of argon; stand still for 10 minutes after modifica...

Embodiment 3～4

[0060] The multi-element alloyed aluminum alloy cylinder liners of Examples 3-4 have the same composition as that of Example 1.

[0061] The preparation method of the multi-element alloyed aluminum alloy cylinder liner of Examples 3-4 is basically the same as that of Example 2, except that the magnetic field strengths are 0.1T and 0.2T respectively.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relate to a multi-component alloying aluminum alloy material, an air cylinder sleeve and a preparation method thereof. The multi-component alloying aluminum alloy air cylinder sleeve isprepared from the following components in percentage by weight: 20-30% of silicon, 5-10% of magnesium, 0.1-1% of titanium, 0.1-1.5% of zirconium and the balance of aluminum. The multi-component alloying aluminum alloy air cylinder sleeve provided by the invention is based on a lattice matching principle. By adding a proper amount of Ti and Zr, an Al-Si-Mg matrix tissue is refined effectively, wherein the element Ti can refine the aluminum alloy matrix, the element Zr can refine the grain size of MG, and more MgSi2 second phase particles can be formed favorably. The formula of the multi-component alloying aluminum alloy air cylinder sleeve is simple in component, and does not contain noble elements such as Ni, so that the production cost is relatively low; and the elements are proportionedreasonably and have a synergistic action, so that the aluminum alloy matrix tissue is fined favorably, and the mechanical properties such as tensile strength of the air cylinder sleeve are improved.

Description

technical field [0001] The invention belongs to the technical field of preparation of a multi-element alloyed aluminum alloy cylinder liner, and in particular relates to a multi-element alloyed aluminum alloy material, a cylinder liner and a preparation method thereof. Background technique [0002] With the continuous enhancement of social environmental protection awareness, the automobile industry has continuously introduced new and more stringent exhaust emission standards, which has brought considerable difficulties to the entire automobile field. Optimizing the design structure of the locomotive, promoting the efficient operation of the engine and reducing the weight of the locomotive are effective ways to solve the problem of reducing exhaust emissions of the current fuel locomotive. [0003] As a key component in the engine, the cylinder liner determines the performance and life of the engine. At present, the materials used for traditional cylinder liners are mostly c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/02B22D13/02F02F1/00
CPCB22D13/02C22C21/02F02F1/004
Inventor 熊毅路妍岳赟贺甜甜范梅香陈艳娜姚怀曹伟马景灵张凌峰任凤章
Owner HENAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com