Preparation method for low-odor colored tile grout

A technology for color tiles and caulking agent, applied in the field of building materials, can solve the problems of large odor and affect the quality of color tile caulking agent, etc., and achieve the effects of improving fluidity, reducing the volatilization of irritating odor and simple operation.

Inactive Publication Date: 2018-04-10
安徽力峰建材科技有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the existing ceramic tile grout has the defect that the peculiar smell is bigger after use, and it takes a long time to dissipate the peculiar smell, which has seriously affected the quality of the colored tile grout

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A preparation method of a low-odor colored tile grout, comprising the following steps:

[0016] (1) In parts by weight, add 36 parts of bamboo powder to 65 parts of water, stir evenly, heat to 85°C, then add 3 parts of polyethanolamine, 1 part of polyglycerin fatty acid ester, 9 parts of phytic acid Sodium, after mixing and stirring evenly, after heat preservation treatment for 2 hours, after the mixture was cooled to room temperature, after spray drying treatment, the deodorant was obtained;

[0017] (2) In parts by weight, mix evenly 40 parts of white cement, 39 parts of quartz powder, 1 part of ethylene-vinyl acetate, 5 parts of deodorant, and 2 parts of pigment to obtain a finished product.

[0018] Specifically, in the above step (1), the average particle size of the bamboo powder is 200 mesh.

[0019] Specifically, in the above step (1), the polyethanolamine has a molecular weight of 1800 and a purity of 99%.

[0020] Specifically, in the above step (2), the pig...

Embodiment 2

[0023] A preparation method of a low-odor colored tile grout, comprising the following steps:

[0024] (1) In parts by weight, add 40 parts of bamboo powder to 68 parts of water, stir evenly, heat to 88°C, then add 4 parts of polyethanolamine, 2 parts of polyglycerin fatty acid ester, 12 parts of phytic acid Sodium, after mixing and stirring evenly, after heat preservation treatment for 2.5 hours, after the mixture was cooled to room temperature, after spray drying treatment, the deodorant was obtained;

[0025] (2) In parts by weight, after uniformly mixing 44 parts of white cement, 41 parts of quartz powder, 2 parts of ethylene-vinyl acetate, 7 parts of deodorant, and 3 parts of pigment, the finished product is obtained.

[0026] Specifically, in the above step (1), the average particle size of the bamboo powder is 230 mesh.

[0027] Specifically, in the above step (1), the polyethanolamine has a molecular weight of 1800 and a purity of 99%.

[0028] Specifically, in the a...

Embodiment 3

[0031] A preparation method of a low-odor colored tile grout, comprising the following steps:

[0032] (1) In parts by weight, add 44 parts of bamboo powder to 70 parts of water, stir evenly, heat to 90°C, then add 5 parts of polyethanolamine, 2 parts of polyglycerin fatty acid ester, 14 parts of phytic acid Sodium, after mixing and stirring evenly, after heat preservation treatment for 3 hours, after the mixture was cooled to room temperature, after spray drying treatment, the deodorant was obtained;

[0033] (2) In parts by weight, mix evenly 46 parts of white cement, 43 parts of quartz powder, 3 parts of ethylene-vinyl acetate, 10 parts of deodorant, and 4 parts of pigment to obtain a finished product.

[0034] Specifically, in the above step (1), the average particle size of the bamboo powder is 250 mesh.

[0035] Specifically, in the above step (1), the polyethanolamine has a molecular weight of 1800 and a purity of 99%.

[0036] Specifically, in the above step (2), the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method for low-odor colored tile grout. The preparation method comprises the following steps: (1) adding bamboo powder into water, carrying out uniform mixing under stirring, then carrying out heating to 85-90 DEG C, adding polyethanolamine, polyglycerol fatty acid ester and sodium phytate, carrying out uniform mixing under stirring, treating the obtained mixture for 2-3 h with the temperature maintained at 85-90 DEG C, cooling the mixture to room temperature and then carrying out spray-drying to prepare a deodorant; and (2) uniform mixing white cement, quartz powder, ethylene-vinyl acetate, the deodorant and pigments so as to obtain the finished low-odor colored tile grout. The preparation method provided by the invention has the advantages of simpleoperation and low cost; and the addition of the deodorant does not affect the original excellent performances of the grout and can effectively remove peculiar smell of the grout applied on a tile andreduce the volatilization of the irritating odor of the tile grout.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a preparation method of a low-odor colored ceramic tile caulking agent. Background technique [0002] The caulking agent has the characteristics of strong adhesion, small shrinkage, strong color fixation, anti-crack flexibility, good decorative texture, pressure resistance, wear resistance, and mold resistance, making it perfect for repairing cracks or damage on the floor surface. The surface can also be painted and has good water resistance. The caulking agent is rich in color and can be prepared by itself, so it is more and more popular among customers. But existing tile grouting agent, after use, exists the defective that peculiar smell is bigger, needs longer time just to disperse peculiar smell, has had a strong impact on the quality of colored tile grouting agent. Contents of the invention [0003] In order to solve the above-mentioned technical p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B24/28C04B111/82
CPCC04B28/04C04B40/0039C04B2111/00025C04B2111/82C04B14/06C04B24/045C04B14/307C04B24/00C04B24/283C04B24/003C04B24/28C04B14/308
Inventor 钱学锋
Owner 安徽力峰建材科技有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com