Medium-temperature degreasing agent for automobile coating surface conditioning pretreatment and degreasing method thereof

A degreasing agent and medium-temperature technology, which is applied in the field of medium-temperature degreasing agent and its degreasing before the surface adjustment of automobile coating, which can solve the problems of affecting product quality, unfavorable on-site operation environment, strong volatility, etc., and avoid cleaning uncleanness and cleaning Good effect and strong dissolving power

Inactive Publication Date: 2018-04-13
武汉钢铁有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Traditional degreasing agents mainly include the following categories: 1) Organic solvents, such as gasoline, freon, trichloroethane, toluene, ethanol, etc., organic solvents have a good cleaning effect on soluble oil stains, but it is difficult to remove inorganic particles, metal particles, etc. And general volatility is strong, poisonous and harmful, be unfavorable for on-the-spot operation environment; May cause metal surface corrosion; 3) emulsion, can remove all kinds of oil stains on the metal surface, and has good cleaning effect, but generally has poor stability and cannot be stored for a long time. cost
[0005] In addition, the coating production line is a continuous production line with fast production speed. Different coating production lines have different cleaning temperatures.
With the existing degreasing agent, the saponification and emulsification ability is not strong under medium temperature cleaning at 40-55 °C, which often leads to poor cleaning on the surface of the steel plate, which affects the product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medium-temperature degreasing agent for automobile coating surface conditioning pretreatment and degreasing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The present embodiment configures the medium-temperature degreasing agent for the pre-treatment of automobile coating surface adjustment according to the following steps: get 30% sodium hydroxide by weight percentage, 50% trisodium phosphate, 10% tetrasodium edetate, dodecylbenzenesulfonate 2% sodium bicarbonate, 5% N,N-dimethylformamide, 3% ethanolamine, and mix these raw materials evenly.

[0026] This embodiment also provides a method for using the degreasing agent to degrease the surface of the car before the surface adjustment, and the steps are as follows:

[0027] 1) Heat the desalted water working solution to 55°C;

[0028] 2) Spraying process: Take part of the desalted water working fluid, add 5% medium temperature degreasing agent, mix well and then spray the surface of the metal workpiece to be treated, spraying time 3min, pressure 0.2MPa;

[0029] 3) Immersion process: take part of the desalted water working solution, add 3.5% medium temperature degreasing ...

Embodiment 2～5

[0033] According to the component ratio in Table 1, configure the medium-temperature degreasing agent for surface conditioning of automobiles.

[0034] Each embodiment component formula table of table 1

[0035] Element

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a medium-temperature degreasing agent for pre-treatment of automobile painting surface adjustment and a degreasing method thereof. The medium-temperature degreasing agent is prepared by mixing the following components in weight percent: 30-50% of strong alkali, 30-50% of soluble phosphate 50%, complexing agent 10-20%, surfactant 2-6% and stabilizer 2-10%. The degreasing method is to heat the desalted water working solution to 40-55° C., add different percentages of the normal temperature degreasing agent, and degrease the automobile steel plate through three processes of spraying, soaking and water washing. The invention has excellent cleaning performance, can adapt to a faster automobile coating production line, and effectively solves the problem of unclean cleaning of the steel plate surface.

Description

technical field [0001] The invention relates to a medium-temperature degreasing agent, in particular to a medium-temperature degreasing agent and a degreasing method for the pre-conditioning treatment of the surface of an automobile coating. Background technique [0002] The chemical degreasing process is an important pre-treatment link in the automobile painting process. It mainly uses lye to saponify, emulsify and dissolve the oil to remove the oil on the surface of the workpiece. The surface chemical cleaning treatment process must be carried out before surface adjustment to remove oil particles and other surface residues on the metal surface. If the oil removal is not clean during the pre-treatment, the oil will be brought into the subsequent process, which will affect the product quality. The treatment effect is good or bad. It is the key to ensure the quality of the paint film. [0003] The chemical degreasing process generally adopts the combination of spraying and i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23G1/19
CPCC23G1/19
Inventor 黄先球马颖郎丰军彭浩程鹏庞涛宋建红黄菲何锐李安平
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap