Acrylic ester pressure sensitive adhesive, pressure sensitive adhesive tape and preparation method of acrylic ester pressure sensitive adhesive

A technology of acrylate and butyl acrylate, which is applied in the field of pressure-sensitive adhesives, can solve the problems of poor high temperature resistance and electrolyte resistance, and achieve excellent high temperature resistance and electrolyte resistance, high production efficiency, and excellent adhesion performance effect

Active Publication Date: 2018-04-03
东莞市骏青电子科技有限公司
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to overcome the shortcomings and deficiencies in the prior art, the object of the present invention is to provide an acrylate pressure-sensitive adhesive, which uses isoprene rubber and SBS elastomer modified acrylate pressure-sensitive adhesive , so that the acrylate pressure-sensitive adhesive has the advantages of acrylate and has the electrolyte and high-temperature resistance of rubber, effectively overcoming the defects of the existing acrylate pressure-sensitive adhesives of poor high-temperature resistance and electrolyte resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An acrylate pressure-sensitive adhesive, comprising the following raw materials in parts by weight: 8 parts of isooctyl acrylate, 7 parts of butyl acrylate, 3 parts of acrylic acid, 4 parts of vinyl acetate, 3 parts of methyl methacrylate, hydroxymethacrylate 3 parts of ethyl ester, 2 parts of trimethylolpropane triacrylate, 4 parts of isoprene rubber with double bond, 4 parts of SBS elastomer with double bond, 45 parts of solvent, and 0.3 part of initiator.

[0027] The solvent is acetone, ethyl ester and toluene, specifically 15 parts of acetone, 20 parts of ethyl ester and 10 parts of toluene.

[0028] The initiator is a BPO initiator.

[0029] A pressure-sensitive adhesive tape as described above, comprising a tape base layer and an adhesive layer coated on the adhesive tape base layer, the adhesive layer is mixed by the acrylate pressure-sensitive adhesive and Bayer 3100 crosslinking agent in a weight ratio of 111:0.1 made.

[0030] Wherein, the thickness of the ...

Embodiment 2

[0038] An acrylate pressure-sensitive adhesive, comprising the following raw materials in parts by weight: 9 parts of isooctyl acrylate, 7.8 parts of butyl acrylate, 3.2 parts of acrylic acid, 4.5 parts of vinyl acetate, 3.4 parts of methyl methacrylate, hydroxymethacrylate 3.2 parts of ethyl ester, 2.2 parts of trimethylolpropane triacrylate, 4.5 parts of isoprene rubber with double bond, 4.5 parts of SBS elastomer with double bond, 48 parts of solvent, and 0.38 part of initiator.

[0039] The solvent is acetone, ethyl ester and toluene, specifically 16 parts of acetone, 21 parts of ethyl ester and 11 parts of toluene.

[0040] The initiator is a BPO initiator.

[0041] A kind of pressure-sensitive adhesive tape as above, comprises adhesive tape substrate layer and the adhesive layer that is coated on adhesive tape substrate layer, adhesive layer is mixed by weight ratio 111:0.15 by described acrylate pressure-sensitive adhesive and Bayer 3100 crosslinking agent made.

[00...

Embodiment 3

[0050] An acrylate pressure-sensitive adhesive, comprising the following raw materials in parts by weight: 10 parts of isooctyl acrylate, 8.5 parts of butyl acrylate, 3.5 parts of acrylic acid, 5 parts of vinyl acetate, methyl methacrylate 3.8 parts, 3.5 parts of hydroxyethyl methacrylate, 2.5 parts of trimethylolpropane triacrylate, 5 parts of isoprene rubber with double bond, 5 parts of SBS elastomer with double bond, 51 parts of solvent, initiator 0.45 parts of the agent.

[0051] The solvent is acetone, ethyl ester and toluene, specifically 17 parts of acetone, 22 parts of ethyl ester and 12 parts of toluene.

[0052] The initiator is a BPO initiator.

[0053] A pressure-sensitive adhesive tape as described above, comprising a tape base layer and an adhesive layer coated on the adhesive tape base layer, the adhesive layer is mixed by the acrylate pressure-sensitive adhesive and Bayer 3100 crosslinking agent in a weight ratio of 111:0.2 made.

[0054] Wherein, the thickn...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of a pressure sensitive adhesive, in particular to an acrylic ester pressure sensitive adhesive, a pressure sensitive adhesive tape and a preparation method of the acrylic ester pressure sensitive adhesive. The acrylic ester pressure sensitive adhesive provided by the invention is prepared from the following raw materials in parts by weight: 8 to 12 parts of 2-ethylhexyl acrylate, 7 to 10 parts of butyl acrylate, 3 to 4 parts of acrylic acid, 4 to 6 parts of vinyl acetate, 3 to 4.5 parts of methyl methacrylate, 3 to 4 parts of hydroxyethyl methylacrylate, 2 to 3 parts of trimethylolpropane triacrylate, 4 to 6 parts of isoprene rubber with double bonds, 4 to 6 parts of SBS elastomers with double bonds, 45 to 60 parts of solvents and 0.3 to 0.6 part of initiating agents. The acrylic ester pressure sensitive adhesive provided by the invention uses the isoprene rubber and the SBS elastomers for modifying the acrylic ester pressure sensitive adhesive, so that the acrylic ester pressure sensitive adhesive has the advantages of acrylic ester, and also has the electrolyte-resistant and high-temperature-resistant performance of rubber; the defectof poor electrolyte-resistant and high-temperature-resistant performance of the existing acrylic ester pressure sensitive adhesive can be effectively overcome.

Description

technical field [0001] The invention relates to the technical field of pressure-sensitive adhesives, in particular to an acrylate pressure-sensitive adhesive, a pressure-sensitive adhesive tape and a preparation method of the acrylate pressure-sensitive adhesive. Background technique [0002] Traditional acrylate pressure-sensitive adhesives do not contain unsaturated bonds in their molecular structure and have the advantages of aging resistance, light resistance, wide bonding surface, and colorless and transparent. However, the high-temperature resistance of traditional acrylate pressure-sensitive adhesives is not good. The final acrylate pressure-sensitive adhesive can only be used in a short-term environment at 150°C, and the electrolyte resistance of traditional acrylic pressure-sensitive adhesives is not good, and the adhesive layer will be soaked in the electrolyte environment for 3 to 4 hours. Osmotically swells, thereby losing viscosity. Therefore, how to effectivel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J151/00C09J151/04C09J7/38C08F291/02C08F220/18C08F220/06C08F218/08C08F220/14C08F220/20C08F222/14
CPCC08F218/08C08F220/06C08F220/14C08F220/20C08F222/103C08F279/02C08F287/00C09J151/006C09J151/04C08F220/1808
Inventor 张涛辉伍平
Owner 东莞市骏青电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products