Drain brick and preparation method thereof

A technology of sewer and pure calcium aluminate cement is applied in the field of refractory materials, which can solve the problem of high cost of sewer bricks, and achieve the effects of reducing the preparation cost, solving the difficulty of forming, and eliminating the need for high-temperature sintering.

Active Publication Date: 2018-04-13
河南新拓耐火材料有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, corundum, or even pure corundum, is used for vibration molding to prepare drain bricks, resulting in high cost of drain bricks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Drain brick and preparation method thereof
  • Drain brick and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Prepare the drain bricks as follows:

[0041] 1. Weigh the following raw materials and mix them evenly:

[0042] Homogenized bauxite clinker 60Kg, wherein, Al in the homogenized material 2 o 3 The mass fraction is 78%. The homogenized material is composed of a homogenized material with a particle size of 5-3 mm, a homogenized material with a particle size of 3-1 mm, and a homogenized material with a particle size of 1-0 mm. The mass ratio 1:2:2, the density of the homogenized bauxite clinker is 2.8g / cm 3 ;

[0043] 20Kg of corundum, wherein the corundum is composed of corundum with a particle size of 1-0mm and corundum powder with a particle size of 240 mesh, the corundum with a particle size of 1-0mm and the corundum with a particle size of 240 mesh The mass ratio of the powder is 1:3, the corundum is white corundum, and the density of the corundum is 3.5g / cm 3 ;

[0044] Spinel 10Kg, the particle size of described spinel is 310 orders;

[0045] Al 2 o 3 20Kg...

Embodiment 2

[0051] Referring to the method described in Example 1 to prepare the drain brick, the only difference is that the ratio of the amount of each raw material is different (the particle size of each raw material is the same as that of Example 1), specifically, the homogenized bauxite clinker 50Kg , corundum 25Kg, spinel 15Kg, Al 2 o 3 25Kg, pure calcium aluminate cement 3Kg, silicon dioxide 1Kg and ADS 0.2Kg; Wherein, in the described homogenized alumina clinker, Al 2 o 3 The quality score is 75%.

Embodiment 3

[0053] Referring to the method described in Example 1 to prepare the drain brick, the only difference is that the ratio of the amount of each raw material is different (the particle size of each raw material is the same as that of Example 1), specifically, the homogenized bauxite clinker 70Kg , corundum 15Kg, spinel 8Kg, Al 2 o 3 15Kg, pure calcium aluminate cement 8Kg, silicon dioxide 2Kg and ADS 0.1Kg; Wherein, in the described homogeneous bauxite clinker, Al 2 o 3 The quality score is 85%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a drain brick and a preparation method thereof. The drain brick comprises a drain brick main body, and the drain brick main body is mainly prepared from the following raw materials in parts by weight: 50-70 parts of homogenized calcined bauxite, 15-25 parts of corundum, 8-15 parts of spinel, 15-25 parts of Al2O3, 3-8 parts of calcium aluminate cement, 1-2 parts of silicondioxide and 0.1-0.3 part of an additive, wherein the mass fraction of Al2O3 in the homogenized calcined bauxite is 75-85%. The drain brick has the advantages of favorable performance, high safety andreliability, low cost and high performance cost ratio. The preparation method is simple to operate, does not need high-temperature sintering, and is molded through vibration only.

Description

technical field [0001] The invention relates to the field of refractory materials, in particular to a drain brick and a preparation method thereof. Background technique [0002] With the development of fast and efficient continuous casting and secondary refining technology and process, the sliding nozzle (Sliding Nozzle, SN for short) system is becoming more and more important in the modern iron and steel smelting process, becoming an indispensable part of smelting. It is a control device for molten steel in the casting process of the continuous casting machine. It can precisely adjust the water flow from the ladle to the continuous casting tundish, so that the inflow and outflow of molten steel can be balanced, so that the continuous casting operation is easier to control. The sliding nozzle system has been developed rapidly because of its good controllability and the ability to improve steelmaking production efficiency. Now, the sliding nozzle system is widely used at hom...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/101B22D41/54
CPCB22D41/54C04B35/101C04B2235/3222C04B2235/3418C04B2235/5427C04B2235/5436C04B2235/602C04B2235/77C04B2235/96
Inventor 李巍马建民吴红梅刘光良赵飞飞
Owner 河南新拓耐火材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap