Preparation method of low-odor zinc stearate

A zinc stearate, low-odor technology, applied in the field of rubber and plastic additives, can solve problems such as obstruction, large obstruction, and low purity

Inactive Publication Date: 2018-04-13
江西宏远化工有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing odor rating reference is divided into 1-6 levels, 1st level evaluation standard: can not feel; 2nd level evaluation standard: can be felt, no hindrance; Major hindrance; Level 4 evaluation standard: obstructed; Level 5 evaluation standard: relatively large obstruction; Level 6 evaluation standard: unbearable
[0003] In recent years, there are two main methods for the production of zinc stearate: one is to use metathesis production, firstly add caustic soda to stearic acid for neutralization reaction, then add zinc salt for metathesis...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] A method for preparing low-odor zinc stearate is to put 100Kg of fatty acid into the reactor, start stirring and raise the temperature to 80-90°C, after it melts, under the condition of 0.01-0.02 MPa and 90°C, pump air through micro-vacuum 15min; then add 16Kg of zinc oxide, 2Kg of hydrogen peroxide, and 10Kg of water in sequence, raise the temperature to 130-135°C, keep warm for 30min, turn on the vacuum of 0.03-0.04MPa, and perform low-vacuum deodorization operation until the color of the reaction solution changes from milky white to clear Transparent, that is, the reaction is complete; then turn on the vacuum of 0.05-0.08 MPa, carry out high-vacuum deodorization operation, and last for 20-25 minutes, and finally discharge and pulverize.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A method for preparing low-odor zinc stearate is to put fatty acid into the reactor, start stirring and heat up, and after it melts, under the conditions of 0.01-0.02 MPa and 90°C, evacuate for 10-15min by micro-vacuum to remove Most stearic acid contains odorous low-boiling molecules; then add zinc oxide and catalyst in sequence, heat up to 130-135°C, turn on vacuum 0.03-0.04MPa, and perform low-vacuum deodorization operation until the color of the reaction solution changes from milky white to In order to be clear and transparent, the reaction is complete; after that, a vacuum of 0.05-0.08 MPa is turned on, and a high-vacuum deodorization operation is carried out, and finally the material is discharged and pulverized. The preparation method of the low-odor zinc stearate of the present invention uses the original three-stage vacuum deodorization technology in the reaction process, and the prepared zinc stearate has lower odor and higher purity and is completely suitable for the field of low-odor plastics.

Description

technical field [0001] The invention relates to the field of rubber and plastic additives, in particular to a method for preparing low-odor zinc stearate. Background technique [0002] Plastics are used more and more in daily life. With people's requirements for ride comfort, health and safety, low-VOC and low-odor plastics are favored by manufacturers, especially in automotive plastics and yoga mats. Formed a low-odor plastic industry. Zinc stearate is commonly used as an additive in plastic production. In the field of low-odor plastics, there is also a corresponding low-odor requirement in the industry. It must pass the corresponding odor test. Generally, the odor level is required to be ≦2. The existing odor rating reference is divided into 1-6 levels, 1st level evaluation standard: can not feel; 2nd level evaluation standard: can be felt, no hindrance; Big hindrance; Grade 4 evaluation standard: obstructed; Grade 5 evaluation standard: relatively large obstruction; Gra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C07C51/41C07C51/43C07C53/126
CPCC07C51/412C07C51/43C07C53/126
Inventor 吴旅良洪颖熊洪龙
Owner 江西宏远化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products