A kind of sanitary ceramic glaze with three-dimensional flashing effect

A sanitary ceramic, three-dimensional technology, applied in the field of sanitary ceramic glaze, can solve the problem of lack of personalized products, and achieve the effects of good roughness, low water absorption, and good anti-cracking performance

Active Publication Date: 2020-06-23
JOMOO KITCHEN & BATHROOM
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. Most of the industry is ordinary white glaze, lacking personalized products; with the steady growth of GDP, the income of ordinary people is also increasing, and they are beginning to pay attention to bathroom decoration, and the demand for personalized high-end sanitary ceramics is increasing. In the future, personalized, mid-to-high-end Sanitary ceramics market has broad prospects;
[0004] 2. There have been some personalized decorative sanitary ceramic products on the market, but most of the surface is made of organic materials, not real ceramic materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of sanitary ceramic glaze with three-dimensional flashing effect
  • A kind of sanitary ceramic glaze with three-dimensional flashing effect
  • A kind of sanitary ceramic glaze with three-dimensional flashing effect

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 1. With water as the medium, 25.3 parts of red lead, 7.2 parts of quartz, 37.1 parts of feldspar, and 3.6 parts of K 2 CO 3 , 8.8 parts of Na 2 CO 3 , 7.5 parts of limestone, 10.0 parts of frit, and 0.15 parts of CMC (sodium carboxymethyl cellulose) were weighed.

[0030] 2. Put the above raw materials into a ceramic ball mill for ball milling. When the particle size reaches 10 μm, accounting for 68%, add 10 parts of high-temperature mica powder material, and continue ball milling until the particle size reaches 10 μm, accounting for 69%. Get the glaze slurry;

[0031] 3. Refining the above-mentioned glaze slurry materials, the performance can reach: the concentration is 351g / 200mL, the slurry temperature is 27°C, and the viscosity is V 0 It is a slurry with a yield value of 13 and a yield value of 83s / 100mL.

[0032] 4. Spray the above-mentioned sanitary ceramic glaze on the surface of the above-mentioned sanitary ceramics, and fire the kiln at 850° C. for 15 hour...

Embodiment 2

[0035] 1. With water as the medium, 25.9 parts of red lead, 7.7 parts of quartz, 36.8 parts of feldspar, and 3.4 parts of K 2 CO 3 , 8.9 parts of Na 2 CO 3 , 7.3 parts of limestone, 10 parts of frit, and 0.15 parts of CMC (sodium carboxymethylcellulose) weighed.

[0036] 2. Put the above raw materials into a ceramic ball mill for ball milling. When the particle size reaches 10 μm, accounting for 68%, add 10 parts of high-temperature mica powder material, and continue ball milling until the particle size reaches 10 μm, accounting for 69%. Get the glaze slurry;

[0037] 3. Refining the above-mentioned glaze slurry material, the performance can reach: a slurry with a concentration of 352g / 200mL, a slurry temperature of 27°C, a viscosity V0 of 84s / 100mL, and a yield value of 13.

[0038]4. Spray the above-mentioned sanitary ceramic glaze on the surface of the above-mentioned sanitary ceramics, and fire the kiln at 880° C. for 15 hours to obtain a sanitary ceramic product with ...

Embodiment 3

[0041] 1. With water as the medium, 24.5 parts of red lead, 7.4 parts of quartz, 37.7 parts of feldspar, and 4.0 parts of K 2 CO 3 , 9.1 parts of Na 2 CO 3 , 7.8 parts of limestone, 9.5 parts of frit, and 0.15 parts of CMC (sodium carboxymethylcellulose) weighed.

[0042] 2. Put the above raw materials into a ceramic ball mill for ball milling. When the particle size reaches 10 μm, accounting for 68%, add 10 parts of high-temperature mica powder material, and continue ball milling until the particle size reaches 10 μm, accounting for 69%. Get the glaze slurry;

[0043] 3. Refining the above-mentioned glaze slurry material, the performance can reach: a slurry with a concentration of 350g / 200mL, a slurry temperature of 22°C, a viscosity V0 of 75s / 100mL, and a yield value of 7.

[0044] 4. Spray the above-mentioned sanitary ceramic glaze on the surface of the above-mentioned sanitary ceramics, and fire it out of the kiln at 890° C. for 15 hours to obtain a sanitary ceramic pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sanitary ceramic glaze with a stereoscopic flickering effect. The sanitary ceramic glaze comprises the following raw materials in parts by mass: 22.0-28.0 parts of minium, 5.0-10.0 parts of quartz, 35.0-40.0 parts of feldspar, 3.0-5.0 parts of K2CO3, 8.0-10.0 parts of Na2CO3, 7.0-9.0 parts of limestone, 8.5-11.5 parts of frits, 0.01-0.50 part of CMC (carboxyl methyl cellulose) and 8-12 parts of mica powder. The ceramic glaze surface prepared by the method provided by the invention has golden yellow metal texture, and meanwhile, the surface has a flickering effect.

Description

technical field [0001] The invention relates to a sanitary ceramic glaze with three-dimensional flashing effect. Background technique [0002] The existing sanitary ceramics have the following problems: [0003] 1. Most of the industry is ordinary white glaze, lacking personalized products; with the steady growth of GDP, the income of ordinary people is also increasing, and they are beginning to pay attention to bathroom decoration, and the demand for personalized high-end sanitary ceramics is increasing. Sanitary ceramics market has broad prospects; [0004] 2. There have been some personalized decorative sanitary ceramic products on the market, but most of the surface is made of organic materials, not real ceramic materials. Contents of the invention [0005] The main purpose of the present invention is to provide a sanitary ceramic glaze with three-dimensional flashing effect. [0006] The adopted technical scheme that the present invention solves its technical probl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More